Process for preparation of composite materials containing nonmetallic particles in a metallic matrix, and composite materials made thereby
Assignee: Novelis Corp
•
Filing: 1986-05-01
•
Granted: 1988-11-22
•
Expires: 2006-05-01
Abstract
Abstract A method and apparatus for preparing cast composite materials of nonmetallic particles in a metallic matrix, wherein particles are mixed into a molten metallic alloy to wet the molten metal to the particles, and the particles and metal are sheared past each other to promote wetting of the particles by the metal. The mixing occurs while minimizing the introduction of gas into the mixture, and while minimizing the retention of gas at the particle-liquid interface. Mixing is done at a maximum temperature whereat the particles do not substantially chemically degrade in the molten metal during the time required for processing, and casting is done at a temperature sufficiently high that there is no solid metal present in the melt. Mixing is preferably accomplished with a dispersing impeller, or a dispersing impeller used with a sweeping impeller.
Inventors
- 👤 Michael D. Skibo
- 👤 David M. Schuster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:02
CPC Classifications
C; C22; C22C; C22C21/00; F; F27; F27D; F27D27/00; B; B01; B01F; B01F27/00; B01F27/80; B01F27/84; C22C1/00; C22C1/10; C22C1/1005; C22C1/1036; C22C1/1047; C22C1/12; C22C32/00; C22C32/001; C22C32/0015; C22C32/0036; C22C32/0047; C22C32/0052; C22C32/0063; F27D3/00; F27D3/0025; F27D3/0026; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12486
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
159 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic refractory material, comprising: melting the metallic material; adding particles of the nonmetallic material to the molten metal; mixing together the molten metal and the particles of the nonmetallic material to wet the molten metal to the particles, under conditions that the particles are distributed throughout the volume of the melt and the particles and the metallic melt are sheared past each other to promote wetting of the particles by the melt, said mixing to occur while minimizing the introduction of any gas into, and while minimizing the retention of any gas within, the mixture of particles and molten metal, and at a temperature whereat the particles do not substantially chemically degrade in the molten metal in the time required to complete said step of mixing; and casting the resulting mixture at a casting temperature sufficiently high that substantially no solid metal is present.
Claim 2
Independent Claim
159 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic refractory material, comprising: melting the metallic material; adding particles of the nonmetallic material to the molten metal; mixing together the molten metal and the particles of the nonmetallic material to wet the molten metal to the particles, under conditions that the particles are distributed throughout the volume of the melt and the particles and the metallic melt are sheared past each other to promote wetting of the particles by the melt, said mixing to occur while minimizing the introduction of any gas into, and while minimizing the retention of any gas within, the mixture of particles and molten metal, and at a temperature whereat the particles do not substantially chemically degrade in the molten metal in the time required to complete said step of mixing; and casting the resulting mixture at a casting temperature sufficiently high that substantially no solid metal is present.
Claim 3
Dependent Claim
13 words
The method of claim 1, wherein the metallic material is an aluminum alloy.
Claim 4
Dependent Claim
29 words
The method of claim 1, wherein the nonmetallic material is a refractory ceramic selected from the group consisting of a metal oxide, metal nitride, metal carbide, and metal silicide.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein the nonmetallic material is selected from the group consisting of silicon carbide, aluminum oxide, boron carbide, silicon nitride and boron nitride.
Claim 6
Dependent Claim
33 words
The method of claim 1, wherein additions of volatile constituents of the metallic material are made to the metallic material to compensate for loss of the volatile constitutents during preparation of the composite.
Claim 7
Dependent Claim
39 words
The method of claim 1, wherein the molten metal is maintained in a temperature range of from about the liquidus temperature of the metal to about 20° C. above the liquidus temperature throughout said steps of adding and mixing.
Claim 8
Dependent Claim
24 words
The method of claim 1, wherein said step of mixing is conducted with a vacuum applied to the mixture of molten metal and particles.
Claim 9
Dependent Claim
17 words
The method of claim 1, wherein said step of mixing is accomplished by a rotating dispersing impeller.
Claim 10
Dependent Claim
27 words
The method of claim 8, wherein the dispersing impeller is rotated at a rate of from about 500 to about 3000 revolutions per minute in the mixture.
Claim 11
Dependent Claim
80 words
The method of claim 1, wherein said step of mixing is accomplished by a mixing head having a rotating dispersing impeller and a rotating sweeping impeller, the dispersing impeller being immersed in the central region of the melt and shearing the particles and the molten metal past each other without introducing gas into the mixture and the sweeping impeller contacting the periphery of the melt and promoting movement of particles and molten metal into the vicinity of the dispersing impeller.
Claim 12
Dependent Claim
10 words
A composite material prepared by the process of claim 1.
