Process for encapsulating microelectronic semi-conductor and layer type circuits
Assignee: Airbus Defence and Space GmbH
•
Filing: 1985-11-18
•
Granted: 1988-11-15
•
Expires: 2005-11-18
Abstract
Abstract A process for encapsulating microelectronic hybrid semi-conductor circuits or microelectronic semi-conductor components in which the components, located on a substrate, receive a soft, sealable poured-on plastic coating, are covered with a plastic/metal composite film or foil and are, if necessary, then encapsulated with a hard synthetic resin sealing compound which is resistant to thermal shock. The external plastic layers of the film or foil combine with the filler or sealing compound and thus form an encapsulation which is temperature and moisture resistant.
Inventors
- 👤 Werner Moeller
- 👤 Harald von Luettichau
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 05:44
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/10; H10W74/111; H10W74/121; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/284; H10W74/01; H10W74/114; H10W72/00; H10W72/50; H10W72/531; H10W72/5363; H10W72/551; H10W72/552; H10W72/5522; H10W72/5524; H10W90/00; H10W90/701; H10W90/751; H10W90/754; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/4913; Y10T29/49146
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
164 words
A process for encapsulating microelectronic hybrid semi-conductor circuits or microelectronic semi-conductor components, comprising the following steps: pour-coating the components (B) located on a substrate (S) with a soft, sealable plastic filling layer (W) to form an intermediate embedded product in which said component is hermetically enclosed on said substrate, covering said intermediate product with a plastic-metal-plastic composite film or foil (F) comprising three layers, of which a first plastic layer comprises a sealable polyolefin, preferably polypropylene, with a layer thickness of 10-100μ, of which a second layer comprises a deformable metal with a layer thickness of 0.25-250μ, and of which a third layer comprises an adhesive polyester with a layer thickness of 1-100μ, and then encapsulating the pour-coated and covered component with synthetic resin (H) so that the first plastic layer of the film or foil is connected and intimately bonded to the sealable plastic filling layer (W) and so that the third layer is connected and intimately bonded to the synthetic resin (H).
Claim 2
Dependent Claim
164 words
A process for encapsulating microelectronic hybrid semi-conductor circuits or microelectronic semi-conductor components, comprising the following steps: pour-coating the components (B) located on a substrate (S) with a soft, sealable plastic filling layer (W) to form an intermediate embedded product in which said component is hermetically enclosed on said substrate, covering said intermediate product with a plastic-metal-plastic composite film or foil (F) comprising three layers, of which a first plastic layer comprises a sealable polyolefin, preferably polypropylene, with a layer thickness of 10-100μ, of which a second layer comprises a deformable metal with a layer thickness of 0.25-250μ, and of which a third layer comprises an adhesive polyester with a layer thickness of 1-100μ, and then encapsulating the pour-coated and covered component with synthetic resin (H) so that the first plastic layer of the film or foil is connected and intimately bonded to the sealable plastic filling layer (W) and so that the third layer is connected and intimately bonded to the synthetic resin (H).
Claim 3
Dependent Claim
46 words
The process of claim 1, wherein a high-purity, relative to the circuit components inert, low-viscosity, flexible epoxy resin with adhesive properties appropriate for the semi-conductor circuit and composite films or foils is used as a filling in the pour-coating step to form said filling layer (W).
Claim 4
Dependent Claim
48 words
The process of claim 1, wherein a high-purity, soft, with respect to the semi-conductor circuit inert, hot-sealable coating, especially made of modified silicone containing polyolefin or of silicone adhesive on a silicone-fluorine base, is used as a filling in the pour-coating step to form said filling layer (W).
Claim 5
Dependent Claim
43 words
The process of claim 1, wherien the plastic-metal-plastic composite is made of a base and film or foil by means of a hot-sealing deformation at temperatures of 30°-250° C. and at pressures of 1-50 bar outside of the wiring and the bonding points.
