Method of producing an optical fiber
Assignee: Nokia Bell Labs
•
Filing: 1987-06-18
•
Granted: 1988-10-04
•
Expires: 2007-06-18
Abstract
Abstract The disclosed method of producing optical fiber comprises providing a silica-based glass rod of diameter D that comprises a core region of effective diameter d surrounded by cladding material (D/d typcially>2) and a silica-based porous jacketing tube, inserting the glass core rod into the porous tube, consolidating the porous material and sintering the jacketing tube onto the core rod such that a substantially pore-free optical fiber preform results. Fiber is then drawn from the preform in the conventional manner. Consolidation and sintering is carried out at a temperature below the softening temperature of the material, typically <1600° C. In a preferred embodiment, the porous tube is produced by a sol/gel process that comprises mixing colloidal silica (surface area 5-100 m 2 /g) and water, adding quaternary ammonium hydroxide to the sol such that a pH in the range 11-14 results, lowering the pH into the range 4-11 by addition of methyl or ethyl formate, casting the sol into an appropriate mold and permitting it to gel. The relatively low processing temperature is an advantageous feature of the inventive process that, inter alia, makes it easier to maintain the fiber core concentric with the cladding.
Inventors
- 👤 Debra A. Fleming
- 👤 David W. Johnson, Jr.
- 👤 John B. MacChesney
- 👤 Frederick W. Walz, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:04
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/10; C03B37/12; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03B37/01205; C03B37/01211; C03B37/01446; C03B2203/00; C03B2203/10; C03B2203/22
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
117 words
Method of producing a silica-based optical fiber comprising (a) inserting a silica-based glass rod into a silica-based tube having a softening temperature and heating the thus formed combination such that a unitary glass body (to be termed the "preform") results; and (b) drawing the optical fiber from the preform; characterized in that the silica-based tube is a porous tube having a density in the range from about 10 to about 80% of the theoretical density of the material of the tube, (a) comprises consolidating the porous tube such that substantially pore-free glass results, and (a) is carried out such that the maximum temperature reached by the combination is lower than the softening temperature of the tube material.
Claim 2
Dependent Claim
117 words
Method of producing a silica-based optical fiber comprising (a) inserting a silica-based glass rod into a silica-based tube having a softening temperature and heating the thus formed combination such that a unitary glass body (to be termed the "preform") results; and (b) drawing the optical fiber from the preform; characterized in that the silica-based tube is a porous tube having a density in the range from about 10 to about 80% of the theoretical density of the material of the tube, (a) comprises consolidating the porous tube such that substantially pore-free glass results, and (a) is carried out such that the maximum temperature reached by the combination is lower than the softening temperature of the tube material.
Claim 3
Dependent Claim
52 words
The method of claim 1, comprising selecting the glass rod and the porous tube such that the consolidation of the porous material of any given axial segment of the tube is completed at substantially the time the inner diameter of the axial segment has decreased to the diameter of the glass rod.
Claim 4
Dependent Claim
28 words
The method of claim 1, comprising heating the combination such that the unitary body is produced by joining the tube to the glass rod progressively along the combination.
Claim 5
Dependent Claim
24 words
The method of claim 1, comprising using a silica-based porous tube that was produced by a method that comprises forming a tubular gel body.
Claim 6
Dependent Claim
51 words
The method of claim 1, wherein at least a part of (a) is carried out such that the porous material of the tube is in contact with an atmosphere that comprises a halogen selected from the group consisting of chlorine and fluorine, with the atmosphere furthermore being substantially free of oxygen.
Claim 7
Dependent Claim
30 words
The method of claim 4, wherein producing the tubular gel body comprises forming a sol comprising silica particles having a nominal surface area in the range 5-100 m 2 /gm.
Claim 8
Dependent Claim
52 words
The method of claim 6, wherein producing the tubular gel body comprises forming the sol such that it has a pH in the range 11-14, and further comprises adding at least one pH-lowering substance to the sol such that the pH of the sol is changed to be in the range 4-11.
Claim 9
Dependent Claim
35 words
The method of claim 7, comprising providing a sol comprising water and at least one quaternary ammonium hydroxide, and wherein the pH-lowering substance is chosen from the group consisting of methyl formate and ethyl formate.
Claim 10
Dependent Claim
47 words
The method of claim 1, comprising providing a glass rod of diameter D' having a central region of relatively high refractive index (the "core") and effective core diameter d' that is contactingly surrounded by a region of relatively low refractive index, with D'/d' being at least 2.
Claim 11
Dependent Claim
26 words
The method of claim 5, comprising maintaining the oxygen/halogen ratio at a value less than or equal to 10 -3 during the part of the heating.
Claim 12
Dependent Claim
43 words
The method of claim 1, comprising providing a porous tube that contains a relatively high concentration of at least one contaminating chemical species and carrying out (a) such that the consolidated tube material has a relatively low concentration of the contaminating chemical species.
Claim 13
Dependent Claim
82 words
The method of claim 5, comprising (i) forming an aqueous sol comprising silica particles having a nominal surface area in the range of 20-100 m 2 /gm and a relatively broad size distribution, the sol further comprising sufficient quaternary ammonium hydroxide to result in a pH in the range of 11-14; (ii) adding an alkyl formate to the sol such that a pH in the range 4-11 results; and (iii) the maximum temperature of step a) is at most about 1600° C.
Claim 14
Dependent Claim
12 words
The method of claim 9, comprising providing a glass rod having D'/d'<6.
References Cited (Backward Citations)
US3782982A
Cited
US4419115A
Cited
US4605428A
Cited
US4648891A
Cited
US4680046A
Cited
US4579571A
Cited
US4643751A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-10-04 | 1992-04-04 | 1992-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-10-04 | 1996-04-04 | 1996-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-10-04 | 2000-04-04 | 2000-10-04 | $7700.00 | Window Closed / Lapsed |