Epoxy resin compositions for use in low temperature curing applications

Claim 2

A composition which comprises (A) an epoxy resin composition containing, as the only epoxy-containing component in said composition, a mixture of (1) at least one diglycidyl ether of a compound having 2 aromatic hydroxyl groups per molecule, said diglycidyl ether having an average of not more than 2 vicinal epoxy groups per molecule and an EEW of from about 170 to about 600; (2) at least one polyglycidyl ether of a compound having an average of more than two aromatic hydroxyl groups per molecule, said polyglycidyl ether having an EEW of from about 150 to about 350; and (3) a rubber or elastomer; wherein components (1) and (2) are employed in amounts such that from about 20 to about 90 percent of the glycidyl ether groups are derived from component (1) and from about 10 to about 80 percent of the glycidyl ether groups are derived from component (2) and component (3) is employed in an amount of from 2 to about 20 percent by weight based on the combined weight of components (1), (2) and (3); and (B) optionally, as a reactive diluent to lower the viscosity of the composition, a low viscosity monoglycidyl ether compound or a low viscosity polyglycidyl ether of a compound having two or more aliphatic hydroxyl groups per molecule; and wherein component (B) is employed in an amount of from zero to about 25 percent by weight based on the combined weight of components (A) and (B).

Claim 3

A composition of claim 1 wherein components (A-1) and (A-2) are employed in amounts such that from about 50 to about 90 percent of the glycidyl ether groups are derived from component (A-1) and from about 10 to about 50 percent of the glycidyl ether groups are derived from component (A-2); component (A-3) is employed in an amount of from about 2 to about 15 percent by weight of the combined weight of components (A-1), (A-2) and (A-3); component (B) is employed in an amount of from about 2 to about 25 percent by weight based on the weight of components (A) and (B).

Claim 4

A composition of claim 2 wherein components (A-1) and (A-2) are employed in amounts such that from about 60 to about 80 percent of the glycidyl ether groups are derived from component (A-1) and from about 20 to about 40 percent of the glycidyl ether groups are derived from component (A-2); component (A-3) is employed in an amount of from about 3 to about 10 percent by weight of the combined weight of components (A-1), (A-2) and (A-3); component (B) is employed in an amount of from about 5 to about 15 percent by weight based on the weight of components (A) and (B).

Claim 5

A composition of claim 1, 2 or 3 wherein (a) component (A-1) is an epoxy resin or mixture of epoxy resins represented by the following formulas I, II or III ##STR4## wherein A is a divalent hydrocarbyl group having from 1 to about 6 carbon atoms, --O--, --S--, --S--S--, --SO--, --SO 2 --, --CO-- or --O--CO--; each R is independently hydrogen or an alkyl group having from 1 to about 4 carbon atoms; each X is independently hydrogen, a hydrocarbyl group or substituted hydrocarbyl group having from 1 to about 10 carbon atoms, a halogen atom, or a nitro group, n has a value of zero or 1; and n' has an average value from zero to about 3; n" has an average value from 1 to about 12; (b) component (A-2) is an epoxy resin or mixture of epoxy resins represented by the following formulas IV, V or VI ##STR5## wherein each R, X and n" are as previously defined; each A' is independently a divalent hydrocarbyl or substituted hydrocarbyl group having from 1 to about 12 carbon atoms; R' is hydrogen or a monovalent hydrocarbyl group or substituted monovalent hydrocarbyl group having from 1 to about 4 carbon atoms; m has a value from about 0.01 to about 12; m' has a value from about 1.01 to about 12; and m" has a value from zero to about 10;.

Claim 6

A composition of claim 4 wherein (a) component (A-1) is an epoxy resin or mixture of epoxy resins represented by formula II wherein A is a divalent hydrocarbyl group having from 1 to about 6 carbon atoms; each R is hydrogen; each X is independently hydrogen, a hydrocarbyl group having from 1 to about 6 carbon atoms or a halogen atom; n has a value of 1; n' has an average value from zero to about 1.5; and (b) component (A-2) is an epoxy resin or mixture of epoxy resins represented by formulas IV or B wherein R and X are as defined in (a); n" has an average value of from about 1 to about 6; each A' is a methylene group; m has an average value from 1 to about 6 and m' has an average value from about 2 to about 6.

Claim 7

A composition of claim 5 wherein (a) in component (A-1), A is a divalent hydrocarbyl group having from 1 to about 3 carbon atoms; each X is independently hydrogen or a hydrocarbyl group having from 1 to about 3 carbon atoms; and n' has a value from zero to about 0.5; (b) in component (A-2), n" has an average value of from about 1 to about 3; m has an average value from about 1 to about 3; m' has an average value from about 2 to about 3; and (c) the rubber or elastomer, component (A-3), is poly(2-ethylhexylacrylate) copolymer rubber, grafted rubber particles or combinations thereof.

