Compositions having the properties of low viscosity polyethylenes
Assignee: MOORE & MUNGER Inc DELAWARE Corp
•
Filing: 1987-02-13
•
Granted: 1988-08-23
•
Expires: 2007-02-13
Abstract
Abstract Compositions are provided which comprise 50-80% of a synthetic wax, such as a Fischer-Tropsch wax, in combination with 10-50% of a polyethylene material having a Brookfield viscosity at 284° F. greater than about 5000 centipoise. The compositions serve as replacements for commercially available low viscosity polyethylenes, i.e., polyethylenes having Brookfield viscosities at 284° F. of less than about 1000 centipoise, in such applications as lubricating plastic extrusions and coating paperboard stock. The compositions can be prepared by melting and then mixing the components. Accordingly, custom tailoring of the compositions for specific applications can be readily performed.
Inventors
- 👤 Janardan D. Upadhyaya
- 👤 Harry M. Farnham
- 👤 Ing C. Lin
- 👤 Alan R. Case
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 17:57
CPC Classifications
D; D21; D21H; D21H19/00; D21H19/10; D21H19/14; C; C08; C08L; C08L91/00; C08L91/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
191 words
A composition comprising: (a) one or more synthetic waxes each of which has been produced synthetically by polymerizing smaller building blocks and each of which has a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, and a congealing point in the range of from about 160° F. to about 240° F., said one or more synthetic waxes comprising between about 50 and about 80 percent by weight of the total composition; and (b) a polyethylene material having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, a needle penetration value at 77° F. of less than 5 mm/10, and a softening point in the range of from about 200° F. to about 250° F., said polyethylene material comprising between about 10 and about 50 percent by weight of the total composition; the final composition having a Brookfield viscosity at 284° F. of less than about 1000 centipoise, a needle penetration value at 77° F. of less than 10 mm/10, and a melting point in the range of from about 190° F. to about 240° F.
Claim 2
Dependent Claim
191 words
A composition comprising: (a) one or more synthetic waxes each of which has been produced synthetically by polymerizing smaller building blocks and each of which has a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, and a congealing point in the range of from about 160° F. to about 240° F., said one or more synthetic waxes comprising between about 50 and about 80 percent by weight of the total composition; and (b) a polyethylene material having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, a needle penetration value at 77° F. of less than 5 mm/10, and a softening point in the range of from about 200° F. to about 250° F., said polyethylene material comprising between about 10 and about 50 percent by weight of the total composition; the final composition having a Brookfield viscosity at 284° F. of less than about 1000 centipoise, a needle penetration value at 77° F. of less than 10 mm/10, and a melting point in the range of from about 190° F. to about 240° F.
Claim 3
Dependent Claim
26 words
The composition of claim 1 wherein the one or more synthetic waxes comprise between about 60 and about 70 percent by weight of the total composition.
Claim 4
Dependent Claim
27 words
The composition of claim 1 wherein the one or more synthetic waxes include an oxidized synthetic wax having an acid number between about 2 and about 50.
Claim 5
Dependent Claim
21 words
The composition of claim 3 wherein the acid number of the oxidized synthetic wax is between about 10 and about 30.
Claim 6
Dependent Claim
16 words
The composition of claim 1 wherein the one or more synthetic waxes includes a Fischer-Tropsch wax.
Claim 7
Dependent Claim
12 words
The composition of claim 1 wherein the polyethylene material has been oxidized.
Claim 8
Dependent Claim
102 words
A composition comprising 60-70 percent by weight of an oxidized Fischer-Tropsch synthetic wax, said wax having a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, a congealing point in the range of 160° F. to 240° F., and an acid number between about 2 and about 50, and 30-40 percent by weight of a non-oxidized polyethylene having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, said composition having a Brookfield viscosity at 284° F. of 175-250 centipoise and an acid number of 10-20 mg KOH/gm.
Claim 9
Dependent Claim
102 words
A composition comprising 60-70 percent by weight of an oxidized Fischer-Tropsch synthetic wax, said wax having a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, a congealing point in the range of 160° F. to 240° F., and an acid number between about 2 and about 50, and 30-40 percent by weight of a non-oxidized polyethylene having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, said composition having a Brookfield viscosity at 284° F. of 175-250 centipoise and an acid number of 10-20 mg KOH/gm.
Claim 10
Dependent Claim
85 words
A composition comprising 50-60 percent by weight of a non-oxidized Fischer-Tropsch synthetic wax, said wax having a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, and a congealing point in the range of 160° F. to 240° F., and 40-50 percent by weight of a non-oxidized polyethylene having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, said composition having a Brookfield viscosity at 284° F. of 350-450 centipoise.
Claim 11
Dependent Claim
85 words
A composition comprising 50-60 percent by weight of a non-oxidized Fischer-Tropsch synthetic wax, said wax having a Brookfield viscosity at 284° F. of less than 50 centipoise, a needle penetration value at 77° F. of less than 20 mm/10, and a congealing point in the range of 160° F. to 240° F., and 40-50 percent by weight of a non-oxidized polyethylene having a Brookfield viscosity at 284° F. greater than about 5000 centipoise, said composition having a Brookfield viscosity at 284° F. of 350-450 centipoise.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |