US3988404A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing a foamed thermoplastic resin article
Assignee: Furukawa Electric Co Ltd
•
Filing: 1974-10-02
•
Granted: 1976-10-26
•
Expires: 1994-10-02
Abstract
Abstract This invention generally pertains to a process for producing a foamed thermoplastic resin article by utilizing the phenomenon that a solid thermoplastic resin sorbs a gas under pressure, and more particularly to a process for producing a foamed thermoplastic resin article comprising the steps of making a solid thermoplastic resin containing a nucleating agent quickly sorb a gas under a high pressure P 1 , lowering said gas pressure to a low pressure P 2 (P 1 > P 2 > the atmospheric pressure) when the gas sorption quantity reaches a predetermined value so as to equilibrate or stabilize said predetermined gas sorption quantity, feeding said gas sorbed thermoplastic resin into an extruder while said gas pressure is maintained at said low pressure P 2 and extruding the resultant resin to thereby produce a foamed thermoplastic resin article. In this invention, the gas sorbed by the thermoplastic resin contributes to foam in the thermoplastic resin.
Inventors
- 👤 Katsumi Orimo
- 👤 Masao Azuma
- 👤 Takashi Shimano
- 👤 Shoji Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:08
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/461; B29C44/3442; B29C44/3446; B29C44/3453; B29C44/3469; B29C44/348; C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/122; C08J9/14; C08J9/143
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
238 words
A process for producing a foamed thermoplastic resin insulation for a communication cable, comprising the steps of: a. feeding into a high pressure tank a solid particulate thermoplastic resin containing a nucleating agent for foaming; b. injecting a gas into said high pressure tank and maintaining the pressure of said gas at a high pressure P 1 for a predetermined time sufficient for said thermoplastic resin to quickly sorb said gas until a gas sorption quantity of predetermined value is reached; c. lowering said gas pressure within said high pressure tank to a low pressure P 2 ; d. transferring said gas sorbed thermoplastic resin within said high presure tank to a low pressure tank in which the gas pressure is held at a low pressure P 2 under which the gas sorption quantity of said thermoplastic resin is in the equilibrium state and wherein said pressure P 2 is lower than said pressure P 1 and higher than the atmospheric pressure; e. feeding said thermoplastic resin within said low pressure tank into an extruder while said gas pressure is maintained at pressure P 2 and extruding said thermoplastic resin on a conductor to form said foamed thermoplastic resin insulation thereon; and f. repeating said steps (a) to (d) to feed additional gas sorbed thermoplastic resin into said low pressure tank before said gas sorbed thermoplastic resin within said low pressure tank is all fed into said extruder.
Claim 2
Dependent Claim
238 words
A process for producing a foamed thermoplastic resin insulation for a communication cable, comprising the steps of: a. feeding into a high pressure tank a solid particulate thermoplastic resin containing a nucleating agent for foaming; b. injecting a gas into said high pressure tank and maintaining the pressure of said gas at a high pressure P 1 for a predetermined time sufficient for said thermoplastic resin to quickly sorb said gas until a gas sorption quantity of predetermined value is reached; c. lowering said gas pressure within said high pressure tank to a low pressure P 2 ; d. transferring said gas sorbed thermoplastic resin within said high presure tank to a low pressure tank in which the gas pressure is held at a low pressure P 2 under which the gas sorption quantity of said thermoplastic resin is in the equilibrium state and wherein said pressure P 2 is lower than said pressure P 1 and higher than the atmospheric pressure; e. feeding said thermoplastic resin within said low pressure tank into an extruder while said gas pressure is maintained at pressure P 2 and extruding said thermoplastic resin on a conductor to form said foamed thermoplastic resin insulation thereon; and f. repeating said steps (a) to (d) to feed additional gas sorbed thermoplastic resin into said low pressure tank before said gas sorbed thermoplastic resin within said low pressure tank is all fed into said extruder.
Claim 3
Dependent Claim
228 words
A process for producing a foamed thermoplastic resin article, comprising the steps of: a. feeding into a high pressure tank a solid particulate thermoplastic resin containing a nucleating agent for foaming: b. injecting a gas into said high pressure tank and maintaining the pressure of said gas at a high pressure P 1 for a predetermined time sufficient for said thermoplastic resin to quickly sorb said gas until a gas sorption quantity of predetermined value is reached; c. lowering said gas pressure with said high pressure tank to a low pressure P 2 ; d. transferring said gas sorbed thermoplastic resin within said high pressure tank to a low pressure tank in which the gas pressure is held at a low pressure P 2 under which the gas sorption quantity of said thermoplastic resin is in the equilibirum state and wherein said pressure P 2 is lower than said pressure P 1 and higher than the atmospheric pressure; e. feeding said thermoplastic resin within said low pressure tank into an extruder while said gas pressure is maintained at pressure P 2 and extruding said thermoplastic resin to form said foamed article; and f. repeating said steps (a) to (d) to feed additional gas sorbed thermoplastic resin into said low pressure tank before said gas sorbed thermoplastic resin within said low pressure tank is all fed into said extruder.
