Fabrication process of semiconductor lasers
Assignee: Hitachi Ltd
•
Filing: 1986-10-30
•
Granted: 1988-11-08
•
Expires: 2006-10-30
Abstract
Abstract A p-GaAlAs cladding layer is exposed to the air if a groove of the form of a stripe is formed by chemical etching in an n-GaAs layer that serves as a current confinement layer on the p-GaAlAs cladding layer, the groove being so formed as to reach the cladding layer. The GaAlAs is oxidized so easily that an unstable degradation layer is formed on the surface thereof. To solve this problem according to the prior art, an undoped GaAs layer that serves as a cover layer is formed on the p-GaAlAs cladding layer, the n-GaAs layer is formed, and the etching is effected so that the undoped GaAs layer is simply exposed. The undoped GaAs layer is then heated in the MBE apparatus while being irradiated with the As molecular beam and is thermally etched. Therefore, the cladding layer is exposed in vacuum and the p-GaAlAs layer is formed thereon. However, this method is not suited for mass-production since the thermal etching is unstable and it needs the MBE apparatus of a very high degree of vacuum. Quality of the crystal decreases, too, due to the heating. This invention therefore provides a fabrication process of semiconductor lasers in which the cover layer disappears due to interdiffusion of constituent elements that stem from the diffusion of impurities such as zinc ions in the undoped GaAs layer.
Inventors
- 👤 Tadashi Fukuzawa
- 👤 Yuichi Ono
- 👤 Shinichi Nakatsuka
- 👤 Takashi Kajimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:18
CPC Classifications
B; B82; B82Y; B82Y20/00; H; H01; H01S; H01S5/00; H01S5/20; H01S5/22; H01S5/223; H01S5/2231; H01S5/30; H01S5/34; H10; H10H; H10H20/00; H10H20/01; H10H20/011; H10H20/013; H01S5/2054; H01S5/2081; H01S5/32; H01S5/323; H01S5/32308; H01S5/32316
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
261 words
A fabrication process of semiconductor lasers, comprising: a step for successively growing a first semiconductor structure, a second semiconductor thin structure for protecting the first semiconductor structure from oxidation, and a third semiconductor layer having a band gap greater than that of said second semiconductor structure but smaller than that of said first semiconductor structure in a crystal growing chamber; a step of forming on said third semiconductor layer, a stripe composed of an insulating film, outside said crystal growing chamber; a step for growing a fourth semiconductor structure on the third semiconductor layer with aaid striped insulating film as a mask; a step for removing the insulating film outside said crystal growing chamber, and for removing the whole of said third semiconductor layer just under the insulating film and the surface portion of said fourth semiconductor structure; a step of growing a fifth semiconductor structure on said second semiconductor thin structure and on said fourth semiconductor structure, said fifth semiconductor structure having impurities doped thereinto and forming a hetero-structure with said second semiconductor thin structure; and a step for increasing the band gap of said second semiconductor thin structure relying upon the impurity diffusion induced intermixing of the hetero-structure that the fifth semiconductor structure forms with the second semiconductor thin structure, which intermixing is effected by the spatial replacement and exchange of constituent elements in said first and fifth semiconductor structures and said second semiconductor thin structure utilizing the impurities doped in the fifth semiconductor structure that is grown on said second semiconductor thin structure and said fourth semiconductor structure.
Claim 2
Dependent Claim
261 words
A fabrication process of semiconductor lasers, comprising: a step for successively growing a first semiconductor structure, a second semiconductor thin structure for protecting the first semiconductor structure from oxidation, and a third semiconductor layer having a band gap greater than that of said second semiconductor structure but smaller than that of said first semiconductor structure in a crystal growing chamber; a step of forming on said third semiconductor layer, a stripe composed of an insulating film, outside said crystal growing chamber; a step for growing a fourth semiconductor structure on the third semiconductor layer with aaid striped insulating film as a mask; a step for removing the insulating film outside said crystal growing chamber, and for removing the whole of said third semiconductor layer just under the insulating film and the surface portion of said fourth semiconductor structure; a step of growing a fifth semiconductor structure on said second semiconductor thin structure and on said fourth semiconductor structure, said fifth semiconductor structure having impurities doped thereinto and forming a hetero-structure with said second semiconductor thin structure; and a step for increasing the band gap of said second semiconductor thin structure relying upon the impurity diffusion induced intermixing of the hetero-structure that the fifth semiconductor structure forms with the second semiconductor thin structure, which intermixing is effected by the spatial replacement and exchange of constituent elements in said first and fifth semiconductor structures and said second semiconductor thin structure utilizing the impurities doped in the fifth semiconductor structure that is grown on said second semiconductor thin structure and said fourth semiconductor structure.
