High speed GaAs MESFET having refractory contacts and a self-aligned cold gate fabrication process
Assignee: International Business Machines Corp
•
Filing: 1987-04-20
•
Granted: 1989-02-28
•
Expires: 2007-04-20
Abstract
Abstract Disclosed is a process fo fabrication of a MESFET in which starting with a GaAs substrate having a shallow N- layer covered with nitride, a submicron-wide dummy gate mask consisting of upper and lower portions made of dissimilar materials is formed. Multilayer organic and sidewall image transfer techniques are employed for forming the mask. The nitride is etched using the gate mask. N+ source/drain are formed by ion implantation. The lower portion of the gate mask is etched to expose the periphery of the nitride. Refractory metal for source/drain contacts is deposited. An oxide laeyr is deposited to passivate the source/drain contacts and to fully cover the exposed nitride periphery. The gate mask is removed. High temperature anneal is accomplished to simultaneously activate the N+ regions and anneal the contact metal. By RIE the exposed nitride removed leaving submicron spacers thereof. Gate metal is deposited in the gate region. Excess gate metal is removed to obtain a gate which has a planar top and has little lapping over the source/drain contacts.
Inventors
- 👤 Karanam Balasubramanyam
- 👤 Robert R. Joseph
- 👤 Robert B. Renbeck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:42
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D30/0612; H10D30/0614; H10D30/60; H10D30/67; H10D30/6729; H10D30/6737; H10D30/6738; H10D30/674; H10D30/675; H10D64/00; H10D64/01; H10D64/012; H10D64/0124; H10D64/0125; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01326; H10D64/01328; H10D64/60; H10D64/64; H10P; H10P76/00; H10P76/40; H10P76/408; H10P76/4085; H10D62/00; H10D62/80; H10D62/85; Y; Y10; Y10S; Y10S148/00; Y10S148/02; Y10S438/00; Y10S438/942; Y10S438/947; Y10S438/948; Y10S438/951
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
187 words
Process for forming a MESFET comprising: providing a GaAs substrate having a lightly doped shallow surface layer of a given conductivity type covered by a first insulator layer: forming a submicron-wide mask having bottom and top portions on said first insulator; utilizing said mask, (a) implanting in said substrate ions of said conductivity type forming source and drain regions self-aligned to said mask structure and (b) removing said first insulator not covered by said mask strucure to limit said first insulator to lie over the channel region of said MESFET; reducing the width of the bottom portion of said mask to correspond with the desired MESFET gate length; forming a conductive material over said source and drain regions; nonconformally depositing a second insulator on the resulting structure; removing said mask to expose the portion of said first insulator thereunder; etching said exposed portion of said first insulator to uncover a gate region in said substrate, and forming over said channel region submicron spacers of said first insulator self-aligned to said gate region and said source and drain regions; and forming a gate metal in said gate region.
Claim 2
Dependent Claim
187 words
Process for forming a MESFET comprising: providing a GaAs substrate having a lightly doped shallow surface layer of a given conductivity type covered by a first insulator layer: forming a submicron-wide mask having bottom and top portions on said first insulator; utilizing said mask, (a) implanting in said substrate ions of said conductivity type forming source and drain regions self-aligned to said mask structure and (b) removing said first insulator not covered by said mask strucure to limit said first insulator to lie over the channel region of said MESFET; reducing the width of the bottom portion of said mask to correspond with the desired MESFET gate length; forming a conductive material over said source and drain regions; nonconformally depositing a second insulator on the resulting structure; removing said mask to expose the portion of said first insulator thereunder; etching said exposed portion of said first insulator to uncover a gate region in said substrate, and forming over said channel region submicron spacers of said first insulator self-aligned to said gate region and said source and drain regions; and forming a gate metal in said gate region.
Claim 3
Dependent Claim
30 words
The process as in claim 1 further comprising planarizing said gate metal and said second insulator to obtain a planar gate with little lapping over the source or drain regions.
Claim 4
Dependent Claim
14 words
The process as in claim 1 wherein said gate metal is formed by sputtering.
Claim 5
Dependent Claim
17 words
The process as in claim 1 wherein said submicron-wide mask is formed by sidewall image transfer process.
Claim 6
Dependent Claim
20 words
The process as in claim 1 wherein the top and bottom portions of said mask are composed of dissimilar materials.
Claim 7
Dependent Claim
16 words
The process as in claim 5 wherein said bottom portion is formed of an organic material.
Claim 8
Dependent Claim
34 words
The process as in claim 1 wherein said said step of reducing the width of said bottom portion is accomplished by undercutting the bottom portion relative to said top portion by reactive ion etching.
Claim 9
Dependent Claim
24 words
The process as in claim 1 wherein said undercutting is accomplished to etch off 0.1-0.25 microns thickness on all sides of said bottom portion.