Claim 6
Dependent Claim
20 words
The process of claim 1, further comprising using heatable hollow stamps (ST) or matrix dies for the heating and deformation.
Claim 7
Dependent Claim
14 words
The process of claim 5, further comprising pour-coating the composite film or foil encapsulation.
Claim 8
Dependent Claim
158 words
A process for encapsulating microelectronic hybrid semi-conductor circuits or microelectronic semi-conductor components, comprising the following steps: by pour-coating the components (B) located on a substrate (S) with a soft sealable plastic filling layer (W), to form an intermediate embedded product, covering said intermediate product with plastic-metal composite film or foil (F) comprising two layers of which a first plastic layer comprises a sealable polyolefin with a layer thickness of 10-100μ, and of which a second metal layer comprises a deformable and solderable metal with a layer thickness of 0.25-250μ, folding the film or foil with the first plastic layer to the inside and hermetically soldering the second metal layer to a soldering ring (LK) previously printed on the substrate (S), and then encapsulating the component and film or foil with synthetic resin (H) so that said first plastic layer is intimately bonded to said filling layer (W), and said metal layer is intimately bonded to said synthetic resin.
Claim 9
Dependent Claim
158 words
A process for encapsulating microelectronic hybrid semi-conductor circuits or microelectronic semi-conductor components, comprising the following steps: by pour-coating the components (B) located on a substrate (S) with a soft sealable plastic filling layer (W), to form an intermediate embedded product, covering said intermediate product with plastic-metal composite film or foil (F) comprising two layers of which a first plastic layer comprises a sealable polyolefin with a layer thickness of 10-100μ, and of which a second metal layer comprises a deformable and solderable metal with a layer thickness of 0.25-250μ, folding the film or foil with the first plastic layer to the inside and hermetically soldering the second metal layer to a soldering ring (LK) previously printed on the substrate (S), and then encapsulating the component and film or foil with synthetic resin (H) so that said first plastic layer is intimately bonded to said filling layer (W), and said metal layer is intimately bonded to said synthetic resin.
Claim 10
Dependent Claim
45 words
The process of claim 7, wherein a high-purity, relative to the circuit components inert, low-viscosity, flexible epoxy resin with adhesive properties appropriate for the semi-conductor circuit and composite films or foils are used as a filling in the pour-coating step for forming said layer (W).
Claim 11
Dependent Claim
48 words
The process of claim 7, wherein a high purity, soft, with respect to the semi-conductor circuit inert, hot-sealable coating, especially made of modified silicone containing polyolefin or of silicone adhesive on a silicone-fluorine base, is used as a filling in the pour-coating step for forming said layer (W).
Claim 12
Dependent Claim
44 words
the process of claim 7, wherein said plastic metal composite is made of a base and film or foil by means of a hot-sealing deformation at temperatures of 30°-250° C. and at pressures of 1-50 bar outside of the wiring and the bonding points.
Claim 13
Dependent Claim
20 words
The process of claim 7, further comprising using heatable hollow stamps (ST) or matrix dies for the heating and deformation.
Claim 14
Dependent Claim
14 words
The process of claim 11, further comprising pour-coating the composite film or foil encapsulation.
References Cited (Backward Citations)
DE1514478A1
Cited
US3608029A
Cited
DE2347049A1
Cited
US3876461A
Cited
DE2545471A1
Cited
US4001863A
Cited
DE2538119A1
Cited
DE2551778A1
Cited
DE2656139A1
Cited
DE2628823A1
Cited
DE2748523A1
Cited
DE2922005A1
Cited
US4327369A
Cited
DE3137480A1
Cited
JPS5790967A
Cited
DE3151902A1
Cited
JPS57128948A
Cited
US4388132A
Cited
DE3222791A1
Cited
EP0122687A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-15 | 1992-05-16 | 1992-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-15 | 1996-05-16 | 1996-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-15 | 2000-05-16 | 2000-11-15 | $7700.00 | Window Closed / Lapsed |