Claim 3
Dependent Claim
61 words
A fabrication process of semiconductor lasers according to claim 1, wherein said first semiconductor structure consists of a Ga 1-x Al x As layer (0.1≦x≦1) and has a thickness over a range of 50 to 1000 angstroms, and said second semiconductor thin film structure consists of a GaAs layer and has a thickness over a range of 50 to 1000 angstroms.
Claim 4
Dependent Claim
14 words
A fabrication process of a semiconductor laser as claimed in claim 2, wherein 0.3≦x≦1.
Claim 5
Dependent Claim
162 words
A fabrication process of a semiconductor laser comprising: a first step of growing first semiconductor layers on a substrate, said first semiconductor layers including an active layer; a second step of growing second semiconductor layers on said first semiconductor layers, said second semiconductor layers including a second sub-layer; a third step of forming a striped groove in the second semiconductor layers, a part of said second sub-layer being exposed at the striped groove; a fourth step of growing a fifth semiconductor layer on the exposed part of the second sub-layer, the fifth semiconductor layer having a larger band gap than that of the second sub-layer said fifth semiconductor layer being provided with impurities; and a fifth step of intermixing the fifth semiconductor layer and the second sub-layer, the intermixing being induced by diffusion of said impurities with which the fifth semiconductor layer is provided, the intermixed second sub-layer and fifth layer having a larger band gap than that of the second sub-layer.
Claim 6
Dependent Claim
162 words
A fabrication process of a semiconductor laser comprising: a first step of growing first semiconductor layers on a substrate, said first semiconductor layers including an active layer; a second step of growing second semiconductor layers on said first semiconductor layers, said second semiconductor layers including a second sub-layer; a third step of forming a striped groove in the second semiconductor layers, a part of said second sub-layer being exposed at the striped groove; a fourth step of growing a fifth semiconductor layer on the exposed part of the second sub-layer, the fifth semiconductor layer having a larger band gap than that of the second sub-layer said fifth semiconductor layer being provided with impurities; and a fifth step of intermixing the fifth semiconductor layer and the second sub-layer, the intermixing being induced by diffusion of said impurities with which the fifth semiconductor layer is provided, the intermixed second sub-layer and fifth layer having a larger band gap than that of the second sub-layer.
Claim 7
Dependent Claim
34 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein said impurities are added to asid fifth semiconductor layer by diffusion or ion implantation after said fifth semiconductor layer is grown.
Claim 8
Dependent Claim
101 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein said third step of providing the striped groove and the step of growing the fifth semiconductor layer include the sub-steps of forming an insulating film on the second semiconductor layers except above the location of the striped groove; then performing selective removal of the second semiconductor layers, using said insulating film as a mask so as to form the striped groove; then removing said insulating film; and then providing said fifth semiconductor layer on said second semiconductor layers, including directly on the exposed part of the second sub-layer.
Claim 9
Dependent Claim
45 words
A fabrication process of a semiconductor laser as claimed in claim 6, wherein said insulating film is formed by providing an insulating layer for forming the insulating film on the entire substrate, and selectively removing said insulating layer so as to form said insulating film.
Claim 10
Dependent Claim
25 words
A fabrication process of a semiconductor laser as claimed in claim 6, wherein said fifth semiconductor layer is formed by metal organic chemical vapor deposition.
Claim 11
Dependent Claim
29 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein said fifth step is done at a crystal growth temperature for growing the fifth semiconductor layer.
Claim 12
Dependent Claim
20 words
A fabrication process of a semiconductor laesr as claimed in claim 6, wherein said fifth step is done by heating.
Claim 13
Dependent Claim
42 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein, in said fifth step, said fifth semiconductor layer and second sub-layer are intermixed so as to transform the fifth semiconductor layer and the second sub-layer into a mixed crystal.
Claim 14
Dependent Claim
20 words
A fabrication process of a semiconductor layer as claimed in claiam 6, wherein said active layer includes a superlattice structure.
Claim 15
Dependent Claim
21 words
A fabrication process of a semiconductor laser as claimed in claim 6, wherein said active layer includes a multi-quantum well structure.
Claim 16
Dependent Claim
27 words
A fabrication process of a semiconductor laser as claimed in claim 13, wherein said multi-quantum well structure includes a GaAs well layer and a GaAlAs barrier layer.
