Nitride-based ceramic material
Assignee: Santrade Ltd
•
Filing: 1988-05-27
•
Granted: 1989-04-04
•
Expires: 2008-05-27
Abstract
Abstract The present invention relates to a sintered nitride-based ceramic material, where the presence of polytype of Si-Al-O-N together with beta' and/or alpha' Si-Al-O-N constitutes the main components. It also contains an intergranular phase and depending on the composition crystalline AlN or Al 2 O 3 . The properties of the material, such as the wear resistance and toughness behaviour, can be improved by adding hard refractory principles and/or fine whisker like fibers. Coating with hard, inert and wear resistant layers is another alternative. The material is suitable to use where the demands of resistance to thermal shocks, high mechanical strength or high heat conductivity are great. It has turned out to be especially suitable for cutting tools but also other applications are possible, e.g. as engine components, wear parts, heat exchangers or as substrate material in the electronic industry.
Inventors
- 👤 Thommy C. Ekstrom
- 👤 Nils A. Ingelstrom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:50
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/58; C04B35/597; C04B35/71; C04B35/78; C04B35/80; C04B41/45; C04B41/50; C04B41/5025; C04B41/80; C04B41/81; C04B41/85; C04B41/87; F; F28; F28F; F28F19/00; F28F19/02
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
58 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 1-70% polytype, 5-80% alpha' and/or beta' phase and 0.1-20% of the intergranular phase.
Claim 2
Dependent Claim
58 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 1-70% polytype, 5-80% alpha' and/or beta' phase and 0.1-20% of the intergranular phase.
Claim 3
Dependent Claim
29 words
The sintered ceramic material of claim 1 wherein the sintered material contains at least 30 percent by volume alpha' phase and at the most 689% by volume beta' phase.
Claim 4
Dependent Claim
19 words
The sintered ceramic material of claim 1 wherein the sintered material contains at the most 50% by volume polytype.
Claim 5
Dependent Claim
24 words
The sintered ceramic material of claim 1 wherein the sintered material contains at the most 70 percent by volume of alpha'+beta' phase of Si-Al-O-N.
Claim 6
Dependent Claim
19 words
The sintered ceramic material of claim 1 further consisting essentially of at the most 20% by volume crystalline AlN.
Claim 7
Dependent Claim
23 words
The sintered ceramic material of claim 1 wherein the sintered material consists essentially of at least 40% by volume of polytype of Si-Al-O-N.
Claim 8
Dependent Claim
24 words
The sintered ceramic material of claim 1 wherein the sintered material consists essentially of at the most 60% by volume alpha'+beta' phase of Si-Al-O-N.
Claim 9
Dependent Claim
22 words
The sintered ceramic material of claim 1 wherein the sintered material consists essentially of at the most 15% by volume intergranular phase.
Claim 10
Dependent Claim
24 words
The sintered ceramic material of claim 1 wherein the sintered material consists essentially of at the most 10% by volume alpha'+beta' phase of Si-Al-O-N.
Claim 11
Dependent Claim
24 words
The sintered ceramic material of claim 1 wherein he sintered material consists essentially of a volume fraction polytype of Si-Al-O-N of at least 20%.
Claim 12
Dependent Claim
23 words
The sintered ceramic material of claim 1 further consisting essentially of a volume fraction of at the most 80% by volume crystalline AlN.
Claim 13
Dependent Claim
25 words
The sintered ceramic material of claim 1 wherein the sintered material contains a volume fraction of at the most 15% by volume of intergranular phase.
Claim 14
Dependent Claim
19 words
The sintered ceramic material of claim 1 further consisting essentially of greater than 5% by volume of silicon carbide.
Claim 15
Dependent Claim
42 words
The sintered ceramic material of claim 1 wherein the sintered ceramic material is coated with one or more wear resistant layers of nitrides, oxynitrides, oxides, borides, carbides, carbonitrides or oxycarbides of the transition elements from the groups III-VI and/or the elements aluminium.
Claim 16
Dependent Claim
77 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 30-99% polytype of Si-Al-O-N, at the most 70% alpha' phase of Si-Al-O-N, at the most 70% beta' phase of Si-Al-O-N, at the most 30% crystalline AlN and 0.1-20% of the intergranular phase.
Claim 17
Dependent Claim
77 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 30-99% polytype of Si-Al-O-N, at the most 70% alpha' phase of Si-Al-O-N, at the most 70% beta' phase of Si-Al-O-N, at the most 30% crystalline AlN and 0.1-20% of the intergranular phase.
Claim 18
Dependent Claim
79 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 5-99% of polytype of Si-Al-O-N, at the most 10% alpha' phase of Si-Al-O-N, at the most 95% crystalline AlN and 0.1-20% of the intergranular phase wherein the sum of the volume percentages is 100%.
Claim 19
Dependent Claim
79 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N and an intergranular phase, the sintered material having in percent by volume: 5-99% of polytype of Si-Al-O-N, at the most 10% alpha' phase of Si-Al-O-N, at the most 95% crystalline AlN and 0.1-20% of the intergranular phase wherein the sum of the volume percentages is 100%.
Claim 20
Dependent Claim
83 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and one or more refractory hard principal phases of nitrides, carbonitrides, carbides and/or oxynitrides of the transition elements from groups IV-VI and/or the elements aluminum, boron or silicon, the sintered material having in percent by volume: 1-70% polytype, 5-80% beta' phase and 0.1-20% of the intergranular phase.
Claim 21
Dependent Claim
83 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and one or more refractory hard principal phases of nitrides, carbonitrides, carbides and/or oxynitrides of the transition elements from groups IV-VI and/or the elements aluminum, boron or silicon, the sintered material having in percent by volume: 1-70% polytype, 5-80% beta' phase and 0.1-20% of the intergranular phase.
Claim 22
Dependent Claim
101 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and 1-50% by volume of refractory, hard materials in a fibrous or whisker formed of SiC, TiN, B 4 C, TiC, Al 2 O 3 and/or Si 2 N 2 O, the fibers having a diameter less than 2 microns and a length/diameter-ratio of more than 10, the sintered material having in percent by volume: 1-70% polytype, 5-80% beta' phase and 0.1-20% of the intergranular phase.
Claim 23
Dependent Claim
101 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and 1-50% by volume of refractory, hard materials in a fibrous or whisker formed of SiC, TiN, B 4 C, TiC, Al 2 O 3 and/or Si 2 N 2 O, the fibers having a diameter less than 2 microns and a length/diameter-ratio of more than 10, the sintered material having in percent by volume: 1-70% polytype, 5-80% beta' phase and 0.1-20% of the intergranular phase.
Claim 24
Dependent Claim
81 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and an additive selected froom SiC, TiN and TaN that improves the electrical conductivity of the sintered material so as to permit spark cutting, the sintered material having in percent by volume: 1-70% polytype, 5-80% alpha' and/or beta' phase and 0.1-20% of the intergranular phase.
Claim 25
Dependent Claim
81 words
A sintered ceramic material based on silicon nitride, aluminum nitride and alumina consisting essentially of a combination of polytype of Si-Al-O-N and an alpha' phase of Si-Al-O-N and/or a beta' phase of Si-Al-O-N, an intergranular phase and an additive selected froom SiC, TiN and TaN that improves the electrical conductivity of the sintered material so as to permit spark cutting, the sintered material having in percent by volume: 1-70% polytype, 5-80% alpha' and/or beta' phase and 0.1-20% of the intergranular phase.
References Cited (Backward Citations)
GB1464022A
Cited
US4113503A
Cited
US4127416A
Cited
US4127416B1
Cited
US4243621A
Cited
US4563433A
Cited
US4711644A
Cited
US4506020A
Cited
US4424066A
Cited
US4426209A
Cited
EP0106817A1
Cited
US4547470A
Cited
US4543345A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |