US4766161A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Bipolar membranes and methods of making same
Assignee: Marmon Industrial Water LLC
•
Filing: 1986-06-05
•
Granted: 1988-08-23
•
Expires: 2006-06-05
Abstract
Abstract Bipolar membranes are disclosed which exhibit high permselectivity, good mechanical strength, ability to operate at high current density, low potential drop and long-term stability. Essential to the production of bipolar membranes with these properties is the construction of the interface layer, which includes a matrix material containing quaternary and non-quaternary amine groups and having dispersed therein a cation exchange resin. A number of additional important characteristics are disclosed directed to the construction of the anion and cation layers of the bipolar membranes. A preferred method for forming bipolar membranes by casting layers on top of one another is also disclosed.
Inventors
- 👤 Frederick P. Chlanda
- 👤 Ming J. Lan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:34
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/20; C08J5/22; C08J5/2206; C08J5/2275; B; B01; B01D; B01D61/00; B01D61/42; B01D61/44; B01D61/445; C08J2327/00; C08J2439/00; C08J2439/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
193 words
A bipolar membrane comprising: (a) a first layer comprising the reaction product of a polymer containing between about 1.2 meq/g and of about 3.9 meq/g benzyl halide and amine having tertiary and non-tertiary amine groups, the reaction product comprising quaternary amine groups derived from halomethyl groups of the polymer in the first layer; (b) a second layer comprising the reaction product of a matrix polymer containing between about 2.0 meq/g and about 3.9 meq/g benzyl halide and amine having tertiary and non-tertiary amine groups, the reaction product comprising quaternary amine groups and non-quaternary amine groups derived from halomethyl groups of the polymer in the second layer, and the matrix polymer having dispersed therein cross-linked cation exchange resin having an ion exchange capacity of between about 3 meq/g and about 5 meq/g, the amount of quaternary and non-quaternary amine groups in the second layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (c) a third layer having a cation exchange capacity of between about 1.0 meq/g and about 1.6 meg/g.
Claim 2
Dependent Claim
193 words
A bipolar membrane comprising: (a) a first layer comprising the reaction product of a polymer containing between about 1.2 meq/g and of about 3.9 meq/g benzyl halide and amine having tertiary and non-tertiary amine groups, the reaction product comprising quaternary amine groups derived from halomethyl groups of the polymer in the first layer; (b) a second layer comprising the reaction product of a matrix polymer containing between about 2.0 meq/g and about 3.9 meq/g benzyl halide and amine having tertiary and non-tertiary amine groups, the reaction product comprising quaternary amine groups and non-quaternary amine groups derived from halomethyl groups of the polymer in the second layer, and the matrix polymer having dispersed therein cross-linked cation exchange resin having an ion exchange capacity of between about 3 meq/g and about 5 meq/g, the amount of quaternary and non-quaternary amine groups in the second layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (c) a third layer having a cation exchange capacity of between about 1.0 meq/g and about 1.6 meg/g.
Claim 3
Dependent Claim
135 words
A bipolar membrane comprising: (a) an anion permselective layer having an ion exchange capacity of between about 1 meq/g and about 2 meq/g and containing quaternary amine groups; (b) an interfacial layer having an ion exchange capacity of between about 1 meq/g and about 3 meq/g for Na + , the interfacial layer having a matrix polymer having dispersed therein cation exchange resin and containing quaternary amine groups and nonquaternary amine groups, the amount of quaternary and nonquaternary amine groups in the interfacial layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (c) a cation perselective layer having an ion exchange capacity of between about 1.3 meq/g and about 1.6 meq/g.
Claim 4
Dependent Claim
135 words
A bipolar membrane comprising: (a) an anion permselective layer having an ion exchange capacity of between about 1 meq/g and about 2 meq/g and containing quaternary amine groups; (b) an interfacial layer having an ion exchange capacity of between about 1 meq/g and about 3 meq/g for Na + , the interfacial layer having a matrix polymer having dispersed therein cation exchange resin and containing quaternary amine groups and nonquaternary amine groups, the amount of quaternary and nonquaternary amine groups in the interfacial layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (c) a cation perselective layer having an ion exchange capacity of between about 1.3 meq/g and about 1.6 meq/g.
Claim 5
Dependent Claim
123 words
A bipolar membrane comprising and anion permselective proton, a cation perselective proton and a region therebetween comprising a matrix material comprising the reaction product of a matrix polymer containing between about 30 wt % and about 60 wt % vinylbenzyl halide and amine having tertiary and nontertiary amine groups, which matrix material includes quaternary and non-quaternary amine groups derived from halomethyl groups of the polymer, and an ion exchange resin having a charge opposite the charge of the quaternary amine groups, the amount of quaternary and nonquaternary amine groups in the region being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.
Claim 6
Dependent Claim
123 words
A bipolar membrane comprising and anion permselective proton, a cation perselective proton and a region therebetween comprising a matrix material comprising the reaction product of a matrix polymer containing between about 30 wt % and about 60 wt % vinylbenzyl halide and amine having tertiary and nontertiary amine groups, which matrix material includes quaternary and non-quaternary amine groups derived from halomethyl groups of the polymer, and an ion exchange resin having a charge opposite the charge of the quaternary amine groups, the amount of quaternary and nonquaternary amine groups in the region being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.
