US4806453A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Positive acting bilayer photoresist development
Assignee: Shipley Co Inc
•
Filing: 1986-05-07
•
Granted: 1989-02-21
•
Expires: 2006-05-07
Abstract
Abstract The invention is for a developer for a bilayer photoresist film comprising a first relatively thick layer of a polyglutarimide and a second relatively thin layer of a diazo sensitized novolak resin. The developer is an aqueous solution of a tetra alkyl ammonium hydroxide where at least two of the alkyl groups have two or more carbon atoms. The developer of the invention permits development of the bottom resist layer without erosion of the top resist layer.
Inventors
- 👤 David A. Vidusek
- 👤 Michael Legenza
- 👤 Jeffery L. Vincent
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:16
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; G03F7/30; G03F7/32; G03F7/322; G03F7/004; G03F7/09; G03F7/094
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
184 words
A process for the exposure and development of a positive acting bilayer photoresist film comprising a bottom planarizing layer of a polyglutarimide photoresist and a top layer of a diazo sensitized novolak photoresist film, said process comprising the steps of i. exposing the top novolak resist layer to activating radiation at a wavelength that does not activate the bottom resist layer to form a latent image in said top layer; ii. developing the top resist layer with a developer that does not dissolve the bottom resist layer to form a conformable mask over the bottom resist layer; iii. exposing the bottom resist layer through the developed top resist layer to a source of activating radiation at a wavelength that does not activate the top resist layer to form a latent image in said bottom layer; and iv. developing the bottom resist layer with an aqueous alkaline solution comprising tetra ethyl ammonium hydroxide solution in a concentration of from 0.5 to 20 weight percent and a quaternary ammonium hydroxide surfactant whereby the botto resist layer is developed within aggressive attack on the top resist layer.
Claim 2
Dependent Claim
184 words
A process for the exposure and development of a positive acting bilayer photoresist film comprising a bottom planarizing layer of a polyglutarimide photoresist and a top layer of a diazo sensitized novolak photoresist film, said process comprising the steps of i. exposing the top novolak resist layer to activating radiation at a wavelength that does not activate the bottom resist layer to form a latent image in said top layer; ii. developing the top resist layer with a developer that does not dissolve the bottom resist layer to form a conformable mask over the bottom resist layer; iii. exposing the bottom resist layer through the developed top resist layer to a source of activating radiation at a wavelength that does not activate the top resist layer to form a latent image in said bottom layer; and iv. developing the bottom resist layer with an aqueous alkaline solution comprising tetra ethyl ammonium hydroxide solution in a concentration of from 0.5 to 20 weight percent and a quaternary ammonium hydroxide surfactant whereby the botto resist layer is developed within aggressive attack on the top resist layer.
Claim 3
Dependent Claim
34 words
The process of claim 1 where the top resist layer has a thickness varying between 0.1 and 1.0 micrometers and the bottom resist layer has a thickness varying between about 1.0 and 3.0 micrometers.
Claim 4
Dependent Claim
23 words
The process of claim 1 where the developer for the top resist layer is an aqueous solution of a tetra ethyl ammonium hydroxide.
Claim 5
Dependent Claim
25 words
The process of claim 1 where the tetra ethyl ammonium hydroxide is present in a concentration of from about 3.0 to 10.0 percent by weight.
Claim 6
Dependent Claim
192 words
A process for the exposure and development of a positive acting bilayer photoresist film comprising a bottom planarizing layer of a polyglutarimide photoresist over a substrate and a top layer of a diazo sensitized novolak photoresist film over the layer of the polyglutarimide resist, said process comprising the steps of i. exposing the top novolak resist layer to activating radiation at a wavelength above 3000 angstroms to form a latent image in said top layer; ii. developing the top resist layer with an aqueous solution of a tetra alkyl ammonium hydroxide developer that does not dissolve the bottom resist layer to form a conformable mask over the bottom resist layer; iii. exposing the bottom resist layer through the developed top resist layer to a source of activating radiation at a wavelength below 3000 angstroms to form a latent image in said bottom layer; and iv. developing the bottom resist layer with an aqueous alkaline solution comprising tetra ethyl ammonium hydroxide solution in a concentration of from 0.5 to 20 weight percent and a quaternary ammonium hydroxide surfactant whereby the bottom resist layer is developed without aggressive attack on the top resist layer.
Claim 7
Dependent Claim
192 words
A process for the exposure and development of a positive acting bilayer photoresist film comprising a bottom planarizing layer of a polyglutarimide photoresist over a substrate and a top layer of a diazo sensitized novolak photoresist film over the layer of the polyglutarimide resist, said process comprising the steps of i. exposing the top novolak resist layer to activating radiation at a wavelength above 3000 angstroms to form a latent image in said top layer; ii. developing the top resist layer with an aqueous solution of a tetra alkyl ammonium hydroxide developer that does not dissolve the bottom resist layer to form a conformable mask over the bottom resist layer; iii. exposing the bottom resist layer through the developed top resist layer to a source of activating radiation at a wavelength below 3000 angstroms to form a latent image in said bottom layer; and iv. developing the bottom resist layer with an aqueous alkaline solution comprising tetra ethyl ammonium hydroxide solution in a concentration of from 0.5 to 20 weight percent and a quaternary ammonium hydroxide surfactant whereby the bottom resist layer is developed without aggressive attack on the top resist layer.
Claim 8
Dependent Claim
34 words
The process of claim 5 where the top resist layer has a thickness varying between 0.1 and 1.0 micrometers and the bottom resist layer has a thickness varying between about 1.0 and 3.0 micrometers.
Claim 9
Dependent Claim
24 words
The process of claim 5 where the tetra alkyl ammonium hydroxide used to develo the top resist layer is a tetra methyl ammonium hydroxide.
Claim 10
Dependent Claim
25 words
The process of claim 5 where the tetra ethyl ammonium hydroxide is present in a concentration of from about 3.0 to 10.0 percent by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-21 | 1992-08-22 | 1993-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-21 | 1996-08-22 | 1997-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-21 | 2000-08-22 | 2001-02-21 | $7700.00 | Window Closed / Lapsed |