Oxidation-and hot corrosion-resistant nickel-base alloy coatings and claddings for industrial and marine gas turbine hot section components and resulting composite articles
Assignee: General Electric Co
•
Filing: 1987-03-17
•
Granted: 1988-09-27
•
Expires: 2007-03-17
Abstract
Abstract New hot corrosion-and oxidation-resistant nickel-base alloys consisting essentially of about 40% chromium, 3% hafnium, 3% silicon, 0.2% yttrium, 0.5% titanium, up to 11% cobalt, remainder nickel are used to provide novel composite articles of nickel-base superalloy gas turbine hot section components having deposited coatings or bonded claddings of these protective alloys.
Inventors
- 👤 Marvin Fishman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:57
CPC Classifications
C; C23; C23C; C23C24/00; C23C24/08; C23C24/082; C23C24/085; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/058; C23C4/00; C23C4/04; C23C4/06; C23C4/067; C23C4/073; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12944
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
42 words
An oxidation and hot corrosion-resistant composite article comprising of nickel-base superalloy gas turbine hot section component and a protective alloy covering bonded thereto consisting essentially of 30-44% chromium, 0.5-10% hafnium, 0.5-4% silicon, 0.1-1% yttrium, 0.3-3% titanium, up to 11% cobalt, remainder nickel.
Claim 2
Dependent Claim
42 words
An oxidation and hot corrosion-resistant composite article comprising of nickel-base superalloy gas turbine hot section component and a protective alloy covering bonded thereto consisting essentially of 30-44% chromium, 0.5-10% hafnium, 0.5-4% silicon, 0.1-1% yttrium, 0.3-3% titanium, up to 11% cobalt, remainder nickel.
Claim 3
Dependent Claim
16 words
An article of claim 1 in which the alloy covering is in the form of coating.
Claim 4
Dependent Claim
18 words
An article of claim 1 in which the covering is in the form of a spray deposited coating.
Claim 5
Dependent Claim
24 words
An article of claim 1 in which the covering is in the form of cladding bonded to the gas turbine hot section component substrate.
Claim 6
Dependent Claim
19 words
An article of claim 4 in which the cladding is bonded to the substrate body by hot isotatic pressing.
Claim 7
Dependent Claim
25 words
An article of claim 1 in which the alloy covering consists essentially of 38-42% chromium, 2.5-3.5% hafnium, 2-4% silicon, 0.1-0.3% yttrium, 0.3-1% titanium, remainder nickel.
Claim 8
Dependent Claim
27 words
An article of claim 1 in which the covering consists essentially of about 40% chromium, 3% hafnium, 3% silicon, 0.2% yttrium, 0.5% titanium, 10% cobalt, remainder nickel.
Claim 9
Dependent Claim
22 words
An oxidation-and hot corrosion-resistant alloy composition consisting essentially of 30-44% chromium, 0.5-10 % hafnium, 0.5-4% silicon, 0.1-1% yttrium, 0.3-3% titanium remainder nickel.
Claim 10
Dependent Claim
22 words
An oxidation-and hot corrosion-resistant alloy composition consisting essentially of 30-44% chromium, 0.5-10 % hafnium, 0.5-4% silicon, 0.1-1% yttrium, 0.3-3% titanium remainder nickel.
Claim 11
Dependent Claim
24 words
The alloy of claim 8 in which the alloy consists essentially of 38-42% chromium, 2.5-3.5% hafnium, 2-4% silicon, 0.1-0.3% yttrium, 0.3-1% titanium, remainder nickel.
Claim 12
Dependent Claim
20 words
The alloy of claim 8 consisting essentially of 40% chromium, 3% hafnium, 3% silicon, 0.2% yttrium, 0.5% titanium, remainder nickel.
Claim 13
Dependent Claim
8 words
The alloy of claim 8 containing 9-11% cobalt.
Claim 14
Dependent Claim
8 words
The alloy of claim 8 containing 10% cobalt.
Claim 15
Dependent Claim
28 words
The article of claim 1 in which the alloy covering consists essentially of about 40% chromium, 2.5% hafnium, 10% cobalt, 3% silicon, 2.5% titanium, 0.3% yttrium, remainder nickel.
References Cited (Backward Citations)
US3479157A
Cited
US4174964A
Cited
US3787202A
Cited
US4039330A
Cited
US3907552A
Cited
US4022587A
Cited
US3904382A
Cited
US4063934A
Cited
US4144380A
Cited
US4118224A
Cited
US4152488A
Cited
US4130420A
Cited
US4137074A
Cited
US4313760A
Cited
US4339509A
Cited
US4419416A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-27 | 1992-03-28 | 1992-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-27 | 1996-03-28 | 1996-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-27 | 2000-03-28 | 2000-09-27 | $7700.00 | Window Closed / Lapsed |