US4814032A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making nonwoven fabrics
Assignee: JNC Corp
•
Filing: 1987-11-25
•
Granted: 1989-03-21
•
Expires: 2007-11-25
Abstract
Abstract A method for making nonwoven fabrics includes the steps of preparing heat-adhesive composite fibers including first and second components, forming a web of the composite fibers alone or containing at least 20% by weight of the composite fibers, and heat-treating the web at a temperature higher than the melting point of the second component but lower than the melting point of the first component, while increasing the temperature of the web at a rate of temperature rise of 100 DEG C./30 seconds and more. The first component is polypropylene having specific physical values with respect to density, isotactic pentad ratio, pentad ratio having two different kinds of configurations, and melt flow rate, and the second component is a polymer composed mainly of polyethylene.
Inventors
- 👤 Masahiko Taniguchi
- 👤 Shigeru Goi
- 👤 Taizo Sugihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:58
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/08; D04H3/16; D04H1/00; D04H1/40; D04H1/54
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
226 words
A method for making nonwoven fabrics which comprises the steps: melt-spinning first and second components to obtain heat-adhesive composite fibers and crimping thereafter, said first component being polypropylene having a density of 0.905 g/cm 3 or higher, and having a boiling n-heptane-insoluble part whose isotactic pentad ratio is 0.950 or higher and those pentad ratio having two different kinds of configurations is 0.002 or lower, and said second component being a polymer composed mainly of polyethylene, said first and second components being of the side-by-side or sheath-core arrangement in which said second component is formed on at least a part of the surfaces of said fibers in a lengthwise continuous manner, and said first component showing a melt flow rate of 3 inclusive to 20 exlusive before melt-spinning and a difference of within 10 between the melt flow rates before and after melt-spinning; forming a web consisting of said composite fibers alone or containing at least 20% by weight of said composite fibers; and heat-treating said web at a treatment temperature equal to or higher than the melting point of said second component but lower than the melting point of said first component, while increasing the temperature of said web at a rate of 100° C./30 seconds or higher to avoid a relaxation of molecular orientation of said first component given during spinning and stretching thereof.
Claim 2
Independent Claim
226 words
A method for making nonwoven fabrics which comprises the steps: melt-spinning first and second components to obtain heat-adhesive composite fibers and crimping thereafter, said first component being polypropylene having a density of 0.905 g/cm 3 or higher, and having a boiling n-heptane-insoluble part whose isotactic pentad ratio is 0.950 or higher and those pentad ratio having two different kinds of configurations is 0.002 or lower, and said second component being a polymer composed mainly of polyethylene, said first and second components being of the side-by-side or sheath-core arrangement in which said second component is formed on at least a part of the surfaces of said fibers in a lengthwise continuous manner, and said first component showing a melt flow rate of 3 inclusive to 20 exlusive before melt-spinning and a difference of within 10 between the melt flow rates before and after melt-spinning; forming a web consisting of said composite fibers alone or containing at least 20% by weight of said composite fibers; and heat-treating said web at a treatment temperature equal to or higher than the melting point of said second component but lower than the melting point of said first component, while increasing the temperature of said web at a rate of 100° C./30 seconds or higher to avoid a relaxation of molecular orientation of said first component given during spinning and stretching thereof.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein said first component has a density greater than 0.910 g/cm 3 .
Claim 4
Dependent Claim
14 words
The method of claim 1, wherein said second component is a homopolymer of ethylene.
Claim 5
Dependent Claim
29 words
The method of claim 1, wherein said second component is a copolymer of ethylene with at least one member selected from the group consisting of propylene, 1-butene, and vinylacetate.
Claim 6
Dependent Claim
15 words
The method of claim 1, wherein said second component is a mixture of ethylene polymers.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said second component has a melting point of at least 20° C. less than the melting point of said first component.
Claim 8
Dependent Claim
20 words
The method of claim 1, wherein said second component has a melt index of from about 5 to about 35.
Claim 9
Dependent Claim
23 words
The method of claim 1, wherein said composite fibers contain said second component in an amount of from 40 to 70% by weight.
Claim 10
Dependent Claim
21 words
The method of claim 1, wherein said web contains said composite fibers in an amount of at least 30% by weight.
References Cited (Backward Citations)
US3457338A
Cited
US3718534A
Cited
US3607509A
Cited
US4189338A
Cited
US4367113A
Cited
US4552603A
Cited
US4469540A
Cited
GB2114581A
Cited
US4500384A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-20 | 1992-09-19 | 1993-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-20 | 1996-09-19 | 1997-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-20 | 2000-09-19 | 2001-03-21 | $7700.00 | Window Closed / Lapsed |