Hot dip aluminum coated chromium alloy steel
Assignee: Armco Inc
•
Filing: 1987-02-20
•
Granted: 1989-01-24
•
Expires: 2007-02-20
Abstract
Abstract Continuously hot dip aluminum coated ferritic chromium alloy steel strip. After the steel has been given a pretreatment to remove surface contaminants, the steel is protected in a hydrogen atmosphere until it is passed into the molten aluminum coating metal. The coating metal readily wets the steel surface to prevent uncoated areas or pin holes in the coating layer.
Inventors
- 👤 Farrell M. Kilbane
- 👤 Richard A. Coleman
- 👤 Frank C. Dunbar
- 👤 Alan F. Gibson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:10
CPC Classifications
C; C23; C23C; C23C2/00; C23C2/04; C23C2/12; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12736; Y10T428/1275; Y10T428/12757; Y10T428/12771; Y10T428/12861; Y10T428/12951; Y10T428/12972; Y10T428/12979
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
70 words
A ferrous base ferritic strip continuously hot dip coated with a coating metal; comprising: the strip including at least about 6% by weight chromium, the coating metal consisting essentially of aluminum, the coating layer on said strip being substantially free of uncoated areas and formed without a thick brittle Fe-Al alloy inner layer, said coating layer being tightly adherent to said strip and resistant to crazing or flaking during bending.
Claim 2
Dependent Claim
70 words
A ferrous base ferritic strip continuously hot dip coated with a coating metal; comprising: the strip including at least about 6% by weight chromium, the coating metal consisting essentially of aluminum, the coating layer on said strip being substantially free of uncoated areas and formed without a thick brittle Fe-Al alloy inner layer, said coating layer being tightly adherent to said strip and resistant to crazing or flaking during bending.
Claim 3
Dependent Claim
20 words
The strip as set forth in claim 1 wherein the base metal includes at least about 10% by weight chromium.
Claim 4
Dependent Claim
18 words
The strip as set forth in claim 2 wherein said base metal includes substantially 0% by weight nickel.
Claim 5
Dependent Claim
26 words
The strip as set forth in claim 2 wherein said base metal includes 10.0%-14.5% by weight chromium, 0.1%-1.0% by weight silicon and 0.2%-0.5% by weight titanium.
References Cited (Backward Citations)
US2082622A
Cited
US2197622A
Cited
US2570906A
Cited
US3468695A
Cited
US3396048A
Cited
US3320085A
Cited
US3378359A
Cited
US3728144A
Cited
US4053663A
Cited
US3907611A
Cited
JPS4999982A
Cited
US3925579A
Cited
US4040981A
Cited
US4079157A
Cited
US4150178A
Cited
US4155235A
Cited
CA1083437A
Cited
JPS5726187A
Cited
EP0134143A1
Cited
US4601999A
Cited
US4535034A
Cited
US4675214A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-01-24 | 1992-07-25 | 1993-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-01-24 | 1996-07-25 | 1997-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-01-24 | 2000-07-25 | 2001-01-24 | $7700.00 | Window Closed / Lapsed |