Porous random fiber composites and a method for preparing same
Assignee: Dow Chemical Co
•
Filing: 1987-05-05
•
Granted: 1988-10-04
•
Expires: 2007-05-05
Abstract
Abstract A process for preparing a porous random fiber polymeric composite sheet through the addition of a cellulose ether which is selectively soluble or insoluble to a random fiber composite slurry under conditions such that the cellulose ether is insoluble, forming the slurry into a sheet, fusing the organic polymer component of the sheet and heating the sheet to solubilize the cellulose ether whereby voids are formed in the sheet. Before the sheet is treated to remove the cellulose ether, it may be combined with other sheets and densified under heat and pressure. Before removing the cellulose ether, the densified sheet may be heated under reduced pressure to expand or loft the sheet in a direciton normal to the plane of the sheet. A random fiber polymeric composite sheet, a densified sheet and a lofted sheet, each comprising a binder, fusable organic polymer, reinforcing material and a cellulose ether are also provided. The same sheets after removal of the cellulose ether are further provided.
Inventors
- 👤 Gaylon L. Dighton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 15:24
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/26; D; D21; D21H; D21H17/00; D21H17/20; D21H17/21; D21H17/24; D21H17/25; D21H17/26; D21H25/00; D21H25/02; D21H13/00; D21H13/10; D21H13/12; D21H13/14; D21H13/36; D21H13/38; D21H13/40; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24273; Y10T428/24322; Y10T428/249921; Y10T428/249953; Y10T428/249981; Y10T442/00; Y10T442/60; Y10T442/659; Y10T442/671
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
78 words
A process for preparing a porous random fiber polymeric composite sheet comprising the addition of a soluble cellulose ether to a random fiber composite slurry comprising a diluent, a fusible organic polymer, reinforcement material and binder under conditions such that said cellulose ether is insoluble: forming said slurry into a sheet; fusing the organic polymer component of said sheet; and treating said sheet under conditions sufficient to solubilize said cellulose ether whereby voids are formed in said sheet.
Claim 2
Dependent Claim
78 words
A process for preparing a porous random fiber polymeric composite sheet comprising the addition of a soluble cellulose ether to a random fiber composite slurry comprising a diluent, a fusible organic polymer, reinforcement material and binder under conditions such that said cellulose ether is insoluble: forming said slurry into a sheet; fusing the organic polymer component of said sheet; and treating said sheet under conditions sufficient to solubilize said cellulose ether whereby voids are formed in said sheet.
Claim 3
Dependent Claim
43 words
The process of claim 1 wherein said random fiber composite slurry is an aqueous slurry wherein said conditions such that said cellulose ether is insoluble are that the temperature of said aqueous slurry is maintained above the gelation point of said cellulose ether.
Claim 4
Dependent Claim
39 words
The process of claim 2 wherein said soluble cellulose ether is an hydroxyalkyl methylcellulose where said alkyl contains 2, 3 or 4 carbon atoms, a hydroxyalkyl cellulose ether where said alkyl contains 3 or 4 carbon atoms, or methylcellulose.
Claim 5
Dependent Claim
14 words
The process of claim 3 wherein said cellulose ether is methylcellulose or hydroxypropyl methylcellulose.
Claim 6
Dependent Claim
17 words
The process of claim 1 where said random fiber composite slurry is prepared with a nonaqueous diluent.
Claim 7
Dependent Claim
22 words
The process of claim 5 where said diluent is a lower aliphatic alcohol containing from about 1 to about 6 carbon atoms.
Claim 8
Dependent Claim
28 words
The process of claim 6 wherein the slurry is maintained under sufficient pressure to keep the alcohol from boiling at a temperature below the cellulose ethers gelation point.
Claim 9
Dependent Claim
10 words
The process of claim 5 where said diluent is perchloroethylene.
Claim 10
Dependent Claim
37 words
The process of claim 1 where said soluble cellulose ether is a surface treated cellulose ether where said conditions such that said cellulose ether is insoluble are dependent on the pH of said random fiber composite slurry.
Claim 11
Dependent Claim
20 words
The process of claim 1 which includes the additional step of lofting said sheet prior to solubilizing said cellulose ether.
Claim 12
Dependent Claim
15 words
A porous random fiber polymeric composite sheet as prepared by the process of claim 1.
