Method for producing thermoplastic resin sheet or filler-containing resin sheet
Assignee: Eneos Corp
•
Filing: 1984-10-05
•
Granted: 1986-10-07
•
Expires: 2004-10-05
Abstract
Abstract A method for producing a thermoplastic resin sheet or a filler-containing thermoplastic resin sheet by which method a difficultly-workable thermoplastic resin as well as an ordinary thermoplastic resin can be formed into a sheet and various kinds of fillers can be compounded into the sheet. The method is characterized in that a thermoplastic resin or a composition of a thermoplastic resin and a filler is fed in powder or preformed sheet form between a pair of tensioned endless belts disposed parallel and travelling together around a set of rolls, the endless belts being heated by being brought into surface-to-surface contact with heating rolls while travelling along a path having at least one bend formed by the heating rolls, and the material is heated and compressed between the endless belts and melted into an integral body at or above the melting point or softening point of the thermoplastic resin.
Inventors
- 👤 Takeo Aoyama
- 👤 Tadashi Kamei
- 👤 Mikio Uehara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:50
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/88; B29C70/882; B29C43/00; B29C43/22; B29C43/24; B29C43/32; B29C43/52; B29C43/44; B29C43/48; B29C2043/483; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0658; B29K2023/0683; B29K2101/00; B29K2101/12; B29K2105/00; B29K2105/06; B29K2105/16; B29K2105/25; B29K2105/251; B29K2105/253; B29K2105/256; B29K2995/00; B29K2995/0003; B29K2995/0005; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0373; H05K1/0393; H05K3/00; H05K3/02; H05K3/022
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
130 words
A method for producing a thermoplastic resin sheet or a filler-containing resin sheet which method is characterized in that a difficultly-workable thermoplastic resin or a composition of a difficulty-workable thermoplastic resin and a filler is fed in powder or preformed sheet form between a pair of endless steel belts stretched under a tension of at least 3 kg/cm, disposed parallel and traveling together around a set of rolls, said endless belts being heated by being brought into surface-to-surface contact with heating rolls while travelling along a path having at least one bend formed on said heating rolls, said resin or composition heated and compressed in said bend between said endless belts and melted into an integral body at or above the melting point or softening point of said thermoplastic resin.
Claim 2
Independent Claim
130 words
A method for producing a thermoplastic resin sheet or a filler-containing resin sheet which method is characterized in that a difficultly-workable thermoplastic resin or a composition of a difficulty-workable thermoplastic resin and a filler is fed in powder or preformed sheet form between a pair of endless steel belts stretched under a tension of at least 3 kg/cm, disposed parallel and traveling together around a set of rolls, said endless belts being heated by being brought into surface-to-surface contact with heating rolls while travelling along a path having at least one bend formed on said heating rolls, said resin or composition heated and compressed in said bend between said endless belts and melted into an integral body at or above the melting point or softening point of said thermoplastic resin.
Claim 3
Dependent Claim
81 words
The method for producing a thermoplastic resin sheet or a filler-containing resin sheet in claim 1, wherein said difficultly-workable thermoplastic resin is a member selected from the group consisting of polyethylene resin having an intrinsic viscosity of 8 or higher in a decalin solution at 135° C., fluorocarbon resin, polycarbonate resin, polyimide resin, polyamide-imide resin, polyether ether ketone resin, polyether sulfone resin, polysulfone resin, polyphenylene oxide resin, polyphenylene ether resin, polyphenylene sulfide resin, aromatic polyamide resin, polyester resin and mixtures thereof.
Claim 4
Dependent Claim
42 words
The method for producing a thermoplastic resin sheet or a filler-containing resin sheet in claim 1, wherein said filler is at least one member selected from the group consisting of fibrous fillers, scaly fillers, flaky fillers, needle fillers and hollow particle fillers.
Claim 5
Dependent Claim
43 words
The method for producing a thermoplastic resin sheet or a filler-containing resin sheet in claim 1, 2 or 3, wherein the compounding ratio of said filler is 5 to 1000 parts by weight to 100 parts by weight of said difficultly-workable thermoplastic resin.
References Cited (Backward Citations)
US2537311A
Cited
US2574588A
Cited
US2960727A
Cited
US3223027A
Cited
GB1098946A
Cited
US3400186A
Cited
US3801250A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |