Process of producing polyethylene drawn filaments and drawn films
Assignee: Toyobo Co Ltd
•
Filing: 1987-12-21
•
Granted: 1989-04-25
•
Expires: 2007-12-21
Abstract
Abstract A process for producing polyethylene drawn filaments and drawn films which comprises molding under pressure a mixture of 51 to 90 parts by weight of polyethylene powder having a weight average molecular weight of at least 4×10 5 and having no history of being molten or dissolved after polymerization, and 49 to 10 parts by weight of a solvent at a temperature lower than the melting point of the mixture, and then hot-stretching the molded product.
Inventors
- 👤 Fujio Okada
- 👤 Toshihiko Ohta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:43
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C55/00; B29C55/005; D; D01; D01F; D01F6/00; D01F6/02; D01F6/04; B29K; B29K2023/00; B29K2023/04; B29K2023/06; C08J2323/00; C08J2323/02; C08J2323/04
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
75 words
A process for producing polyethylene drawn filaments and drawn films which comprises molding under pressure a mixture of 51-90 parts by weight of polyethylene powder having a weight average molecular weight of at least 4×10 5 and having no history of being molten or dissolved after polymerization, and 49 to 10 parts by weight of a solvent at a temperature lower than the endothermic peak temperature of the mixture, and then hot-stretching the molded product.
Claim 2
Dependent Claim
75 words
A process for producing polyethylene drawn filaments and drawn films which comprises molding under pressure a mixture of 51-90 parts by weight of polyethylene powder having a weight average molecular weight of at least 4×10 5 and having no history of being molten or dissolved after polymerization, and 49 to 10 parts by weight of a solvent at a temperature lower than the endothermic peak temperature of the mixture, and then hot-stretching the molded product.
Claim 3
Dependent Claim
85 words
A process according to claim 1 wherein the polyethylene powder having no history of being melted or dissolved after polymerization has a melting point of not lower than 130° C. and has a maximum draw ratio of at least 40 which is determined by the following measuring procedure: polyethylene powder is compression molded by a plate press at 130° C. under pressure of 400kg/cm 2 to form a sheet which is stretched in an air bath at 130° C. to measure its maximum draw ratio.
Claim 4
Dependent Claim
28 words
A process according to claim 1, wherein the molding is carried out by heating the mixture fed to the die to swell it and extruding from the die.
Claim 5
Dependent Claim
38 words
A process according to claim 3, wherein a die hole does not increase in sectional area in the extrusion direction, and the outlet sectional area is in the range of from 6 to 80% of the inlet one.
Claim 6
Dependent Claim
16 words
A process according to claim 1 wherein the molding is carried out by a roller press.
Claim 7
Dependent Claim
14 words
A process according to claim 2 wherein the draw ratio is at least 10.
Claim 8
Dependent Claim
28 words
A process according to claim 2, wherein the molding is carried out by heating the mixture fed to the die to swell it and extruding from the die.
Claim 9
Dependent Claim
16 words
A process according to claim 2, wherein the molding is carried out by a roller press.
Claim 10
Dependent Claim
14 words
A process according to claim 2, wherein the draw ratio is at least 10.
Claim 11
Dependent Claim
22 words
A process according to claim 1, wherein the molding temperature is 3°-20° C. lower than the endothermic peak temperature of the mixture.
Claim 12
Dependent Claim
22 words
A process according to claim 2, wherein the molding temperature is 3°-20° C. lower than the endothermic peak temperature of the mixture.
Claim 13
Dependent Claim
14 words
A process according to claim 1, wherein the molding temperature is between 100°-124° C.
Claim 14
Dependent Claim
14 words
A process according to claim 2, wherein the molding temperature is between 100°-124° C.
Claim 15
Dependent Claim
20 words
A process according to claim 1, wherein the molded product has a tensile strength of at least about 1.3 GPa.
Claim 16
Dependent Claim
20 words
A process according to claim 2, wherein the molded product has a tensile strength of at least about 1.3 GPa.
Claim 17
Dependent Claim
15 words
A process according to claim 1, wherein the tensile modulus is at least 51 GPa.
Claim 18
Dependent Claim
15 words
A process according to claim 2, wherein the tensile modulus is at least 51 GPa.
References Cited (Backward Citations)
US3184526A
Cited
JPS55135630A
Cited
US4272474A
Cited
US4487875A
Cited
JPS5889326A
Cited
US4615853A
Cited
US4643865A
Cited
JPS60189420A
Cited
NL8500428A
Cited
NL8402961A
Cited
US4734196A
Cited
JPS61293229A
Cited
US4769433A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-24 | 1992-10-24 | 1993-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-24 | 1996-10-24 | 1997-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-24 | 2000-10-24 | 2001-04-25 | $7700.00 | Window Closed / Lapsed |