Claim 13
Dependent Claim
133 words
A process for preparing an expanded, porous random fiber polymeric composite sheet comprising (a) preparing a random fiber composite slurry comprising a diluent, a fusible organic polymer, at least one reinforcing material, a binder and a cellulose ether, which is selectively soluble or insoluble, under conditions such that said cellulose ether is insoluble; (b) destabilizing and forming said slurry into a mat or sheet; (c) dewatering and drying said mat; (d) fusing a plurality of mats into a densified sheet; (e) heating said densified sheet under conditions sufficient to soften the fusible polymer and expand said sheet in a direction normal to the plane of the sheet thereby forming a lofted sheet; and (f) treating said lofted sheet under conditions sufficient to solubilize said cellulose ether and form voids in said lofted sheet.
Claim 14
Dependent Claim
133 words
A process for preparing an expanded, porous random fiber polymeric composite sheet comprising (a) preparing a random fiber composite slurry comprising a diluent, a fusible organic polymer, at least one reinforcing material, a binder and a cellulose ether, which is selectively soluble or insoluble, under conditions such that said cellulose ether is insoluble; (b) destabilizing and forming said slurry into a mat or sheet; (c) dewatering and drying said mat; (d) fusing a plurality of mats into a densified sheet; (e) heating said densified sheet under conditions sufficient to soften the fusible polymer and expand said sheet in a direction normal to the plane of the sheet thereby forming a lofted sheet; and (f) treating said lofted sheet under conditions sufficient to solubilize said cellulose ether and form voids in said lofted sheet.
Claim 15
Dependent Claim
38 words
The process of claim 12 wherein said cellulose ether is a hydroxyalkyl methylcellulose where said alkyl contains 2, 3 or 4 carbon atoms, a hydroxyalkyl cellulose ether where said alkyl contains 3 or 4 carbon atoms, or methylcellulose.
Claim 16
Dependent Claim
25 words
The process of claim 12 wherein said diluent is water, a lower aliphatic alcohol containing from about one to about six carbon atoms or perchloroethylene.
Claim 17
Dependent Claim
33 words
The process of claim 12 wherein said cellulose ether is a surface treated cellulose ether which is selectively soluble or insoluble depending upon the pH of the slurry in which it is dispersed.
Claim 18
Dependent Claim
16 words
An expanded porous random fiber polymeric composite sheet as prepared by the process of claim 12.
Claim 19
Dependent Claim
24 words
A random fiber polymeric composite sheet comprising: (a) a binder, (b) a fusible organic polymer, (c) a reinforcing material, and (d) a cellulose ether.
Claim 20
Dependent Claim
24 words
A random fiber polymeric composite sheet comprising: (a) a binder, (b) a fusible organic polymer, (c) a reinforcing material, and (d) a cellulose ether.
Claim 21
Dependent Claim
24 words
The sheet of claim 17 wherein said cellulose ether is removed by treating said sheets under conditions such that said cellulose ether is dissolved.
Claim 22
Dependent Claim
38 words
The sheet of claim 17 where said cellulose ether is a hydroxyalkyl methylcellulose where said alkyl contains 2, 3 or 4 carbon atoms, a hydroxyalkyl cellulose ether where said alkyl contains 3 or 4 carbon atoms, or methylcellulose.
Claim 23
Dependent Claim
14 words
The sheet of claim 19 where said cellulose ether is hydroxypropyl methylcellulose or methylcellulose.
Claim 24
Dependent Claim
31 words
The process of claim 4 wherein the cellulose ether has a degree of substitution between about 1.1 and about 2.0 and a molar substitution of between about 0.001 and about 1.0.
References Cited (Backward Citations)
US2773286A
Cited
US2831852A
Cited
US2835666A
Cited
US3121658A
Cited
US3297583A
Cited
US3578544A
Cited
GB1263812A
Cited
US3957651A
Cited
US3865661A
Cited
US4100238A
Cited
US4431696A
Cited
FR2507123A1
Cited
US4426470A
Cited
US4518642A
Cited
US4643940A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-04 | 1992-04-04 | 1992-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-04 | 1996-04-04 | 1996-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-04 | 2000-04-04 | 2000-10-04 | $7700.00 | Window Closed / Lapsed |