Nickel-chromium-cobalt alloys
Assignee: Huntington Alloys Corp
•
Filing: 1974-12-24
•
Granted: 1977-08-02
•
Expires: 1994-12-24
Abstract
Abstract A nickel-base alloy containing correlated percentages of chromium, cobalt, tungsten, molybdenum, titanium, aluminum, carbon, tantalum, niobium, zirconium, hafnium, boron, yttrium and lanthanum displays excellent stress rupture strength at elevated temperatures together with good corrosion resistance in sulphur- and chloride-containing environments.
Inventors
- 👤 Stuart Walter Ker Shaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:46
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/051; C22C19/055
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
186 words
A nickel-base alloy adapted for use at elevated temperature and characterized by high stress-rupture strength and good corrosion resistance in sulphur-and chloride-containing environments while concomitantly exhibiting extended resistance to embrittlement for long periods upon prolonged exposure to temperatures at least as high as 870° C., said alloy consisting of about 21% to 24% chromium, about 5% to 25% cobalt, from 1% to 5% tungsten, up to 3.5% molybdenum, the tungsten and molybdenum being correlated such that the %W + 0.5 (% Mo) is not greater than about 5%, about 1.7% to 5% titanium and about 1% to 4% aluminum, the sum of the titanium and aluminum being about 4% to 6.5% with the ratio therebetween being from 0.75:1 to 4:1, from 0.02% to 0.25% carbon, from 0.5% to 3% tantalum, about 0.3% to 2% niobium, 0.005% to 1% zirconium and up to 2% hafnium, the value of %Zr + 0.5 (% Hf) being from about 0.01% to 1%, about 0.001% to 0.05% boron, up to about 0.2% in total of yttrium and/or lanthanum, and the balance being essentially nickel in an amount of at least 30%.
Claim 2
Dependent Claim
186 words
A nickel-base alloy adapted for use at elevated temperature and characterized by high stress-rupture strength and good corrosion resistance in sulphur-and chloride-containing environments while concomitantly exhibiting extended resistance to embrittlement for long periods upon prolonged exposure to temperatures at least as high as 870° C., said alloy consisting of about 21% to 24% chromium, about 5% to 25% cobalt, from 1% to 5% tungsten, up to 3.5% molybdenum, the tungsten and molybdenum being correlated such that the %W + 0.5 (% Mo) is not greater than about 5%, about 1.7% to 5% titanium and about 1% to 4% aluminum, the sum of the titanium and aluminum being about 4% to 6.5% with the ratio therebetween being from 0.75:1 to 4:1, from 0.02% to 0.25% carbon, from 0.5% to 3% tantalum, about 0.3% to 2% niobium, 0.005% to 1% zirconium and up to 2% hafnium, the value of %Zr + 0.5 (% Hf) being from about 0.01% to 1%, about 0.001% to 0.05% boron, up to about 0.2% in total of yttrium and/or lanthanum, and the balance being essentially nickel in an amount of at least 30%.
Claim 3
Dependent Claim
34 words
An alloy in accordance with claim 1 containing from 4.75% to 6% of titanium plus aluminum, the ratio of the former to the latter being from cobalt 1:1 to 3:1 and 10% to 20%.
Claim 4
Dependent Claim
28 words
An alloy in accordance with claim 1 in which tungsten does not exceed 4% and the carbon is from 0.04% to 0.2% and tantalum is 0.6% to 2.5%.
Claim 5
Dependent Claim
18 words
An alloy in accordance with claim 2 containing 0.01% to 0.5% zirconium and from 0.003% to 0.03% boron.
Claim 6
Dependent Claim
13 words
An alloy in accordance with claim 4 containing from 0.5% to 1.5% hafnium.
Claim 7
Dependent Claim
73 words
An alloy in accordance with claim 1 containing 21% to 24% chromium, 10% to 20% cobalt, 1.5% to 4% tungsten, up to 1% molybdenum, 1% to 2% tantalum, 0.75% to 1.5% columbium, 3% to 4.5% titanium, 1.5% to 2.5% aluminum, the sum of the titanium and aluminum being 4.75% to 6%, and the ratio therebetween being 1:1 to 3:1, 0.04% to 0.2% carbon, 0.05% to 0.25% zirconium and from 0.002% to 0.02% boron.
Claim 8
Dependent Claim
37 words
An alloy in accordance with claim 1 in which the tantalum, niobium, titanium and aluminum are correlated to satisfy the following relationship 6.7 ≦ 1/2 (%Ta) + % Nb + % Ti + % Al ≦ 7.7.
Claim 9
Dependent Claim
37 words
An alloy in accordance with claim 6 in which the tantalum, niobium, titanium and aluminum are correlated to satisfy the following relationship 6.7 ≦ 1/2 (%Ta) + % Nb + % Ti + % Al ≦ 7.7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-01 | 1981-01-31 | 1981-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-01 | 1985-01-31 | 1985-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-01 | 1989-01-31 | 1989-08-02 | $7700.00 | Window Closed / Lapsed |