Claim 10
Dependent Claim
15 words
The process as in claim 1 wherein said conductive material is formed by lift-off process.
Claim 11
Dependent Claim
15 words
The process as in claim 1 wherein said second insulator is formed by plasma deposition.
Claim 12
Dependent Claim
16 words
The process as in claim 1 wherein said conductive material is the quadruple layer of In-Ge-Mo-W.
Claim 13
Dependent Claim
32 words
The process as in claim 11 wherein said conductive material is formed by E-beam evaporation of In, Ge, Mo and W in the same evaporation system at the same temperature and pressure.
Claim 14
Dependent Claim
18 words
The process as in claim 12 wherein said evaporation is accomplished by maintaining said substrate at room temperature.
Claim 15
Dependent Claim
14 words
The process as in claim 1 wherein said first insulator is plasma-deposited silicon nitride.
Claim 16
Dependent Claim
13 words
The process as in claim 1 wherein said conductivity type is N type.
Claim 17
Dependent Claim
218 words
Process for forming a GaAs MESFET comprising: providing a GaAs substrate covered with a first insulator layer; forming a submicron-wide dummy gate composed of bottom and top portions made of dissimilar materials on said first insulator; utilizing said dummy gate as a mask, (a) implanting in said substrate ions of a given conductivity type forming source and drain regions self-aligned to said dummy gate and (b) removing said first insulator not masked by said dummy gate to limit said first insulator to lie over the channel reqion of said MESFET; side etching said bottom portion to reduce the width of said bottom portion relative to that of said top portion and thereby exposing a peripheral portion of said first insulator; depositing a conductive material over said source and drain regions while masking said peripheral portion by the top portion of said dummy gate; covering said conductive material and said peripheral portion of said first insulator by depositing a second insulator; removing said dummy gate to expose a central portion of said first insulator; etching off said central portion expose a gate region of said substrate, and forming over said channel region submicron spacers of said first insulator self-aligned to said gate region and said source and drain regions; and forming a conductive gate material in said gate region.
Claim 18
Dependent Claim
218 words
Process for forming a GaAs MESFET comprising: providing a GaAs substrate covered with a first insulator layer; forming a submicron-wide dummy gate composed of bottom and top portions made of dissimilar materials on said first insulator; utilizing said dummy gate as a mask, (a) implanting in said substrate ions of a given conductivity type forming source and drain regions self-aligned to said dummy gate and (b) removing said first insulator not masked by said dummy gate to limit said first insulator to lie over the channel reqion of said MESFET; side etching said bottom portion to reduce the width of said bottom portion relative to that of said top portion and thereby exposing a peripheral portion of said first insulator; depositing a conductive material over said source and drain regions while masking said peripheral portion by the top portion of said dummy gate; covering said conductive material and said peripheral portion of said first insulator by depositing a second insulator; removing said dummy gate to expose a central portion of said first insulator; etching off said central portion expose a gate region of said substrate, and forming over said channel region submicron spacers of said first insulator self-aligned to said gate region and said source and drain regions; and forming a conductive gate material in said gate region.
Claim 19
Dependent Claim
33 words
The process as in claim 16 further comprising forming a shallow and lightly doped region of the first conductivity type on the surface of said substrate prior to covering with said first insulator.
Claim 20
Dependent Claim
21 words
The process as in claim 17 wherein said dummy gate is formed by utilizing multilayer resist and sidewall image transfer techniques.
Claim 21
Dependent Claim
104 words
The process as in claim 17 wherein said dummy gate forming step comprises: forming, in order, first and second layers of photosensitive material on said first insulator; patterning said second layer into a mandrel having substantially vertical surface using an imaging layer and photolithography and etching processes; depositing conformally a third insulator layer of submicron thickness on said patterned second layer and the first layer not masked by said mandrel; establishing a submicron-wide sidewall of said third insulator on said vertical surfaces by anisotropic etching of said third insulator; removing said mandrel; and anisotropically etching said first layer using said sidewall as a mask.
Claim 22
Dependent Claim
36 words
The process as in claim 16 further comprising planarizing said gate material and said second insulator to obtain a top gate surface which is substantially planar and coplanar with the top surface of said second insulator.
References Cited (Backward Citations)
US4229966A
Cited
US4553316A
Cited
US4503599A
Cited
US4546540A
Cited
US4472872A
Cited
US4700455A
Cited
US4694564A
Cited
US4670090A
Cited
US4732871A
Cited
US4731339A
Cited
US4711701A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-28 | 1992-08-29 | 1993-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-28 | 1996-08-29 | 1997-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-28 | 2000-08-29 | 2001-02-28 | $7700.00 | Window Closed / Lapsed |