Claim 17
Dependent Claim
43 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein the fifth step is done by heating, the heating being performed so as to cause said intermixing, to transform the fifth semiconductor layer and second sub-layer into a mixed crystal.
Claim 18
Dependent Claim
23 words
A fabrication process of a semiconductor laser as claimed in claim 15, wherein said heating is performed at a temperature of 750°-850° C.
Claim 19
Dependent Claim
35 words
A fabrication process of a semiconductor laser as claimed in claim 6, wherein each of said first semiconductor layers, said second semiconductor layers, and said fifth semiconductor layer is formed by organometallic vapor phase epitaxy.
Claim 20
Dependent Claim
18 words
A fabrication process of a semiconductor laser as claimed in claim 6, wherein said impurities are zinc ions.
Claim 21
Dependent Claim
50 words
A fabrication process of a semiconductor laser as claimed in claim 18, wherein the zinc ions are included in said fifth semiconductor layer, at a concentration of at least 5×10 18 cm -3 , at least in a part of the fifth semiconductor layer formed on the exposed second sub-layer.
Claim 22
Dependent Claim
36 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein each of said first semiconductor layers, said second semiconductor layers, and said fifth semiconductor layer is formed by metal organic chemical vapor deposition.
Claim 23
Dependent Claim
49 words
A fabrication process of a semiconductor laser as claimed in claim 4, wherein said second sub-layer of the second semiconductor layers is made of a semiconductor material that is more resistant to oxidation than the semiconductor material of a sub-layer of the second semiconductor layers beneath the second sub-layer.
Claim 24
Dependent Claim
128 words
A fabrication process of a semiconductor laser comprising: a first step of growing first semiconductor layers on a substrate, said first semiconductor layers including an active layer; a second step of growing second semiconductor layers on said first semiconductor layers, the second semiconductor layers including a second sub-layer; a third step of forming a striped groove in the second semiconductor layers, a part of the second sub-layer being exposed at the striped groove; a fourth step of growing a fifth semiconductor layer on the exposed part of the second sub-layer, so as to form a hetero-structure with the exposed part of the second sub-layer, the fifth layer being provided with impurities; and a fifth step of diffusing impurities provided in the layer so as to smear the hetero-structure.
Claim 25
Dependent Claim
128 words
A fabrication process of a semiconductor laser comprising: a first step of growing first semiconductor layers on a substrate, said first semiconductor layers including an active layer; a second step of growing second semiconductor layers on said first semiconductor layers, the second semiconductor layers including a second sub-layer; a third step of forming a striped groove in the second semiconductor layers, a part of the second sub-layer being exposed at the striped groove; a fourth step of growing a fifth semiconductor layer on the exposed part of the second sub-layer, so as to form a hetero-structure with the exposed part of the second sub-layer, the fifth layer being provided with impurities; and a fifth step of diffusing impurities provided in the layer so as to smear the hetero-structure.
Claim 26
Dependent Claim
33 words
A fabrication process of a semiconductor laser as claimed in claim 22, wherein said fifth step is performed by interdiffusing atoms of the second sub-layer and fifth semiconductor layer at the heterostructure interface.
Claim 27
Dependent Claim
37 words
A fabrication process of a semiconductor laser as claimed in claim 23, wherein said fifth semiconductor layer has impurities doped therein, and wherein said fifth step of interdiffusing atoms is induced by the diffusion of said impurities.
Claim 28
Dependent Claim
49 words
A fabrication process of a semiconductor laser as claimed in claim 24, wherein said second sub-layer of the second semiconductor layers is made of a semiconductor material that is more resistant to oxidation than the semiconductor material of a sub-layer of the second semiconductor layers, beneath the second sub-layer.
Claim 29
Dependent Claim
49 words
A fabrication process of a semiconductor laser as claimed in claim 22, wherein said second sub-layer of the second semiconductor layers is made of a semiconductor material that is more resistant to oxidation than the semiconductor material of a sub-layer of the second semiconductor layers beneath the second sub-layer.
References Cited (Backward Citations)
US4329660A
Cited
US4360919A
Cited
US4566171A
Cited
US4635268A
Cited
US4569721A
Cited
US4585491A
Cited
US4567060A
Cited
US4667332A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-11-08 | 1992-05-09 | 1992-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-11-08 | 1996-05-09 | 1996-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-11-08 | 2000-05-09 | 2000-11-08 | $7700.00 | Window Closed / Lapsed |