Method for producing microcellular foamed plastic material with smooth integral skin
Assignee: Eastman Kodak Co
•
Filing: 1987-01-27
•
Granted: 1988-08-02
•
Expires: 2007-01-27
Abstract
Abstract The present invention is directed to the continuous production of microcellular plastic web material having integral unmodified laminar skin. In accordance with the invention a web of plastic material impregnated with an inert gas is delivered continuously to a degassing device in which the degree to which gas diffuses out of the surfaces of the web can be selectively and continuously controlled, whereupon the web enters a foaming station where it is reheated to induce foaming. The temperature of the reheated web and the duration of the foaming process prior to quenching are also selectively controllable to produce the desired web characteristics. The gas-impregnated plastic web can be produced initially by any of several novel means including a continuous device for impregnating a previously formed web and several versions of die devices which operate either by rapidly quenching the extruded gas-impregnated plastic material before any significant foaming has occurred or by maintaining the material above its foaming pressure within the die until the material has cooled to below the temperature at which foaming occurs.
Inventors
- 👤 Scott B. Hardenbrook
- 👤 Louis P. Harasta, Jr.
- 👤 Stephen T. Faulkenberry
- 👤 Richard D. Bomba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:01
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/56; B29C44/5609; B29C44/3469; B29C44/348; B29C44/36; B29C44/46; B29C44/50; B29C44/505
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
144 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of: (1) continuously providing to an environment at substantially atmospheric pressure an elongate element of gas-impregnated plastic material at below the atmospheric foaming temperature at which said material foams at such substantially atmospheric pressure. (2) conveying said element along a degassing path at a predetermined speed to permit gas to partially diffuse out of said element and selectively establishing the length of said degassing path for controlling the degree to which gas diffuses out of said element along said path. (3) heating said element beyond said degassing path, while at least some gas remains in core regions of said element, to a temperature above said atmospheric foaming temperature to initiate foaming thereof, and (4) cooling said heated element to below said atmospheric foaming temperature to terminate said foaming.
Claim 2
Independent Claim
144 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of: (1) continuously providing to an environment at substantially atmospheric pressure an elongate element of gas-impregnated plastic material at below the atmospheric foaming temperature at which said material foams at such substantially atmospheric pressure. (2) conveying said element along a degassing path at a predetermined speed to permit gas to partially diffuse out of said element and selectively establishing the length of said degassing path for controlling the degree to which gas diffuses out of said element along said path. (3) heating said element beyond said degassing path, while at least some gas remains in core regions of said element, to a temperature above said atmospheric foaming temperature to initiate foaming thereof, and (4) cooling said heated element to below said atmospheric foaming temperature to terminate said foaming.
Claim 3
Dependent Claim
80 words
The method according to claim 1 in which the step of continuously providing said element of gas-impregnated plastic material comprises the steps of: (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, and (2) maintaining the gas-impregnated plastic material within said extrusion die under sufficient pressure to prevent foaming while cooling such material to below its atmospheric foaming temperature prior to its extrusion from said extrusion die.
Claim 4
Dependent Claim
116 words
The method according to claim 1 in which the step of continuously providing said element of gas-impregnated plastic material comprises the steps of: (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, (2) maintaining said gas-impregnated plastic material within said extrusion die under sufficient pressure to prevent foaming of said material, (3) extruding said material from said extrusion die into said environment at substantially atmospheric pressure while said material is above its atmospheric foaming temperature, and (4) cooling said material rapidly to below its atmospheric foaming temperature before said material has been exposed to substantially atmospheric pressure long enough to undergo significant foaming.
Claim 5
Dependent Claim
92 words
The method according to claim 1 in which the step of continuously providing said element of gas-impregnated plastic material comprises the steps of: (1) passing previously formed substantially gas free plastic material in elongate form continuously through a substantially sealed pressure vessel containing pressurized gas to impregnate said material within said vessel with such gas, and (2) selectively controlling the degree to which the material within said pressure vessel is impregnated with gas by selectively adjusting the length of the path followed by said material during its passage through said pressure vessel.
Claim 6
Independent Claim
157 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of: (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, (2) maintaining the gas-impregnated material within said extrusion die under sufficient pressure to prevent foaming while cooling such material to below its atmospheric foaming temperature prior to its extrusion from said extrusion die, (3) extending said gas-impregnated material from said die at below its atmospheric foaming temperature, (4) conveying said material below its atmospheric foaming temperature along a degassing path beyond said die for allowing gas with which said material was impregnated to partially diffuse out of said material, and (5) reheating said material, after said gas has diffused out of surface regions of said material but while at least some gas remains in core regions thereof, to a temperature above said atmospheric foaming temperature to initiate foaming.
Claim 7
Independent Claim
157 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of: (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, (2) maintaining the gas-impregnated material within said extrusion die under sufficient pressure to prevent foaming while cooling such material to below its atmospheric foaming temperature prior to its extrusion from said extrusion die, (3) extending said gas-impregnated material from said die at below its atmospheric foaming temperature, (4) conveying said material below its atmospheric foaming temperature along a degassing path beyond said die for allowing gas with which said material was impregnated to partially diffuse out of said material, and (5) reheating said material, after said gas has diffused out of surface regions of said material but while at least some gas remains in core regions thereof, to a temperature above said atmospheric foaming temperature to initiate foaming.
Claim 8
Independent Claim
179 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of; (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, (2) maintaining said gas-impregnated plastic within said extrusion die under sufficient pressure to prevent foaming of said material, (3) extending said material from said extrusion die into an environment at substantially atmospheric pressure while said material is above its atmospheric foaming temperature, (4) cooling said material rapidly to below its atmospheric foaming temperature before said material has been exposed to substantially atmospheric pressure long enough to undergo significant foaming, (5) conveying said material below its atmospheric foaming temperature along a degassing path beyond said die for allowing gas with which said material was impregnated to partially diffuse out of said material, and (6) reheating said material, after said gas has diffused out of surface regions of said material but while at least some gas remains in core regions thereof, to a temperature above said atmospheric foaming temperature to initiate foaming.
Claim 9
Independent Claim
179 words
A method for continuously producing foamed plastic material with integral unmodified laminar skin, comprising the steps of; (1) delivering molten gas-impregnated plastic material from an extruder to an extrusion die under sufficient pressure to prevent foaming of said material, (2) maintaining said gas-impregnated plastic within said extrusion die under sufficient pressure to prevent foaming of said material, (3) extending said material from said extrusion die into an environment at substantially atmospheric pressure while said material is above its atmospheric foaming temperature, (4) cooling said material rapidly to below its atmospheric foaming temperature before said material has been exposed to substantially atmospheric pressure long enough to undergo significant foaming, (5) conveying said material below its atmospheric foaming temperature along a degassing path beyond said die for allowing gas with which said material was impregnated to partially diffuse out of said material, and (6) reheating said material, after said gas has diffused out of surface regions of said material but while at least some gas remains in core regions thereof, to a temperature above said atmospheric foaming temperature to initiate foaming.
References Cited (Backward Citations)
US2768407A
Cited
US2317448A
Cited
US2447055A
Cited
US2531665A
Cited
US2751627A
Cited
US3154605A
Cited
US3158886A
Cited
US3389199A
Cited
US3224497A
Cited
US3350734A
Cited
US3676537A
Cited
US3364519A
Cited
US3608056A
Cited
US3610000A
Cited
US3711584A
Cited
US3883625A
Cited
US3762870A
Cited
US4055612A
Cited
US3922328A
Cited
US3988404A
Cited
US4107354A
Cited
US4065137A
Cited
US4250130A
Cited
US4244078A
Cited
US4268977A
Cited
US4304713A
Cited
US4473665A
Cited
JPS59169824A
Cited
JPS59169825A
Cited
JPS6099629A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-02 | 1992-02-01 | 1992-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-02 | 1996-02-01 | 1996-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-02 | 2000-02-01 | 2000-08-02 | $7700.00 | Window Closed / Lapsed |