Process of making via holes in a double-layer insulation
Assignee: International Business Machines Corp
•
Filing: 1988-03-23
•
Granted: 1989-03-28
•
Expires: 2008-03-23
Abstract
Abstract A method of making via holes in a double-layer insulation of nitride and polyimide. The via holes are made with one photomask only by applying a photoresist process with double exposure, and a multi-step dry etching process. The double exposure, which includes an image-wise exposure followed by blanket irradiation, achieves an edge angle in the photoresist between approx. 60 DEG and 70 DEG , depending on the exposure time ratios. This angle is transferred into the polyimide layer in a dry etching process. In a first etching step with CF4 as etching gas the greater part of the polyimide is removed. For removing the residual polyimide in the via holes there now follows an etching step in O2. Etch bias is thus kept on a very low level. The nitride layer is then etched with CF4 as etching gas, with the etching process being executed in two steps, each followed by an etching step in O2 for laterally shifting the photoresist and the polyimide via the resist angle. By softening the step height a softer profile of the via holes is ensured, which permits very good covering by a second layer of metallurgy.
Inventors
- 👤 Eva Horner
- 👤 Reinhold Muhl
- 👤 Hans-Joachim Trumpp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:23
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/082
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
259 words
Method of making via holes in a double-layer insulation, comprising the following steps: (1) applying a first insulation layer (7) of inorganic material onto a substrate with a first layer of metallurgy (6); (2) applying a second insulation layer (8) of polymeric material onto the first insulation layer (7); (3) applying a layer (9) of positive photoresist on the double layer (7, 8) and pre-baking; (4) image-wise exposing of the photoresist layer (9) and subsequently blanket exposing thereof, and post-baking; (5) developing the photoresist layer (9) with a basic developer; (6) reactive ion etching (RIE) with a first etching gas of approximately 2/3 to 3/4 of the thickness of the second insulation layer (8) in the areas of the respective via holes exposed by the photoresist mask; (7) RIE with a second etching gas for completely removing the second insulation layer (8) in the areas exposed by the mask, with the first insulation layer (7) serving as an etch stop; (8) RIE with the first etching gas approximately half the thickness of the first insulation layer (7); (9) RIE with the second etching gas to effect via the angle of the resist a lateral shifting of the photoresist (9) and of the second insulation layer (8); (10) RIE with the first etching gas of the second half of the first insulation layer (7); (11) RIE with the second etching gas to effect via the angle of the resist a lateral shifting of the photoresist (9) and of the second insulation layer (8); and (12) stripping the residual photoresist (9).
Claim 2
Dependent Claim
259 words
Method of making via holes in a double-layer insulation, comprising the following steps: (1) applying a first insulation layer (7) of inorganic material onto a substrate with a first layer of metallurgy (6); (2) applying a second insulation layer (8) of polymeric material onto the first insulation layer (7); (3) applying a layer (9) of positive photoresist on the double layer (7, 8) and pre-baking; (4) image-wise exposing of the photoresist layer (9) and subsequently blanket exposing thereof, and post-baking; (5) developing the photoresist layer (9) with a basic developer; (6) reactive ion etching (RIE) with a first etching gas of approximately 2/3 to 3/4 of the thickness of the second insulation layer (8) in the areas of the respective via holes exposed by the photoresist mask; (7) RIE with a second etching gas for completely removing the second insulation layer (8) in the areas exposed by the mask, with the first insulation layer (7) serving as an etch stop; (8) RIE with the first etching gas approximately half the thickness of the first insulation layer (7); (9) RIE with the second etching gas to effect via the angle of the resist a lateral shifting of the photoresist (9) and of the second insulation layer (8); (10) RIE with the first etching gas of the second half of the first insulation layer (7); (11) RIE with the second etching gas to effect via the angle of the resist a lateral shifting of the photoresist (9) and of the second insulation layer (8); and (12) stripping the residual photoresist (9).
Claim 3
Dependent Claim
23 words
Method as claimed in claim 1, characterized in that as first insulation layer a silicon nitride layer (7) conformal with all wafer topographies.
Claim 4
Dependent Claim
22 words
Method as claimed in claim 2, characterized in that the silicon nitride layer has a thickness between approximately 0.2 and 0.8 μm.
Claim 5
Dependent Claim
18 words
Method as claimed in claim 1, characterized in that as second insulation layer a planarizing polyimide layer (8).
Claim 6
Dependent Claim
21 words
Method as claimed in claim 4, characterized in that the polyimide layer has a thickness of approximately 0.8 to 2 μm.
Claim 7
Dependent Claim
36 words
Method as claimed in claim 1, characterized in that the positive photoresist is a positive photoresist (9) on Novolak basis with a diazonaphthoquinone inhibitor and is applied with a thickness of approximately 3 to 5 μm.
Claim 8
Dependent Claim
31 words
Method as claimed in claim 1 characterized in that the image-wise exposing and blanket exposing of the photoresist layer is performed with a radiation wave length of 436 nm or less.
Claim 9
Dependent Claim
27 words
Method as claimed in claim 1, characterized in that the slope angle of the photoresist edges is controlled via the ratio of blanket to image-wise exposure duration.
Claim 10
Dependent Claim
23 words
Method as claimed in claim 8, characterized in that the ratio of blanket to image-wise exposure duration is between approximately 1:2.0 and 1:5.
Claim 11
Dependent Claim
18 words
Method as claimed in claim 9, characterized in that the ratio of blanket to image-wise exposure is 1:2.5.
Claim 12
Dependent Claim
38 words
Method as claimed in claim 1, characterized in that the photoresist layer is pre-baked prior to exposure for approximately 20 minutes at approximately 85° C., and post-baked after blanket irradiation for approximately 10 minutes at approximately 105° C.
Claim 13
Dependent Claim
27 words
Method as claimed in claim 1 characterized in that as a first etching gas CF 4 is used, and as a second etching gas oxygen is used.
Claim 14
Dependent Claim
30 words
Method as claimed in claim 12, characterized in that the RIE of the first and second insulation layers in CF 4 is decoupled by an RIE etching step in oxygen.
Claim 15
Dependent Claim
23 words
Method as claimed in claim 1, characterized in that the etching rate ratio of photoresist to the second insulation layer is approximately 1:1.
Claim 16
Dependent Claim
32 words
Method as claimed in claim 13, characterized in that the RIE etching step of the second insulation layer in oxygen is performed at a pressure less than or equal to 100 μbar.
Claim 17
Dependent Claim
23 words
Method as claimed in claim 1, characterized in that after step (12), the method further characterized by depositing a second layer of metallurgy.
Claim 18
Dependent Claim
16 words
Method as claimed in claim 16, characterized in that Ti-Al-Cu is the second layer of metallurgy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-27 | 1992-09-26 | 1993-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-27 | 1996-09-26 | 1997-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-27 | 2000-09-26 | 2001-03-28 | $7700.00 | Window Closed / Lapsed |