US4765950A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for fabricating parts from particulate material
Assignee: INJECTAMAX Corp
•
Filing: 1987-10-07
•
Granted: 1988-08-23
•
Expires: 2007-10-07
Abstract
Abstract Provided is a method of manufacturing sintered parts from particulate material, e.g metal or ceramic parts. The method comprises mixing together predetermined amounts of powdered particulate material and a binder, which mixture is then molded under heat and pressure. The binder comprises at least a lower melting point component and a higher melting point component, with the lower melting point component remaining in a liquid state, becoming semi-solid or relatively soft upon cooling to ambient temperatures. Prior to sintering, the lower melting point component of the binder is selectively dissolved in a liquid solvent, and the higher melting point component is removed upon heating at temperatures below the sintering temperature. The result is a process which eliminates or prevents the formation of oxides, substantially reduces the time required for debinding and sintering, and essentially eliminates cracking in the finished part.
Inventors
- 👤 Kenneth P. Johnson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:20
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/638; B; B22; B22F; B22F1/00; B22F1/10; B22F1/103; B22F3/00; B22F3/10; B22F3/1017; B22F3/1021; B22F3/1025; B22F3/22; B22F3/225; C04B35/632; C04B35/634; C04B35/63404; C04B35/63408; C04B35/63492; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0285; B22F2998/00
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
200 words
A method of manufacturing sintered parts of particulate material consisting essentially of: (i) mixing together predetermined amounts of powdered particulate material and a binder to produce a liquid slurry mixture, said binder being comprised of at least two components having differing melting points, at least a lower melting point component and a higher melting point component, with the lower melting point component remaining in a liquid state, becoming semi-solid or relatively soft upon cooling to ambient temperature; (ii) molding the mixture of particulate material and binder into a part of desired shape by injecting said mixture under heat and pressure into a mold, and allowing said mixture to solidify; (iii) removing the lower melting point component of the binder by a liquid solvent which selectively dissolves the lower melting point component and leaves at least the higher melting point component of the binder undissolved, rendering said part porous and free of cracks; (iv) removing the higher melting point component of the binder by heating at a temperature below the final sintering temperature to thereby provide a part which is essentially free of binder; and (v) subjecting the binder-free part to a final sintering temperature in order to complete the sintering.
Claim 2
Independent Claim
200 words
A method of manufacturing sintered parts of particulate material consisting essentially of: (i) mixing together predetermined amounts of powdered particulate material and a binder to produce a liquid slurry mixture, said binder being comprised of at least two components having differing melting points, at least a lower melting point component and a higher melting point component, with the lower melting point component remaining in a liquid state, becoming semi-solid or relatively soft upon cooling to ambient temperature; (ii) molding the mixture of particulate material and binder into a part of desired shape by injecting said mixture under heat and pressure into a mold, and allowing said mixture to solidify; (iii) removing the lower melting point component of the binder by a liquid solvent which selectively dissolves the lower melting point component and leaves at least the higher melting point component of the binder undissolved, rendering said part porous and free of cracks; (iv) removing the higher melting point component of the binder by heating at a temperature below the final sintering temperature to thereby provide a part which is essentially free of binder; and (v) subjecting the binder-free part to a final sintering temperature in order to complete the sintering.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein the liquid solvent is maintained at a temperature below its boiling point.
Claim 4
Dependent Claim
22 words
The method of claim 2, wherein the liquid solvent is maintained at a temperature below the melting points of the binder components.
Claim 5
Dependent Claim
41 words
The method of claim 2, wherein the liquid solvent is maintained at a temperature below the melting point of the higher melting point component of the binder, but above the melting point of the lower melting point component of the binder.
Claim 6
Dependent Claim
18 words
The method of claim 1, wherein the higher melting point component of the binder is a plastic material.
Claim 7
Dependent Claim
13 words
The method of claim 5, wherein the plastic material is polypropylene or polyethylene.
Claim 8
Dependent Claim
17 words
The method of claim 1, wherein the lower melting point component of the binder comprises an oil.
Claim 9
Dependent Claim
20 words
The method of claim 7, wherein the lower melting point component comprises a mixture of an oil and a wax.
Claim 10
Dependent Claim
24 words
The method of claim 8, wherein the oil is vegetable oil or hydrogenated vegetable oil and the wax is paraffin wax or carnauba wax.
Claim 11
Dependent Claim
11 words
The method of claim 8, wherein the oil is peanut oil.
Claim 12
Dependent Claim
30 words
The method of claim 8, wherein the mixture of oil and wax has a weight ratio of oil to wax in the range of from about 99/1 to about 50/50.
