Foam catalysts, method of manufacture and method of using
Assignee: Johnson Matthey PLC
•
Filing: 1987-08-28
•
Granted: 1989-03-07
•
Expires: 2007-08-28
Abstract
Abstract A catalyst, or a precursor thereto, comprises, as the active material or as a support therefor, a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 . The foam may be made by forming a negative replica of an open cell plastics foam by impregnation of the latter with a dispersion of the ceramic material, followed by drying and calcining the impregnated foam to remove the plastics material and to cause the ceramic material to sinter. For a steam reforming catalyst the ceramic may be alpha alumina and the active material nickel and/or cobalt.
Inventors
- 👤 Martyn V. Twigg
- 👤 William M. Sengelow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:55
CPC Classifications
C; C04; C04B; C04B38/00; C04B38/06; C04B38/0615; B; B01; B01J; B01J35/00; B01J35/50; B01J35/56; B01J35/60; C01; C01B; C01B3/00; C01B3/02; C01B3/32; C01B3/34; C01B3/38; C01B3/40; B01J2235/00; B01J35/30; B01J35/31; B01J35/32; B01J35/61; B01J35/612; B01J35/63; B01J35/633; C01B2203/00; C01B2203/10; C01B2203/1041; C01B2203/1047; C04B2111/00; C04B2111/00474; C04B2111/0081; C04B2111/10; C04B2111/1056; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
86 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range of 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 1 g.cm -3 .
Claim 2
Dependent Claim
86 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range of 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 1 g.cm -3 .
Claim 3
Dependent Claim
24 words
A catalyst or precursor according to claim 1 wherein the foam has an apparent density in the range 1 to 2.5 g.cm -3 .
Claim 4
Dependent Claim
27 words
A catalyst or precursor according to claim 1 wherein the foam has a total pore volume in the range 0.2 to 1.5 cm 3 .g -1 .
Claim 5
Dependent Claim
18 words
A catalyst or precursor according to claim 1 wherein the foam has a megaporosity of at least 60%.
Claim 6
Dependent Claim
22 words
A catalyst or precursor according to claim 1 wherein the megaporosity of the foam is 60 to 90% of the total porosity.
Claim 7
Dependent Claim
26 words
A catalyst or precursor according to claim 1 wherein the ceramic material comprises alumina, iron oxide, an iron oxide chromia mixture, zinc oxide, or a zeolite.
Claim 8
Dependent Claim
36 words
A catalyst or precursor according to claim 1 comprising a ceramic foam support impregnated with a catalytically active material or with a material convertible thereto by at least one step selected from heating, reduction, and oxidation.
Claim 9
Dependent Claim
32 words
A catalyst or precursor according to claim 7 comprising a ceramic foam support impregnated with at least one alkali, or alkaline earth, metal oxide, or with a material convertible thereto by heating.
Claim 10
Dependent Claim
38 words
A catalyst or precursor according to claim 1 wherein the ceramic foam comprises a major amount, by weight, of oxides of one or more metals selected from iron, cobalt, nickel, copper, vanadium, molybdenum, tungsten, chromium, manganese, and zinc.
Claim 11
Dependent Claim
61 words
A steam reforming catalyst or precursor according to claim 6 wherein the catalytically active material comprises at least one metal selected from nickel and cobalt, or the material convertible to catalytically active material comprises at least compound selected from reducible nickel and cobalt compounds, and said catalytically active material, or material convertible thereto, is supported on a foam of alpha alumina.
Claim 12
Dependent Claim
125 words
A process for the production of a catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam, said process comprising forming said ceramic foam by forming a negative replica of an open cell organic plastics foam by impregnating said foam with a thixotropic dispersion of a particulate ceramic material in a carrier liquid so that the pores of the foam are filled with said dispersion, drying said impregnated foam without removing ceramic material from the pores thereof, heating said foam in air to remove the organic plastics foam and to cause the ceramic particles to sinter.
Claim 13
Dependent Claim
125 words
A process for the production of a catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam, said process comprising forming said ceramic foam by forming a negative replica of an open cell organic plastics foam by impregnating said foam with a thixotropic dispersion of a particulate ceramic material in a carrier liquid so that the pores of the foam are filled with said dispersion, drying said impregnated foam without removing ceramic material from the pores thereof, heating said foam in air to remove the organic plastics foam and to cause the ceramic particles to sinter.
Claim 14
Dependent Claim
67 words
A process according to claim 11 for the production of a catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, is supported on, a ceramic foam, wherein after forming said ceramic foam it is impregnated with said catalytically active material or with material convertible thereto.
Claim 15
Dependent Claim
110 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises a ceramic foam containing a major amount, by weight, of oxides of one or more metals selected from iron, cobalt, nickel, copper, vanadium, molybdenum, tungsten, chromium, manganese, and zinc, said ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 .
Claim 16
Dependent Claim
110 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises a ceramic foam containing a major amount, by weight, of oxides of one or more metals selected from iron, cobalt, nickel, copper, vanadium, molybdenum, tungsten, chromium, manganese, and zinc, said ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 .
Claim 17
Dependent Claim
94 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 , and the megaporosity constitutes 60-90% of the total porosity.
Claim 18
Dependent Claim
94 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, comprises, or is supported on, a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 , and the megaporosity constitutes 60-90% of the total porosity.
Claim 19
Dependent Claim
83 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, is supported on a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 .
Claim 20
Dependent Claim
83 words
A catalyst containing a catalytically active material, or a precursor to such a catalyst containing a material convertible to catalytically active material, wherein said catalytically active material, or said material convertible thereto, is supported on a ceramic foam having a network of irregular passages extending therethrough, said passages having an average minimum dimension in the range 20 to 300 μm, said foam having a total porosity in the range 40 to 85% and an apparent density of at least 0.7 g.cm -3 .
Claim 21
Dependent Claim
64 words
A process according to claim 12 for forming a steam reforming catalyst precursor comprising forming the calcined ceramic negative replica of the plastics foam from a silica-free ceramic material and impregnating the ceramic foam with at least one metal nitrate including at least one nitrate selected from nickel and cobalt nitrates, and calcining the impregnated replica to decompose the nitrates to the corresponding oxides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-03-06 | 1992-09-05 | 1993-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-03-06 | 1996-09-05 | 1997-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-03-06 | 2000-09-05 | 2001-03-07 | $7700.00 | Window Closed / Lapsed |