Method of coating copper conductors on polyimide with a corrosion resistant metal, and module produced thereby
Assignee: Unisys Corp
•
Filing: 1987-06-10
•
Granted: 1988-09-13
•
Expires: 2007-06-10
Abstract
Abstract A module, for interconnecting integrated circuits, is comprised of a substrate, a layer of polyimide disposed thereon, and a plurality of spaced apart copper conductors on the layer of polyimide. This module is dipped into a solution of palladium chloride, thereafter it is dipped into a solution of sodium hydroxide, and thereafter it is dipped into an electroless plating solution for cobalt. As a result, a film of cobalt is deposited on all exposed surfaces of the copper conductors, but no cobalt is deposited on the exposed polyimide surface between the conductors. This cobalt film protects the copper conductors from corrosion, and it does not short the conductors together.
Inventors
- 👤 Faith M. Zeller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:23
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H10; H10W; H10W70/00; H10W70/01; H10W70/05
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
101 words
A method of coating spaced apart copper conductors which lie on one layer of polyimide with a corrosion resistant metal without shorting said conductors together; said method including the steps of: dipping said one layer of polyimide and said copper conductors which lie thereon into a solution of a catalyst for electrolessly plating said metal; immersing, subsequent to said dipping step, said one layer of polyimide and said conductors which lie thereon into an hydroxide solution; bathing, subsequent to said immersing step, said one layer of polyimide and said conductors which lie thereon in an electroless plating solution for said metal.
Claim 2
Independent Claim
101 words
A method of coating spaced apart copper conductors which lie on one layer of polyimide with a corrosion resistant metal without shorting said conductors together; said method including the steps of: dipping said one layer of polyimide and said copper conductors which lie thereon into a solution of a catalyst for electrolessly plating said metal; immersing, subsequent to said dipping step, said one layer of polyimide and said conductors which lie thereon into an hydroxide solution; bathing, subsequent to said immersing step, said one layer of polyimide and said conductors which lie thereon in an electroless plating solution for said metal.
Claim 3
Dependent Claim
18 words
A method according to claim 1 wherein said solution in said dipping step contains palladium as said catalyst.
Claim 4
Dependent Claim
15 words
A method according to claim 1 wherein said hydroxide in said immersing step is sodium-hydroxide.
Claim 5
Dependent Claim
15 words
A method according to claim 1 wherein said hydroxide in said immersing step is potassium-hydroxide.
Claim 6
Dependent Claim
16 words
A method according to claim 1 wherein said solution in said bathing step electrolessly plates cobalt.
Claim 7
Dependent Claim
16 words
A method according to claim 1 wherein said solution in said bathing step electrolessly plates nickel.
Claim 8
Dependent Claim
26 words
A method according to claim 1 wherein said dipping step lasts from five to fifteen seconds and said immersing step lasts from fifteen to sixty seconds.
Claim 9
Independent Claim
106 words
A method of coating the surfaces of spaced apart conductors which lie on one layer of polyimide with a corrosion resistant metal without also coating the surface of said polyimide between said conductors; said method including the steps of: activating said surfaces of said conductors by immersing them into a solution of a catalyst for electrolessly plating said metal; immersing, subsequent to said activating step, all of said surfaces into another solution which includes a means for deactivating said polyimide surface while keeping said conductor surfaces active; and bathing all of said surfaces, subsequent to said immersing step, in an electroless plating solution for said metal.
Claim 10
Independent Claim
106 words
A method of coating the surfaces of spaced apart conductors which lie on one layer of polyimide with a corrosion resistant metal without also coating the surface of said polyimide between said conductors; said method including the steps of: activating said surfaces of said conductors by immersing them into a solution of a catalyst for electrolessly plating said metal; immersing, subsequent to said activating step, all of said surfaces into another solution which includes a means for deactivating said polyimide surface while keeping said conductor surfaces active; and bathing all of said surfaces, subsequent to said immersing step, in an electroless plating solution for said metal.
Claim 11
Dependent Claim
14 words
A method according to claim 8 wherein said means for deactivating is a hydroxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-13 | 1992-03-14 | 1992-09-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-13 | 1996-03-14 | 1996-09-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-13 | 2000-03-14 | 2000-09-13 | $7700.00 | Window Closed / Lapsed |