Claim 13
Independent Claim
154 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic material, comprising: forming a mixture of the molten metallic alloy and the particles; maintaining the mixture in a temperature range of from about the liquidus temperature of the metallic material to a temperature whereat the particles do not substantially degrade during the time required for the subsequent processing steps; mixing together the particles and the molten metal for a time sufficient to wet the molten metal to the particles and to distribute the particles throughout the molten metal, using a rotating dispersing impeller immersed in the molten mixture to shear the particles and the molten metal past each other while minimizing the introduction of gas into the mixture and while minimizing the retention of gas already present in the mixture, said step of mixing to occur with a vacuum applied to the mixture; and casting the resulting mixture.
Claim 14
Independent Claim
154 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic material, comprising: forming a mixture of the molten metallic alloy and the particles; maintaining the mixture in a temperature range of from about the liquidus temperature of the metallic material to a temperature whereat the particles do not substantially degrade during the time required for the subsequent processing steps; mixing together the particles and the molten metal for a time sufficient to wet the molten metal to the particles and to distribute the particles throughout the molten metal, using a rotating dispersing impeller immersed in the molten mixture to shear the particles and the molten metal past each other while minimizing the introduction of gas into the mixture and while minimizing the retention of gas already present in the mixture, said step of mixing to occur with a vacuum applied to the mixture; and casting the resulting mixture.
Claim 15
Dependent Claim
13 words
The method of claim 12, wherein the metallic material is an aluminum alloy.
Claim 16
Dependent Claim
29 words
The method of claim 12, wherein the nonmetallic material is a refractory ceramic selected from the group consisting of a metal oxide, metal nitride, metal carbide, and metal silicide.
Claim 17
Dependent Claim
27 words
The method of claim 12, wherein the nonmetallic material is selected from the group consisting of silicon carbide, aluminum oxide, boron carbide, silicon nitride, and boron nitride.
Claim 18
Dependent Claim
30 words
The method of claim 12, wherein the molten metal is maintained in a temperature range of from about the liquidus of the metal to about 20° C. above the liquidus.
Claim 19
Dependent Claim
30 words
The method of claim 12, wherein a sweeping impeller is also immersed into the molten mixture to move the particulate and molten metal into the vicinity of the dispersing impeller.
Claim 20
Dependent Claim
19 words
The method of claim 17, wherein the dispersing impeller rotates at a greater rate than does the sweeping impeller.
Claim 21
Dependent Claim
10 words
A composite material made by the process of claim 12.
Claim 22
Independent Claim
131 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic material, comprising: forming a mixture of the metallic alloy and the particles in a crucible, under vacuum, and at a temperature above the liquidus of the metallic alloy; mixing together the particles and the molten metal with an impeller which is positioned below the surface of the melt and which is operated to avoid a vortex at the surface of the melt, said step of mixing to occur at a temperature above the liquids of the metallic alloy and for a time sufficient to wet the molten metallic alloy to the particles and to distribute the particles throughout the molten metallic alloy, with a vacuum applied to the molten mixture; and casting the resulting mixture.
Claim 23
Independent Claim
131 words
A method for preparing a composite of a metallic alloy reinforced with particles of a nonmetallic material, comprising: forming a mixture of the metallic alloy and the particles in a crucible, under vacuum, and at a temperature above the liquidus of the metallic alloy; mixing together the particles and the molten metal with an impeller which is positioned below the surface of the melt and which is operated to avoid a vortex at the surface of the melt, said step of mixing to occur at a temperature above the liquids of the metallic alloy and for a time sufficient to wet the molten metallic alloy to the particles and to distribute the particles throughout the molten metallic alloy, with a vacuum applied to the molten mixture; and casting the resulting mixture.
Claim 24
Dependent Claim
13 words
The method of claim 20, wherein the metallic material is an aluminum alloy.
Claim 25
Dependent Claim
29 words
The method of claim 20, wherein the nonmetallic material is a refractory ceramic selected from the group consisting of a metal oxide, metal nitride, metal carbide, and metal silicide.
Claim 26
Dependent Claim
12 words
The method of claim 20, wherein the nonmetallic material is silicon carbide.
Claim 27
Dependent Claim
12 words
The method of claim 20, wherein the nonmetallic material is aluminum oxide.
Claim 28
Dependent Claim
10 words
A composite material prepared by the method of claim 29.
References Cited (Backward Citations)
US2375211A
Cited
US2793949A
Cited
DE1433420A1
Cited
US3227547A
Cited
US3454455A
Cited
US3759708A
Cited
US3468658A
Cited
US3432295A
Cited
US3515542A
Cited
US3889348A
Cited
US3728108A
Cited
US3626073A
Cited
US3753694A
Cited
US3887365A
Cited
US3961945A
Cited
US3858640A
Cited
US3888661A
Cited
US4060412A
Cited
US4080200A
Cited
US4318438A
Cited
US4383970A
Cited
US4259112A
Cited
US4489138A
Cited
US4492265A
Cited
US4463058A
Cited
US4452865A
Cited
US4473103A
Cited
US4435213A
Cited
US4450207A
Cited
US4481031A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-22 | 1992-05-23 | 1992-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-22 | 1996-05-23 | 1996-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-22 | 2000-05-23 | 2000-11-22 | $7700.00 | Window Closed / Lapsed |