Claim 8

A composition of claim 6 wherein (a) component (A-1) is a diglycidyl ether of bisphenol A; and (b) component (A-2) is a phenol-formaldehyde or a cresol-formaldehyde epoxy novolac resin or a polyglycidyl ether of an adduct of dicyclopentadiene and phenol or cresol.

Claim 9

A low temperature curable composition which comprises (A) an epoxy resin composition containing, as the only epoxy-containing component in said composition, a mixture of (1) at least one diglycidyl ether of a compound having 2 aromatic hydroxyl groups per molecule, said diglycidyl ether having an average of not more than 2 vicinal epoxy groups per molecule and an EEW of from about 170 to about 600; (2) at least one polyglycidyl ether of a compound having an average of more than two aromatic hydroxyl groups per molecule, said polyglycidyl ether having an EEW of from about 150 to about 350; and (3) a rubber or elastomer; wherein components (1) and (2) are employed in amounts such that from about 20 to about 90 percent of the glycidyl ether groups are derived from component (1) and from about 10 to about 80 percent of the glycidyl ether groups are derived from component (2) and component (3) is employed in an amount of from 2 to about 20 percent by weight based on the combined weight of components (1), (2) and (3); (B) optionally, as a reactive diluent to lower the viscosity of the composition, a low viscosity monoglycidyl ether compound or a low viscosity polyglycidyl ether of a compound having two or more aliphatic hydroxyl groups per molecule; (C) at least one cycloaliphatic amine hardener; (D) optionally, an accelerator for component (C); and wherein component (B) is employed in an amount of from about zero to about 25 percent by weight based upon the combined weight of components (A) and (B); component (C) is employed in an amount which provides a ratio of equivalents of component (C) per epoxide equivalent of components (A) and (B) combined of from about 0.95:1 to about 1.2:1; and component (D) is employed in an amount of from zero to about 5 percent by weight based upon the combined weight of components (A), (B), (C) and (D).

Claim 10

A low temperature curable composition which comprises (A) an epoxy resin composition containing, as the only epoxy-containing component in said composition, a mixture of (1) at least one diglycidyl ether of a compound having 2 aromatic hydroxyl groups per molecule, said diglycidyl ether having an average of not more than 2 vicinal epoxy groups per molecule and an EEW of from about 170 to about 600; (2) at least one polyglycidyl ether of a compound having an average of more than two aromatic hydroxyl groups per molecule, said polyglycidyl ether having an EEW of from about 150 to about 350; and (3) a rubber or elastomer; wherein components (1) and (2) are employed in amounts such that from about 20 to about 90 percent of the glycidyl ether groups are derived from component (1) and from about 10 to about 80 percent of the glycidyl ether groups are derived from component (2) and component (3) is employed in an amount of from 2 to about 20 percent by weight based on the combined weight of components (1), (2) and (3); (B) optionally, as a reactive diluent to lower the viscosity of the composition, a low viscosity monoglycidyl ether compound or a low viscosity polyglycidyl ether of a compound having two or more aliphatic hydroxyl groups per molecule; (C) at least one cycloaliphatic amine hardener; (D) optionally, an accelerator for component (C); and wherein component (B) is employed in an amount of from about zero to about 25 percent by weight based upon the combined weight of components (A) and (B); component (C) is employed in an amount which provides a ratio of equivalents of component (C) per epoxide equivalent of components (A) and (B) combined of from about 0.95:1 to about 1.2:1; and component (D) is employed in an amount of from zero to about 5 percent by weight based upon the combined weight of components (A), (B), (C) and (D).

Claim 11

A low temperature curable composition of claim 8 wherein components (A-1) and (A-2) are employed in amounts such that from about 50 to about 90 percent of the glycidyl ether groups are derived from component (A-1) and from about 10 to about 50 percent of the glycidyl ether groups are derived from component (A-2); component (A-3) is employed in an amount of from about 2 to about 15 percent by weight of the combined weight of components (A-1), (A-2) and (A-3); component (B) is employed in an amount of from about 2 to about 25 percent by weight based on the weight of components (A) and (B); component (C) is employed in amounts which provide a ratio of equivalents of component (C) per epoxide equivalent of components (A) and (B) combined of from about 0.95:1 to about 1.15:1; and component (D) is employed in an amount of from about 0.05 to about 2.5 percent by weight based upon the combined weight of components (A), (B), (C) and (D).

Claim 12

A low temperature curable composition of claim 9 wherein components (A-1) and (A-2) are employed in amounts such that from about 60 to about 80 percent of the glycidyl ether groups are derived from component (A-1) and from about 20 to about 40 percent of the glycidyl ether groups are derived from component (A-2); component (A-3) is employed in an amount of from about 3 to about 10 percent by weight of the combined weight of components (A-1), (A-2) and (A-3); component (B) is employed in an amount of from about 5 to about 15 percent by weight based on the weight of components (A) and (B); component (C) is employed in an amount which provides a ratio of equivalents of component (C) per epoxide equivalent of components (A) and (B) combined of from about 1:1 to about 1.15:1; and component (D) is employed in an amount of from about 0.5 to about 2 percent by weight based upon the combined weight of components (A), (B), (C) and (D).

