Method of selective reactive ion etching of substrates
Assignee: International Business Machines Corp
•
Filing: 1987-10-30
•
Granted: 1989-05-02
•
Expires: 2007-10-30
Abstract
Abstract A method of image transfer transfer into a substrate by reactive ion etch technique is provided. A mask layer on said substrate is formed by a spin-on film which film is comprised of a mixed organo-functional zircoaluminate or zircotitanate material. The film is dried and cured, and thereafter coated with a radiation sensitive resist. The reist is imagewise exposed and developed, which developing preferably also removes the pattern in the mask exposing the substrate. The substrate is then reactive ion etched, the remaining film acting as a barrier material to the etching.
Inventors
- 👤 Brian H. Desilets
- 👤 Richard D. Kaplan
- 👤 Harbans S. Sachdev
- 👤 Krishna G. Sachdev
- 👤 Susan A. Sanchez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:05
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/094; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/95
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
121 words
A method of image transfer into a substrate material by reactive ion etch (RIE) technique comprising the steps of, selecting a substrate material into which a pattern is to be etched, applying a spin-on film forming mask layer on said substrate material, said mask layer comprising a mixed organometallic polymer selected from the group consisting of organo functional zircoaluminates, organo functional zircotitanates, and organo functional hafniumaluminates, drying and curing said mask film, forming a pattern in said mask to expose the substrate to the pattern to be etched on the substrate, and thereafter reactive ion etching to transfer the mask pattern into said exposed substrate utilizing the remaining portions of the patterned film as a barrier to the reactive ion etching.
Claim 2
Independent Claim
121 words
A method of image transfer into a substrate material by reactive ion etch (RIE) technique comprising the steps of, selecting a substrate material into which a pattern is to be etched, applying a spin-on film forming mask layer on said substrate material, said mask layer comprising a mixed organometallic polymer selected from the group consisting of organo functional zircoaluminates, organo functional zircotitanates, and organo functional hafniumaluminates, drying and curing said mask film, forming a pattern in said mask to expose the substrate to the pattern to be etched on the substrate, and thereafter reactive ion etching to transfer the mask pattern into said exposed substrate utilizing the remaining portions of the patterned film as a barrier to the reactive ion etching.
Claim 3
Dependent Claim
62 words
The method as defined in claim 1, wherein the pattern is formed in said mask by first applying a radiation sensitive resist coating over said mask layer, imagewise exposing said resist film, and thereafter developing the exposed resist pattern with simultaneous removal of said underlying mask in the developed resist areas to form a patterned composite of the resist and said mask.
Claim 4
Dependent Claim
55 words
The method as defined in claim 2, wherein said developing is in an aqueous base developer and wherein the mixed metal organometallic RIE mask material is selected to be soluble in said aqueous-base developer used to develop the resist coating, whereby the resist is developed and the mask material is patterned in a single step.
Claim 5
Dependent Claim
22 words
The method as defined in claim 3, wherein the developer is selected from the group consisting of aqueous bases and alcoholic bases.
Claim 6
Dependent Claim
76 words
The method as defined in claim 1, wherein the pattern is formed in said mask by first applying a radiation sensitive resist coating over said mask layer, imagewise exposing said resist film and then transferring the resist pattern into the mixed-metal organometallic RIE mask in a separate step wherein the resist is first developed in an organic solvent without affecting the underlying mask, and thereafter said mask is patterned to expose the substrate to be etched.
Claim 7
Dependent Claim
37 words
The method as defined in claim 5, wherein the developer for the resist layer is an organic solvent and the developer for said mask layer is selected from the group consisting of aqueous bases and alcoholic bases.
Claim 8
Dependent Claim
26 words
The method as defined in claim 5 wherein the resist pattern is developed with an organic solvent and said mask layer is patterned by dry etching.
Claim 9
Dependent Claim
43 words
The method as defined in claim 1, wherein the substrate material is an organic polymer film in which the pattern is transferred by selective dry etching using a gas selected from the group consisting of oxygen and a mixture of fluorocarbons and oxygen.
Claim 10
Dependent Claim
20 words
The method as defined in claim 8, wherein the RIE mask material is an organo-functional zircoaluminate having carboxy functional ligands.
Claim 11
Dependent Claim
20 words
The invention as defined in claim 8, wherein the RIE mask material is an organo-functional zircoaluminate, having amino functional ligands.
Claim 12
Dependent Claim
58 words
The method as defined in claim 1, wherein the substrate material is selected from the group consisting of silicon, polysilicon, silicon oxide, and silicon nitride, wherein selective reactive ion etching is carried out by using a composition selected from the group consisting of SF 6 , halogenated hydrocarbons, chloro-fluoro-carbons, fluorocarbons, and mixed fluorocarbons and oxygen and mixtures thereof.
Claim 13
Dependent Claim
45 words
The method as defined in claim 1, wherein said mixed metal organometallic polymers are organo-functional zircoaluminates wherein the functional groups are selected from the group consisting of isopropanol, butanol, 1,2-dihydroxyisobutane, carboxylic acids, hydroxy caroxylic acids, amino acids, glycols, monoesters of glycols, and diesters of glycols.
References Cited (Backward Citations)
US4493855A
Cited
US4539049A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-01 | 1992-10-31 | 1993-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-01 | 1996-10-31 | 1997-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-01 | 2000-10-31 | 2001-05-02 | $7700.00 | Window Closed / Lapsed |