Sintered high-silica glass and articles comprising same
Assignee: Furukawa Electric North America Inc
•
Filing: 1984-08-03
•
Granted: 1986-08-12
•
Expires: 2004-08-03
Abstract
Abstract High silica glass is formed by sintering a dried gel. The gel has a pore size distribution such that at most about 5% of the total pore volume is contributed by pores having an effective pore diameter greater than about 0.5 μm, and such that at least 10% of the total pore volume is contributed by pores having an effective pore diameter greater than about 0.02 μm. This pore size distribution permits effective migration of fluid into, and out of, the gel, permits sintering at a lower temperature, and results in increased perfection of the glass. The pore size distribution can be achieved by appropriate comminution, e.g., ball-milling, of intermediate material. A novel process for forming high silica glass is also disclosed. The process comprises forming intermediate material by hydrolysis of one or more metal alkoxides, comminuting the intermediate material to produce colloidal particles, forming a sol by dispersing the particles in liquid, gelling the sol, drying the gel, and sintering the dried gel.
Inventors
- 👤 David W. Johnson, Jr.
- 👤 John B. MacChesney
- 👤 Eleizer M. Rabinovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:30
CPC Classifications
C; C03; C03B; C03B19/00; C03B19/12; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
217 words
Method of fabricating a high silica glass body, the method comprising (a) forming a first gel, the first gel formed either (i) by a first process that comprises forming a first sol by dispersing first particles in a liquid, with the first particles consisting substantially of colloidal silica particles, and gelling the first sol, or (ii) by a second process comprising hydrolyzing at least one metal alkoxide; (b) at least partially drying the first gel, thereby forming an intermediate high silica material; (c) forming second particles by comminution of intermediate high silica material; (d) forming a second sol by dispersing the second particles in a liquid; (e) gelling the second sol to form a second gel; (f) substantially drying the second gel, whereby a substantially dry porous body is formed, the porous body having a pore size distribution, such that at most about 5% of the total pore volume of the porous body is contributed by pores having an effective pore diameter greater than about 0.5 μm, and such that at least about 10% of the total pore volume of the porous body is contributed by pores having an effective pore diameter that is greater than about 0.02 μm; and (g) sintering the porous body at a sintering temperature, whereby a high silica glass body is produced.
Claim 2
Dependent Claim
217 words
Method of fabricating a high silica glass body, the method comprising (a) forming a first gel, the first gel formed either (i) by a first process that comprises forming a first sol by dispersing first particles in a liquid, with the first particles consisting substantially of colloidal silica particles, and gelling the first sol, or (ii) by a second process comprising hydrolyzing at least one metal alkoxide; (b) at least partially drying the first gel, thereby forming an intermediate high silica material; (c) forming second particles by comminution of intermediate high silica material; (d) forming a second sol by dispersing the second particles in a liquid; (e) gelling the second sol to form a second gel; (f) substantially drying the second gel, whereby a substantially dry porous body is formed, the porous body having a pore size distribution, such that at most about 5% of the total pore volume of the porous body is contributed by pores having an effective pore diameter greater than about 0.5 μm, and such that at least about 10% of the total pore volume of the porous body is contributed by pores having an effective pore diameter that is greater than about 0.02 μm; and (g) sintering the porous body at a sintering temperature, whereby a high silica glass body is produced.
Claim 3
Dependent Claim
39 words
Method of claim 1, wherein the pore size distribution is such that at most about 1% of the total pore volume of the porous body is contributed by pores having an effective pore diameter greater than about 0.5 μm.
Claim 4
Dependent Claim
23 words
Method of claim 1, wherein the high silica glass body is an optical fiber preform comprising the glass body formed in step (g).
Claim 5
Dependent Claim
15 words
Method of claim 3, further comprising producing an optical fiber from the optical fiber preform.
Claim 6
Dependent Claim
19 words
Method of claim 1, wherein the intermediate high silica material is, prior to formation of particles therefrom, substantially dry.
Claim 7
Dependent Claim
14 words
Method of claim 1, wherein the sintering temperature is at most about 1400° C.
Claim 8
Dependent Claim
62 words
Method of claim 5, wherein the sintering temperature is at least about 50° C. less than the temperature required to sinter a second porous body that differs from the first porous body only in that more than 5% of the total pore volume of the second porous body is contributed by pores having an effective pore diameter greater than about 0.5 μm.
Claim 9
Dependent Claim
41 words
Method of claim 1, wherein comminution is carried out in comminution means having intermediate-material-contacting surfaces, and wherein during comminution the intermediate material, and fragments and particles formed therefrom, is in contact only with intermediate-material-contacting surfaces consisting essentially of high silica glass.
Claim 10
Dependent Claim
42 words
Method of claim 8, wherein the comminuting means comprise ball-milling means comprising an intermediate-material container consisting essentially of borosilicate glass or of fused SiO 2 , the intermediate-material container charged with a muliplicity of bodies consisting essentially of fused SiO 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-11 | 1990-02-10 | 1990-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-11 | 1994-02-10 | 1994-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-11 | 1998-02-10 | 1998-08-12 | $7700.00 | Window Closed / Lapsed |