Claim 13

A low temperature curable composition of claim 8, 9 or 10 wherein (a) component (A-1) is an epoxy resin or mixture of epoxy resins represented by the following formulas I, II or III ##STR6## wherein A is a divalent hydrocarbyl group having from 1 to about 6 carbon atoms, --O--, --S--, --S--S--, --SO--, --SO 2 --, --CO-- or --O--CO--; each R is independently hydrogen or an alkyl group having from 1 to about 4 carbon atoms; each X is independently hydrogen, a hydrocarbyl group or substituted hydrocarbyl group having from 1 to about 6 carbon atoms, a halogen atom, or a nitro group; n has a value of zero or 1; and n' has an average value from zero to about 1.5; n" has an average value from 1 to about 6; (b) component (A-2) is an epoxy resin or mixture of epoxy resins represented by the following formulas IV, V or VI ##STR7## wherein A is a divalent hydrocarbyl group having from 1 to about 6 carbon atoms, --O--, --S--, --S--S--, --SO--, --SO 2 --, --CO-- or --O--CO--; each R is independently hydrogen or an alkyl group having from 1 to about 4 carbon atoms; each X is independently hydrogen, a hydrocarbyl group or substituted hydrocarbyl group having from 1 to about 10 carbon atoms, a halogen atom, or a nitro group; n has a value of zero or 1; and n' has an average value from zero to about 3; n" has an average value from 1 to about 12; and (c) component (C) is a curing agent or mixture of curing agents represented by the following formulas VII or VIII ##STR8## wherein each A and n is as defined above and each X' is independently hydrogen or an alkyl group having suitably from 1 to about 12, more suitably from 1 to about 6, most suitably from 1 to about 3, carbon atoms.

Claim 14

A low temperature curable composition of claim 11 wherein (a) component (A-1) is an epoxy resin or mixture of epoxy resins represented by formula II wherein A is a divalent hydrocarbyl group having from 1 to about 6 carbon atoms; each R is hydrogen; each X is independently hydrogen, a hydrocarbyl group having from 1 to about 6 carbon atoms or a halogen atom; n has a value of 1; n' has an average value from zero to about 1.5; (b) component (A-2) is an epoxy resin or mixture of epoxy resins represented by formulas IV or V wherein R and X are as defined in (a); n" has an average value of from about 1 to about 6; each A' is a methylene group; m has an average value from 1 to about 6 and m' has an average value from about 2 to about 6; and (c) component (C) is a curing agent or mixture of curing agents represented by formulas VII or VIII wherein A is --CH 2 --; n has a value of xero or 1; and each X' is independently hydrogen or an alkyl group having from 1 to about 3 carbon atoms.

Claim 15

A low temperature curable composition of claim 12 wherein (a) in component (A-1), A is a divalent hydrocarbyl group having from 1 to about 3 carbon atoms; each X is independently hydrogen or a hydrocarbyl group having from 1 to about 3 carbon atoms; and n' has a value from zero to about 0.5; (b) in component (A-2), n" has an average value of from about 1 to about 3; m has an average value from about 1 to about 3; m' has an average value from about 2 to about 3; (c) the rubber or elastomer, component (A-3), is poly(2-ethylhexylacrylate) copolymer rubber, grafted rubber particles or combinations thereof; and (d) component (C) is a compound represented by formula VII.

Claim 16

A low temperature curable composition of claim 13 wherein (a) component (A-1) is a diglycidyl ether of bisphenol A; (b) component (A-2) is a phenol-formaldehyde or a cresol-formaldehyde epoxy novolac resin or a polyglycidyl ether of an adduct of dicyclopentadiene and phenol or cresol; and (c) the rubber or elastomer, component (A-3), is poly(2-ethylhexylacrylate) copolymer rubber; (d) component (C) is diaminocyclohexane; and (e) the catalyst or accelerator is 2-ethyl-4-methylimidazole.

Claim 17

An article resulting from curing the composition of claim 8, 9 or 10 which also contains a reinforcing agent.

Claim 18

An article of claim 15 wherein the reinforcing agent is glass, aramid or graphite in woven, mat or roving form.

Claim 19

An article resulting from curing the composition of claim 11 which also contains a reinforcing agent.

Claim 20

An article of claim 17 wherein the reinforcing agent is glass, aramid or graphite in woven, mat or roving form.

Claim 21

An article resulting from curing the composition of claim 12 which also contains a reinforcing agent.

Claim 22

An article of claim 19 wherein the reinforcing agent is glass, aramid or graphite in woven, mat or roving form.

Claim 23

An article resulting from curing the composition of claim 13 which also contains a reinforcing agent.

Claim 24

An article of claim 21 wherein the reinforcing agent is glass, aramid or graphite in woven, mat or roving form.

Claim 25

An article resulting from curing the composition of claim 14 which also contains a reinforcing agent.

Claim 26

An article of claim 23 wherein the reinforcing agent is glass, aramid or graphite in woven, mat or roving form.