Turbine rotor
Assignee: Niterra Co Ltd
•
Filing: 1986-03-14
•
Granted: 1988-10-18
•
Expires: 2006-03-14
Abstract
Abstract In a turbine rotor composed of a ceramic turbine blade and a metal shaft with an end to be machined, martensite stainless steel or martensite heat-resistant steel which can be hardened in a gas or vacuum after having been heated beyond the quenching temperature thereof is used as the metal. The ceramic blade and the metal shaft are heat-connected by brazing or shrinkage fit at 800 DEG C., or more. The metal shaft hardened through the heat-connection is tempered only at the end to be machined or the metal shaft heated to the quenching temperature is quench hardened only in part other than the end to be machined, thus facilitating the machining of the metal shaft locally which keeping the remaining part thereof in a quench hardened condition.
Inventors
- 👤 Masaya Ito
- 👤 Noboru Ishida
- 👤 Mitsuyoshi Kawamura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:22
CPC Classifications
F; F04; F04D; F04D29/00; F04D29/26; F04D29/266; C; C04; C04B; C04B37/00; C04B37/02; C04B37/021; C04B37/023; C04B37/026; C21; C21D; C21D9/00; C21D9/28; F01; F01D; F01D5/00; F01D5/02; F01D5/025; F16; F16D; F16D1/00; F16D1/02; F16D1/027; F16D1/04; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6565; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/123; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/368; C04B2237/40; C04B2237/405; C04B2237/406; F02; F02B; F02B1/00; F02B1/02; F02B1/04
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
105 words
A turbine rotor including a ceramic member and a metal shaft member with an end to be machined, wherein the metal member is made of any one of martensite heat-resistant steel and martensite stainless steel which is quench hardened in a gas or vacuum after having been heated beyond a quench hardening temperature thereof to heat-connect the metal shaft member with the ceramic member, the metal shaft member quench hardened when heat-connected with the ceramic member having been tempered only at the end to be machined while keeping part of the metal shaft member other than the end to be machined in a hardened state.
Claim 2
Dependent Claim
105 words
A turbine rotor including a ceramic member and a metal shaft member with an end to be machined, wherein the metal member is made of any one of martensite heat-resistant steel and martensite stainless steel which is quench hardened in a gas or vacuum after having been heated beyond a quench hardening temperature thereof to heat-connect the metal shaft member with the ceramic member, the metal shaft member quench hardened when heat-connected with the ceramic member having been tempered only at the end to be machined while keeping part of the metal shaft member other than the end to be machined in a hardened state.
Claim 3
Dependent Claim
17 words
The turbine rotor as set forth in claim 1, wherein the heat-connection is brazing and/or shrinkage fit.
Claim 4
Dependent Claim
45 words
The turbine rotor as set forth in claim 2, wherein the brazing and/or shrinkage fit are/is effected in dependence upon a connecting portion of the ceramic member and a corresponding connecting portion of the metal shaft member enclosing or surrounding the ceramic member connecting portion.
Claim 5
Dependent Claim
23 words
The turbine rotor as set forth in claim 1, wherein the quench hardening of the metal shaft member occurs due to martensite transformation.
Claim 6
Dependent Claim
31 words
The turbine rotor as set forth in claim 4, wherein the metal shaft is capable of expanding by at least 0.02 vol % through the martensite transformation during the cooling process.
Claim 7
Dependent Claim
27 words
The turbine rotor as set forth in claim 1, wherein the metal shaft member has been quench hardened to a hardness H RC of at least 40.
Claim 8
Dependent Claim
100 words
A turbine rotor including a ceramic member and a metal shft member with an end to be machined, wherein the metal member is made of any one of martensite heat-resistant steel and martensite stainless steel which is quench hardened in a gas or vacuum after having been heated beyond a quench hardening temperature thereof to heat-connect the metal shaft member with the ceramic member, the metal shaft member having been quench hardened when heat-connected with the ceramic member only in part of the metal shaft member other than the end to be machined without hardening the end to be machined.
Claim 9
Dependent Claim
100 words
A turbine rotor including a ceramic member and a metal shft member with an end to be machined, wherein the metal member is made of any one of martensite heat-resistant steel and martensite stainless steel which is quench hardened in a gas or vacuum after having been heated beyond a quench hardening temperature thereof to heat-connect the metal shaft member with the ceramic member, the metal shaft member having been quench hardened when heat-connected with the ceramic member only in part of the metal shaft member other than the end to be machined without hardening the end to be machined.
Claim 10
Dependent Claim
17 words
The turbine rotor as set forth in claim 7, wherein the heat-connection is brazing and/or shrinkage fit.
Claim 11
Dependent Claim
45 words
The turbine rotor as set forth in claim 8, wherein the brazing and/or shrinkage fit are/is effected in dependence upon a connecting portion of the ceramic member and a corresponding connecting portion of the meatl shaft member enclosing or surrounding the ceramic member connecting portion.
Claim 12
Dependent Claim
23 words
The turbine rotor as set forth in claim 7, wherein the quench hardening of the metal shft member occurs due to martensite transformation.
Claim 13
Dependent Claim
32 words
The turbine rotor as set forth in claim 10, wherein the metal shaft member is capable of expanding by at least 0.02 vol % through the martensite transformation during the cooling process.
Claim 14
Dependent Claim
26 words
The turbine rotor as set forth in claim 7, wherein the metal shaft member is quench hardened to a hardness H RC of at least 40.
References Cited (Backward Citations)
US3834833A
Cited
US3839779A
Cited
US4090813A
Cited
DE2734747A1
Cited
US4142923A
Cited
US4335998A
Cited
US4557704A
Cited
US4614453A
Cited
JPS61286274A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-18 | 1992-04-18 | 1992-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-18 | 1996-04-18 | 1996-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-18 | 2000-04-18 | 2000-10-18 | $7700.00 | Window Closed / Lapsed |