Elastoplastic compositions
Assignee: MALAYSIAN RUBBER PRODUCERS' RESEARCH ASSOCIATION TUN ABDUL RAZAK LABORATORY BRICKENDONBURY HERTFORD SG13 8NL ENGLAND
•
Filing: 1987-03-18
•
Granted: 1988-09-06
•
Expires: 2007-03-18
Abstract
Abstract The elastoplastic composition comprises a blend of a thermoplastic polyolefin resin, such as polypropylene, and vulcanized epoxidized natural rubber and has good oil resistance without the use of nitrile rubber and has good mechanical properties without the need for compatibilizing agents. The elastoplastic composition may be prepared by a method which comprises mixing the thermoplastic polyolefin resin and epoxidized natural rubber at a temperature sufficient to soften or melt the resin to give an intimate blend, then while continuing mixing, adding curative for the rubber and vulcanizing the epoxidized natural rubber at a vulcanization temperature.
Inventors
- 👤 Ian R. Gelling
- 👤 Andrew J. Tinker
- 👤 Carl L. Riddiford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:05
CPC Classifications
C; C08; C08L; C08L15/00; C08K; C08K5/00; C08K5/04; C08K5/10; C08L19/00; C08L19/003; C08L23/00; C08L23/02; C08L23/10; C08L7/00; C08L19/006; C08L23/04; C08L23/06; C08L23/12
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
78 words
An elastoplastic composition comprising a blend of from 15 to 90 parts per hundred of the total weight of the blend of a thermoplastic polyolefin resin and 80 to 10 parts per hundred of the total weight of the blend of vulcanized epoxidized natural rubber having a level of epoxide modification in the range of 15 to 85 mole percent prior to vulcanization and a Mooney viscosity in the range of from 10 to 150 at 100° C.
Claim 2
Dependent Claim
78 words
An elastoplastic composition comprising a blend of from 15 to 90 parts per hundred of the total weight of the blend of a thermoplastic polyolefin resin and 80 to 10 parts per hundred of the total weight of the blend of vulcanized epoxidized natural rubber having a level of epoxide modification in the range of 15 to 85 mole percent prior to vulcanization and a Mooney viscosity in the range of from 10 to 150 at 100° C.
Claim 3
Dependent Claim
14 words
A composition according to claim 1, wherein the thermoplastic polyolefin is polyethylene or polypropylene.
Claim 4
Dependent Claim
12 words
A composition according to claim 2, wherein the thermoplastic polyolefin is polypropylene.
Claim 5
Dependent Claim
32 words
A composition according to claim 1, wherein the blend comprises from 80 to 35 parts by weight of vulcanized epoxidised natural rubber and from 20 to 65 parts by weight of polyolefin.
Claim 6
Dependent Claim
26 words
A composition according to claim 1, wherein the vulcanized epoxidised natural rubber has, prior to vulcanization, a level of epoxide modification of about 50 mole %.
Claim 7
Dependent Claim
56 words
A composition according to claim 1, which also contains 0 to 25 parts per hundred by weight based on the total weight of the blend of a compatabilizing agent comprising a block copolymer having at least one segment which is compatible with the polyolefin and at least one segment which is compatible with epoxidized natural rubber.
Claim 8
Dependent Claim
87 words
A method of producing an elastoplastic composition as claimed in claim 1 which comprises mixing the thermoplastic polyolefin resin and epoxidised natural rubber at a temperature sufficient to soften or melt the resin so as to form an intimate blend of resin and epoxidised natural rubber, then while continuing the mixing adding curative for the rubber in an amount sufficient to achieve essentially complete gelation of the epoxidised natural rubber, and continuing the mixing at a vulcanization temperature until vulcanization of the epoxidised natural rubber is complete.
Claim 9
Dependent Claim
14 words
A method according to claim 7, wherein the thermoplastic polyolefin is polyethylene or polypropylene.
Claim 10
Dependent Claim
12 words
A method according to claim 8, wherein the thermoplastic polyolefin is polypropylene.
Claim 11
Dependent Claim
22 words
A method according to claim 7, wherein the epoxidised natural rubber has a level of epoxide modification of about 50 mole %.
Claim 12
Dependent Claim
31 words
A method according to claim 7, wherein the blend comprises from 80 to 35 parts by weight of epoxidised natural rubber and from 20 to 65 parts by weight of polyolefin.
Claim 13
Dependent Claim
70 words
A method according to claim 7, wherein, prior to the vulcanization stage, 0 to 25 parts per hundred by weight of the total weight of the blend of a compatibilizing agent comprising a block copolymer having at least one segment which is compatible with the polyolefin and at least one segment which is compatible with the epoxidized natural rubber is incorporated into the blend of epoxidized natural rubber and polyolefin.
Claim 14
Dependent Claim
51 words
A method according to claim 12, wherein the compatibilizing agent is formed in situ in the blend from one or more suitable percursors, which precursors are present in amounts ranging from 0 to the total replacement of the polyolefin blend when said one or more suitable percursors are suitable modified olefins.
Claim 15
Dependent Claim
34 words
A method according to claim 7, wherein one or more plasticizers are incorporated into the blend in amounts of 0 to 60 parts per hundred, based on the total weight of the polymeric blend.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-09-06 | 1992-03-07 | 1992-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-09-06 | 1996-03-07 | 1996-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-09-06 | 2000-03-07 | 2000-09-06 | $7700.00 | Window Closed / Lapsed |