Claim 4
Dependent Claim
228 words
A process for producing a foamed thermoplastic resin article, comprising the steps of: a. feeding into a high pressure tank a solid particulate thermoplastic resin containing a nucleating agent for foaming: b. injecting a gas into said high pressure tank and maintaining the pressure of said gas at a high pressure P 1 for a predetermined time sufficient for said thermoplastic resin to quickly sorb said gas until a gas sorption quantity of predetermined value is reached; c. lowering said gas pressure with said high pressure tank to a low pressure P 2 ; d. transferring said gas sorbed thermoplastic resin within said high pressure tank to a low pressure tank in which the gas pressure is held at a low pressure P 2 under which the gas sorption quantity of said thermoplastic resin is in the equilibirum state and wherein said pressure P 2 is lower than said pressure P 1 and higher than the atmospheric pressure; e. feeding said thermoplastic resin within said low pressure tank into an extruder while said gas pressure is maintained at pressure P 2 and extruding said thermoplastic resin to form said foamed article; and f. repeating said steps (a) to (d) to feed additional gas sorbed thermoplastic resin into said low pressure tank before said gas sorbed thermoplastic resin within said low pressure tank is all fed into said extruder.
Claim 5
Dependent Claim
41 words
A process as set forth in claim 1, wherein said high pressure P 2 is lower than two-thirds as much as the critical pressure of said gas at the temperature of said gas when it is sorbed by said thermoplastic resin.
Claim 6
Dependent Claim
15 words
A process as set forth in claim 1, wherein said gas comprises CO 2 .
Claim 7
Dependent Claim
15 words
A process as set forth in claim 1, wherein said gas comprises CClF 3 .
Claim 8
Dependent Claim
15 words
A process as set forth in claim 1, wherein said gas comprises CHClF 2 .
Claim 9
Dependent Claim
48 words
A process as set forth in claim 1, wherein said thermoplastic resin comprises a resinous composition selected from the group consisting of low density polyethylene, high density polyethylene, copolymer of ethylene and vinylacetate, copolymer of ethylene and tetrafluoroethylene, nylon, polypropylene and a composition mainly including polystyrene and polyethylene.
Claim 10
Dependent Claim
46 words
A process as set forth in claim 1, wherein said nucleating agent for foaming comprises powder of material such as is thermally decomposable within said extruder and wherein the quantity of said powder added is 0.01 to 0.5 parts as against 100 parts of said thermoplastics.
Claim 11
Dependent Claim
48 words
A process as set forth in claim 1, wherein said nucleating agent for foaming comprises powder of material such as is not thermally decomposable within said extruder and wherein the quantity of said powder added is 0.1 to 5.0 parts as against 100 parts of said thermoplastic resin.
Claim 12
Dependent Claim
31 words
A process as set forth in claim 3, wherein said thermoplastic resin is high density polyethylene and wherein said low pressure P 2 ranges from 4 to 33 kg/cm 2 .
Claim 13
Dependent Claim
29 words
A process as set forth in claim 4, wherein said thermoplastic resin is low density polyethylene and wherein said low pressure ranges from 3 to 30 kg/cm 2 .
Claim 14
Dependent Claim
33 words
A process as set forth in claim 4, wherein said thermoplastic resin is copolymer of ethylene and vinylacetate and wherein said low pressure P 2 ranges from 2 to 25 kg/cm 2 .
Claim 15
Dependent Claim
29 words
A process as set forth in claim 4, wherein said thermoplastic resin is polypropylene and wherein said low pressure P 2 ranges from 6 to 40 kg/cm 2 .
Claim 16
Dependent Claim
29 words
A process as set forth in claim 4, wherein said thermoplastic resin is nylon and wherein said low pressure P 2 ranges from 7 to 40 kg/cm 2 .
Claim 17
Dependent Claim
33 words
A process as set forth in claim 4 wherein said thermoplastic resin is copolymer of ethylene and tetrafluoroethylene and wherein said low pressure P 2 ranges from 5 to 40 kg/cm 2 .
Claim 18
Dependent Claim
29 words
A process as set forth in claim 5, wherein said thermoplastic resin is high density polyethylene and wherein said low pressure ranges from 3 to 25 kg/cm 2 .
Claim 19
Dependent Claim
31 words
A process as set forth in claim 5, wherein said thermoplastic resin is low density polyethylene and wherein said low pressure P 2 ranges from 3 to 25 kg/cm 2 .
Claim 20
Dependent Claim
33 words
A process as set forth in claim 5, wherein said thermoplastic resin is copolymer of ethylene and vinylacetate and wherein said low pressure P 2 ranges from 2 to 25 kg/cm 2 .
Claim 21
Dependent Claim
29 words
A process as set forth in claim 5, wherein said thermoplastic resin is polypropylene and wherein said low pressure P 2 ranges from 5 to 25 kg/cm 2 .
Claim 22
Dependent Claim
29 words
A process as set forth in claim 5, wherein said thermoplastic resin is nylon and wherein said low pressure P 2 ranges from 6 to 25 kg/cm 2 .
Claim 23
Dependent Claim
31 words
A process as set forth in claim 5, wherein said thermoplastic resin is copolymer of ethylene and tetrafluoroethylene and wherein said low pressure ranges from 3 to 25 kg/cm 2 .
References Cited (Backward Citations)
US2768407A
Cited
US2751627A
Cited
US2714748A
Cited
US3054146A
Cited
US3217364A
Cited
US3489830A
Cited
US3538203A
Cited
US3806291A
Cited
US3879155A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-26 | 1980-04-26 | 1980-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-26 | 1984-04-26 | 1984-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-26 | 1988-04-26 | 1988-10-26 | $7700.00 | Window Closed / Lapsed |