Claim 7
Dependent Claim
167 words
A bipolar membrane comprising: (a) an anion permselective layer comprising a crosslinked reaction production of vinylbenzyl halide containing copolymer containing between about 18 wt % and about 60 wt % vinylbenzyl halide and amine having tertiary and non-tertiary amine groups, the crosslinked reaction product comprising quaternary amine groups, the anion perselective layer being essentially free of cation exchange resin; (b) an interfacial layer comprising (i) crosslinked reaction product of a matrix vinylbenzyl halide containing copolymer containing between about 30 wt % vinylbenzyl halide with amine having tertiary and non-tertiary amine groups, the reaction product including quaternary and non-quaternary amine groups, the amount of quaternary and non-quaternary amine groups in the interfacial layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (ii) cation exchange resin dispersed in the matrix crosslinked reaction product; and (c) a cation permselective layer being essentially free of amine groups.
Claim 8
Dependent Claim
167 words
A bipolar membrane comprising: (a) an anion permselective layer comprising a crosslinked reaction production of vinylbenzyl halide containing copolymer containing between about 18 wt % and about 60 wt % vinylbenzyl halide and amine having tertiary and non-tertiary amine groups, the crosslinked reaction product comprising quaternary amine groups, the anion perselective layer being essentially free of cation exchange resin; (b) an interfacial layer comprising (i) crosslinked reaction product of a matrix vinylbenzyl halide containing copolymer containing between about 30 wt % vinylbenzyl halide with amine having tertiary and non-tertiary amine groups, the reaction product including quaternary and non-quaternary amine groups, the amount of quaternary and non-quaternary amine groups in the interfacial layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and (ii) cation exchange resin dispersed in the matrix crosslinked reaction product; and (c) a cation permselective layer being essentially free of amine groups.
Claim 9
Dependent Claim
15 words
The bipolar membrane of claim 1 wherein the reaction product of element (a) is crosslinked.
Claim 10
Dependent Claim
39 words
The bipolar membrane of claim 1 wherein the benzyl halide copolymer of elements (a) and (b) is poly(styrene-vinylbenzyl halide) copolymer and wherein the first layer has an anion exchange capacity of between about 1 meq/g and about 2 meq/g.
Claim 11
Dependent Claim
20 words
The bipolar membrane of claim 2 wherein the degree of swelling in water is between about 20% and about 50%.
Claim 12
Dependent Claim
13 words
The bipolar membrane of claim 5 wherein the cation exchange resin comprises divinylbenzene.
Claim 13
Dependent Claim
21 words
The bipolar membrane of claim 8 wherein the amount of divinylbenzene in the resin is at least about 30 wt %.
Claim 14
Dependent Claim
27 words
The bipolar membrane of claim 5 wherein the weight ratio of cation exchange resin to copolymer in the interfacial layer is between about 1:2 and about 2:1.
Claim 15
Dependent Claim
33 words
The bipolar membrane of claim 5 wherein the amount of vinylbenzyl halide in the copolymer from which the anion permselective layer derived is between about 30 wt % and about 45 wt %.
Claim 16
Dependent Claim
71 words
A bipolar membrane comprising an anion exchange layer, a cation exchange layer and an interfacial layer comprising a matrix polymer having dispersed therein a cation exchange resin and said matrix polymer also containing a sufficient amount of quaternary and non-quaternary amine groups so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.
Claim 17
Dependent Claim
71 words
A bipolar membrane comprising an anion exchange layer, a cation exchange layer and an interfacial layer comprising a matrix polymer having dispersed therein a cation exchange resin and said matrix polymer also containing a sufficient amount of quaternary and non-quaternary amine groups so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.
Claim 18
Dependent Claim
149 words
A process for forming bipolar membranes comprising the steps of: (a) forming a first layer comprising a polymer having chemically reactive sites, the polymer having amine groups affixed thereto by the reaction of a precursor polymer with mixed amines comprising N,N-dimethy-1,3-propanediamine and N,N,N',N'-tetramethyl-1,6-hexane diamine in a molar ratio of between about 1:2 and about 5:1; (b) forming on the first layer a second layer comprising a polymer having quaternary and non-quaternary amine groups affixed thereto, and a cation exchange resin dispersed in the polymer of the second layer, the amount of quaternary and non-quaternary amine groups in the second layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and, (c) forming a third layer on said second layer, the third layer being a cation perselective layer.
Claim 19
Dependent Claim
149 words
A process for forming bipolar membranes comprising the steps of: (a) forming a first layer comprising a polymer having chemically reactive sites, the polymer having amine groups affixed thereto by the reaction of a precursor polymer with mixed amines comprising N,N-dimethy-1,3-propanediamine and N,N,N',N'-tetramethyl-1,6-hexane diamine in a molar ratio of between about 1:2 and about 5:1; (b) forming on the first layer a second layer comprising a polymer having quaternary and non-quaternary amine groups affixed thereto, and a cation exchange resin dispersed in the polymer of the second layer, the amount of quaternary and non-quaternary amine groups in the second layer being sufficient so that the bipolar membrane has a potential drop of less than 1.2 volts at 109 mA/cm 2 in 0.5 M Na 2 SO 4 at about 30° C.; and, (c) forming a third layer on said second layer, the third layer being a cation perselective layer.
Claim 20
Dependent Claim
22 words
The process of claim 13 wherein the second layer further comprises non-quaternary amine groups attached to the polymer in the second layer.
Claim 21
Dependent Claim
30 words
The process of claim 13 wherein the ratio of moles of diamine to moles of halomethyl group used to form the first layer is between about 1.2:1 to about 4:1.
Claim 22
Dependent Claim
26 words
The process of claim 13 wherein the weight ratio of cation exchange resin to polymer in the second layer is between about 1:2 and about 2:1.
References Cited (Backward Citations)
US2829095A
Cited
US3388080A
Cited
GB1038777A
Cited
US3372101A
Cited
US3654125A
Cited
US4140815A
Cited
US4024043A
Cited
US4057481A
Cited
US4116889A
Cited
US4253900A
Cited
US4225412A
Cited
US4355116A
Cited
EP0143582A2
Cited
US4584246A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |