High thermal conductivity ceramic body

Claim 2

A process for producing a sintered polycrystalline aluminum nitride ceramic body having a composition defined and encompassed by polygon ABCFGH of FIG. 2, a porosity of less than about 10% by volume of said body and a thermal conductivity greater than 0.70 W/cm·K at 25° C. which consists essentially of the steps: (a) forming a mixture consisting essentially of an oxygen-containing aluminum nitride powder, gadolinium oxide and free carbon, shaping said mixture into a compact, said mixture and said compact having a composition wherein the equivalent % of said gadolinium and aluminum ranges from point A to point F of FIG. 2, said gadolinium ranging from about 8.0 equivalent % to about 0.3 equivalent %, said aluminum ranging from about 92.0 equivalent % to about 99.7 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon ABCFGH of FIG. 2, (b) heating said compact in a nitrogen-containing nonoxidizing atmosphere at a temperature ranging from about 1350° C. to a temperature sufficient to deoxidize the compact but below its pore closing temperature reacting said free carbon with oxygen contained in said aluminum nitride producing a deoxidized compact, said deoxidized compact having a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon ABCFGH of FIG. 2, said free carbon being in an amount which produces said deoxidized compact, and (c) sintering said deoxidized compact in a nitrogen-containing nonoxidizing atmosphere at a minimum temperature of about 1840° C. producing said polycrystalline body.

Claim 3

The process according to claim 1 wherein said nitrogen-containing atmosphere in step (b) contains sufficient nitrogen to facilitate deoxidation of the aluminum nitride to produce said sintered body.

Claim 4

The process according to claim 1 wherein said nitrogen-containing atmosphere in step (c) contains sufficient nitrogen to prevent significant weight loss of said aluminum nitride.

Claim 5

The process according to claim 1 wherein said process is carried out at ambient pressure.

Claim 6

The process according to claim 1 wherein said porosity is less than about 4% by volume of said body.

Claim 7

The process according to claim 1 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point A up to point Q of FIG. 2, said gadolinium ranging from about 8.0 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 92.0 equivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon ABCQRS of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined and encompassed by polygon ABCQRS excluding line CQ of FIG. 2.

Claim 8

The process according to claim 1 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point I up to point Q of FIG. 2, said gadolinium ranging from about 5.75 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 94.25 equivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon IJKQRS of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon IJKQRS but excluding line KQ of FIG. 2.

Claim 9

The process according to claim 1 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point M up to point Q of FIG. 2, said gadolinium ranging from about 3.75 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 96.25 equivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon MNOQRS of FIG. 2, said deoxidized compact and sintered body are comprised of a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon MNOQRS excluding line OQ of FIG. 2, and wherein said minimum sintering temperature is about 1850° C.

Claim 10

The process according to claim 1 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point S up to point F of FIG. 2, said gadolinium ranging from about 2.4 equivalent % to greater than about 0.3 equivalent % and said aluminum ranging from about 97.6 equivalent % to less than about 99.7 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon SRQFGH of FIG. 2, said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined and encompassed by polygon SRQFGH, excluding line QF of FIG. 2, and wherein said minimum sintering temperature ranges from about 1890° C. to about 1920° C.

Claim 11

The process according to claim 1 wherein said mixture and said compact hav a composition wherein the equivalent % of said gadolinium and aluminum ranges from point K to point O of FIG. 2, said gadolinium ranging from about 1.8 equivalent % to about 0.8 equivalent % and said aluminum ranging from about 98.2 equivalent % to about 99.2 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined by line KO of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined by line KO of FIG. 2.

Claim 12

The process according to claim 1 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point O to point F of FIG. 2, said Gd ranging from about 0.8 equivalent % to about 0.3 equivalent % and said aluminum ranging from about 99.2 equivalent % to about 99.7 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined by line OF, said deoxidized compact and said sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined by line OF of FIG. 2, and wherein said minimum sintering temperature is about 1850° C.

Claim 13

A process for producing a sintered polycrystalline aluminum nitride ceramic body having composition defined and encompassed by polygon ABCFGH of FIG. 2, a porosity of less than about 10% by volume of said body and a thermal conductivity greater than 0.70 W/cm·K at 25° C. which consisting essentially of the steps: (a) forming a mixture consisting essentially of an oxygen-containing aluminum nitride powder, gadolinium oxide or precursor therefor, and a carbonaceous additive selected from the group consisting essentially of free carbon, a carbonaceous organic material and mixture thereof, said carbonaceous organic material thermally decomposing at a temperature ranging from about 50° C. to about 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, shaping said mixture into a compact, said mixture and said compact having a composition wherein the equivalent % of said gadolinium and aluminum ranges from point A to point F of FIG. 2, said gadolinium ranging from about 8.0 equivalent % to about 0.3 equivalent %, said aluminum ranging from about 92.0 equivalent % to about 99.7 equivalent % aluminum, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon ABCFGH of FIG. 2, (b) heating said compact in a nonoxidizing atmosphere at a temperature up to about 1200° C. thereby providing gadolinium oxide and free carbon, (c) heating said compact in a nitrogen-containing nonoxidizing atmosphere at a temperature ranging from about 1350° C. to a temperature sufficient to deoxidize the compact but below its pore closing temperature reacting said free carbon with oxygen contained in said aluminum nitride producing a deoxidized compact, said deoxidized compact having a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon ABCFGH of FIG. 2, said free carbon being in an amount which produces said deoxidized compact, and (d) sintering said deoxidized compact in a nitrogen-containing nonoxidizing atmosphere at a minimum temperature of about 1840° C. producing said polycrystalline body.

Claim 14

A process for producing a sintered polycrystalline aluminum nitride ceramic body having composition defined and encompassed by polygon ABCFGH of FIG. 2, a porosity of less than about 10% by volume of said body and a thermal conductivity greater than 0.70 W/cm·K at 25° C. which consisting essentially of the steps: (a) forming a mixture consisting essentially of an oxygen-containing aluminum nitride powder, gadolinium oxide or precursor therefor, and a carbonaceous additive selected from the group consisting essentially of free carbon, a carbonaceous organic material and mixture thereof, said carbonaceous organic material thermally decomposing at a temperature ranging from about 50° C. to about 1000° C. to free carbon and gaseous product of decomposition which vaporizes away, shaping said mixture into a compact, said mixture and said compact having a composition wherein the equivalent % of said gadolinium and aluminum ranges from point A to point F of FIG. 2, said gadolinium ranging from about 8.0 equivalent % to about 0.3 equivalent %, said aluminum ranging from about 92.0 equivalent % to about 99.7 equivalent % aluminum, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon ABCFGH of FIG. 2, (b) heating said compact in a nonoxidizing atmosphere at a temperature up to about 1200° C. thereby providing gadolinium oxide and free carbon, (c) heating said compact in a nitrogen-containing nonoxidizing atmosphere at a temperature ranging from about 1350° C. to a temperature sufficient to deoxidize the compact but below its pore closing temperature reacting said free carbon with oxygen contained in said aluminum nitride producing a deoxidized compact, said deoxidized compact having a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon ABCFGH of FIG. 2, said free carbon being in an amount which produces said deoxidized compact, and (d) sintering said deoxidized compact in a nitrogen-containing nonoxidizing atmosphere at a minimum temperature of about 1840° C. producing said polycrystalline body.

Claim 15

The process according to claim 12 wherein said nitrogen-containing atmosphere in step (c) contains sufficient nitrogen to facilitate deoxidation of the aluminum nitride to produce said sintered body.

Claim 16

The process according to claim 12 wherein said nitrogen-containing atmosphere in step (d) contains sufficient nitrogen to prevent significant weight loss of said aluminum nitride.

Claim 17

The process according to claim 12 wherein said process is carried out at ambient pressure.

Claim 18

The process according to claim 12 wherein said porosity is less than about 4% by volume of said body.

Claim 19

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point A up to point Q of FIG. 2, said gadolinium ranging from about 8.0 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 92.0 equivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon ABCQRS of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined and encompassed by polygon ABCQRS excluding line CQ of FIG. 2.

Claim 20

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point I up to point Q but excludes line KQ of FIG. 2, said gadolinium ranging from about 5.75 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 94.25 equivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon IJKQRS of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined and encompassed by polygon IJKQRS but excluding line KQ of FIG. 2.

Claim 21

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point M up to point Q of FIG. 2, said gadolinium ranging from about 3.75 equivalent % to greater than about 0.55 equivalent % and said aluminum ranging from about 96.25 eqiivalent % to less than about 99.45 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined and encompassed by polygon MNOQRS of FIG. 2, said deoxidized compact and sintered body are comprised of a composition wherein the equivalent % of Al, Gd, O and N is defined and encompassed by polygon MNOQRS excluding line OQ of FIG. 2, and wherein said minimum sintering temperature is about 1850° C.

Claim 22

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point S up to point F of FIG. 2, said gadolinium ranging from about 2.4 equivalent % to greater than about 0.3 equivalent % and said aluminum ranging from about 97.6 equivalent % to less than about 99.7 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N, outside the composition defined and encompassed by polygon SRQFGH of FIG. 2, said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined and encompassed by polygon SRQFGH excluding line QF of FIG. 2, and wherein said minimum sintering temperature ranges from about 1890° C. to about 1920° C.

Claim 23

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point K to point O of FIG. 2, said gadolinium ranging from about 1.8 equivalent % to about 0.8 equivalent % and said aluminum ranging from about 98.2 equivalent % to about 99.2 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined by line KO of FIG. 2, and said deoxidized compact and sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined by line KO of FIG. 2.

Claim 24

The process according to claim 12 wherein said mixture and said compact have a composition wherein the equivalent % of said gadolinium and aluminum ranges from point O to point F of FIG. 2, said Gd ranging from about 0.8 equivalent % to about 0.3 equivalent % and said aluminum ranging from about 99.2 equivalent % to about 99.7 equivalent %, said mixture and said compact having an equivalent % composition of Gd, Al, O and N outside the composition defined by line OF, said deoxidized compact and said sintered body are comprised of a composition wherein the equivalent percent of Al, Gd, O and N is defined by line OF of FIG. 2, and wherein said minimum sintering temperature is about 1850° C.