Claim 13
Dependent Claim
15 words
The method of claim 7, wherein the oil comprises vegetable oil or hydrogenated vegetable oil.
Claim 14
Dependent Claim
11 words
The method of claim 7, when the oil comprises peanut oil.
Claim 15
Dependent Claim
30 words
The method of claim 1, wherein the higher melting point component of the binder has a melting point about 150° F. greater than that of the lower melting point component.
Claim 16
Dependent Claim
46 words
The method of claim 14, wherein the higher melting point component has a melting point in the range of about 300° F. to about 400° F., and the lower melting point component has a melting point in the range of about ambient to about 175° F.
Claim 17
Dependent Claim
26 words
The method of claim 1, wherein the higher melting point component is removed by heating in the range of about 700° F. to about 1400° F.
Claim 18
Dependent Claim
25 words
The method of claim 1, wherein the part is immersed in the liquid solvent for a period of time of about 2 hours or less.
Claim 19
Dependent Claim
39 words
The method of claim 1, wherein the higher melting point component of the binder comprises polypropylene or polyethylene, and the lower melting point component of the binder comprises an oil or a mixture of an oil and a wax.
Claim 20
Dependent Claim
16 words
The method of claim 18, wherein the oil is peanut oil or a hydrogenated vegetable oil.
Claim 21
Dependent Claim
14 words
The method of claim 1, wherein the powdered particulate material is a nickel/iron alloy.
Claim 22
Dependent Claim
11 words
The method of claim 1, wherein the particulate material comprises aluminum.
Claim 23
Dependent Claim
15 words
The method of claim 1, wherein the liquid solvent is methylene chloride, acetone or naphtha.
Claim 24
Independent Claim
240 words
A method of manufacturing sintered metal parts consisting essentially of: (i) mixing together predetermined amounts of powdered particulate material and a binder to produce a liquid slurry mixture, said binder being comprised of at least two components having differing melting points, at least a lower melting point component and a higher melting point component, with the lower melting point component remaining in a liquid state, becoming semi-solid or relatively soft upon cooling to ambient temperatures and comprising an oil or a mixture of an oil and wax, and with the higher melting point component comprising polypropylene or polyethylene; (ii) molding the mixture of particulate material and binder into a part of desired shape by injecting said mixture under heat and pressure into a mold, and allowing said mixture to solidify; (iii) removing the lower melting point component of the binder by placing the part in a liquid solvent, the solvent comprising methylene chloride, acetone or naphtha, which solvent selectively dissolves the lower melting point component and leaves at least the higher melting point component of the binder undissolved, rendering said part porous and free of cracks; (iv) removing the high melting point component of the binder by heating at a temperature in the range of from about 700° F. to about 1400° F. to thereby provide part which is essentially free of binder; and (v) subjecting the binder-free part to a final sintering temperature in order to complete the sintering.
Claim 25
Independent Claim
240 words
A method of manufacturing sintered metal parts consisting essentially of: (i) mixing together predetermined amounts of powdered particulate material and a binder to produce a liquid slurry mixture, said binder being comprised of at least two components having differing melting points, at least a lower melting point component and a higher melting point component, with the lower melting point component remaining in a liquid state, becoming semi-solid or relatively soft upon cooling to ambient temperatures and comprising an oil or a mixture of an oil and wax, and with the higher melting point component comprising polypropylene or polyethylene; (ii) molding the mixture of particulate material and binder into a part of desired shape by injecting said mixture under heat and pressure into a mold, and allowing said mixture to solidify; (iii) removing the lower melting point component of the binder by placing the part in a liquid solvent, the solvent comprising methylene chloride, acetone or naphtha, which solvent selectively dissolves the lower melting point component and leaves at least the higher melting point component of the binder undissolved, rendering said part porous and free of cracks; (iv) removing the high melting point component of the binder by heating at a temperature in the range of from about 700° F. to about 1400° F. to thereby provide part which is essentially free of binder; and (v) subjecting the binder-free part to a final sintering temperature in order to complete the sintering.
Claim 26
Dependent Claim
12 words
The method of claim 23, wherein the particulate material comprises nickel/iron alloy.
References Cited (Backward Citations)
US3933652A
Cited
US3926671A
Cited
US4225345A
Cited
US4225345B1
Cited
US4483905A
Cited
US4483905B1
Cited
US4569821A
Cited
US4604259A
Cited
US4664883A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-23 | 1992-02-22 | 1992-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-23 | 1996-02-22 | 1996-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-23 | 2000-02-22 | 2000-08-23 | $7700.00 | Window Closed / Lapsed |