Microcellular closed cell foams and their method of manufacture
Assignee: Massachusetts Institute of Technology
•
Filing: 1982-07-30
•
Granted: 1984-09-25
•
Expires: 2002-07-30
Abstract
Abstract Microcellular foam materials having void fractions of about 5 to 30 percent and uniform void sizes on the order of 2 to 25 microns are produced by pre-saturating the material to be processed with a uniform concentration of a gas while controlling temperature and pressure to avoid cell nucleation. Processing is also done under pressure to avoid nucleation. After processing, pressure is released and cell nucleation occurs at or near the glass transition temperature of the material; it is then cooled quickly to preserve the microcellular structure.
Inventors
- 👤 Jane E. Martini-Vvedensky
- 👤 Nam P. Suh
- 👤 Francis A. Waldman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:18
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; B; B29; B29C; B29C44/00; B29C44/34; B29C44/3469; B29C44/348; B29C44/36; B29C44/38; B29C44/42; B29C44/46; B29C44/50; B29C44/505; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/13; Y10S264/83
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
104 words
A method for producing closed cell, microcellular-foamed structures in pre-formed polymeric materials, the method comprising: (a) saturating the material at an elevated pressure between about 1 cc (STP)/gram and about 4 cc (STP)/gram with a uniform concentration of a non-reactive gas; (b) heating the material to its glass transition temperature; (c) reducing the pressure to a state where the material is super-saturated with gas and a very large number of cells are nucleated; and (d) rapidly dropping the temperature of the material to prevent cell growth, whereby a foamed polymeric material having voids on the order of about 2 to 25 microns is produced.
Claim 2
Independent Claim
104 words
A method for producing closed cell, microcellular-foamed structures in pre-formed polymeric materials, the method comprising: (a) saturating the material at an elevated pressure between about 1 cc (STP)/gram and about 4 cc (STP)/gram with a uniform concentration of a non-reactive gas; (b) heating the material to its glass transition temperature; (c) reducing the pressure to a state where the material is super-saturated with gas and a very large number of cells are nucleated; and (d) rapidly dropping the temperature of the material to prevent cell growth, whereby a foamed polymeric material having voids on the order of about 2 to 25 microns is produced.
Claim 3
Dependent Claim
70 words
A microcellular foam material formed by saturating a polymeric material at about its glass transition temperature with a uniform concentration of a gas, reducing the pressure, and then cooling the material, thereby controlling the nucleation of cells within the material, the material being characterized by uniformaly packed, closed cells ranging in size from about 2 microns to 25 microns and having a void fraction of about 5 to 30 percent.
Claim 4
Dependent Claim
70 words
A microcellular foam material formed by saturating a polymeric material at about its glass transition temperature with a uniform concentration of a gas, reducing the pressure, and then cooling the material, thereby controlling the nucleation of cells within the material, the material being characterized by uniformaly packed, closed cells ranging in size from about 2 microns to 25 microns and having a void fraction of about 5 to 30 percent.
Claim 5
Dependent Claim
21 words
The material of claim 2 wherein the material is further characterized by uniform closed cells less than 10 microns in diameter.
Claim 6
Dependent Claim
22 words
The material of claim 2 wherein the material is further characterized by having a void fraction of about 20 to 25 percent.
Claim 7
Dependent Claim
20 words
The material of claim 2 wherein the material further comprises at least one surface composed of a non-foamed thin skin.
Claim 8
Independent Claim
131 words
A method of processing polymeric materials to produce closed cell, microcellular foams, the method comprising: (a) saturating the material at an elevated pressure and at a temperature below the glass transition temperature of the material with a uniform concentration of gas; (b) heating the material to a molten state to render it processable; (c) shaping the material at an elevated pressure sufficiently high to prevent cell nucleation within the material (d) reducing the temperature and pressure to a state where the material is super-saturated with gas and a very large number of cells are nucleated; and (e) rapidly dropping the temperature of the material after nucleation has occurred to prevent cell growth, whereby a foamed polymeric material having voids on the order of about 2 to to 25 microns is produced.
Claim 9
Independent Claim
131 words
A method of processing polymeric materials to produce closed cell, microcellular foams, the method comprising: (a) saturating the material at an elevated pressure and at a temperature below the glass transition temperature of the material with a uniform concentration of gas; (b) heating the material to a molten state to render it processable; (c) shaping the material at an elevated pressure sufficiently high to prevent cell nucleation within the material (d) reducing the temperature and pressure to a state where the material is super-saturated with gas and a very large number of cells are nucleated; and (e) rapidly dropping the temperature of the material after nucleation has occurred to prevent cell growth, whereby a foamed polymeric material having voids on the order of about 2 to to 25 microns is produced.
Claim 10
Dependent Claim
44 words
The method of claim 6 wherein the step of saturating the material at an elevated pressure further comprises saturating the material at an elevated pressure to produce an initial uniform concentration of gas in the material of about 1 cc (STP)/gram to 4 cc(STP)/gram.
Claim 11
Dependent Claim
30 words
The method of claim 6 wherein the step of saturating the material at an elevated pressure with a uniform concentration of gas further comprises saturating the material with argon gas.
Claim 12
Dependent Claim
33 words
The method of claim 6 wherein the step of saturating the material at an elevated pressure with a uniform concentration of gas further comprises saturating the material with a uniform concentration of nitrogen.
Claim 13
Dependent Claim
34 words
The method of claim 6 wherein the step of saturating the material at an elevated pressure with a uniform concentration of gas further comprises saturating the material with a uniform concentration of carbon dioxide.
Claim 14
Dependent Claim
40 words
The method of claim 6 wherein the step of reducing the temperature and pressure to a state where the material is supersaturated further comprises the steps of first reducing the temperature in a quenchant chamber and then reducing the pressure.
Claim 15
Dependent Claim
28 words
The method of claim 11 wherein the step of reducing the temperature in a quenchant chamber further comprises reducing the temperature in a quenchant chamber filled with glycerin.
Claim 16
Dependent Claim
20 words
The method of claim 6 wherein the step of processing the material further comprises processing the material by die extrusion.
Claim 17
Dependent Claim
20 words
The method of claim 6 wherein the step of processing the material further comprises processing the material by injection molding.
Claim 18
Dependent Claim
9 words
The material produced by the method of claim 1.
Claim 19
Dependent Claim
21 words
The material of claim 15 wherein the average void size is on the order of about 2 microns to 10 microns.
Claim 20
Dependent Claim
23 words
The material of claim 16 wherein the material is further characterized by having a average void size of about 25 microns or less.
Claim 21
Dependent Claim
22 words
The material of claim 15 wherein the material is further characterized as having a void fraction of about 5 to 30 percent.
Claim 22
Dependent Claim
10 words
The material of claim 15 wherein the material is polystyrene.
Claim 23
Dependent Claim
11 words
The material of claim 15 wherein the material is impact polystyrene.
Claim 24
Dependent Claim
15 words
The material of claim 15 wherein the material further comprises a polymeric material with fillers.
Claim 25
Dependent Claim
12 words
The material of claim 7 wherein the fillers further comprise carbon black.
Claim 26
Dependent Claim
11 words
The material of claim 15 wherein the material is a polyester.
Claim 27
Dependent Claim
10 words
The material of claim 15 wherein the material is nylon.
Claim 28
Dependent Claim
11 words
The material of claim 15 wherein the material is a polycarbonate.
References Cited (Backward Citations)
US2531665A
Cited
US2590156A
Cited
US2751627A
Cited
US2783894A
Cited
GB899389A
Cited
US3121760A
Cited
US3436445A
Cited
US3491032A
Cited
US3558764A
Cited
US3551362A
Cited
US3544384A
Cited
US3647329A
Cited
US3871897A
Cited
US3745057A
Cited
US3822331A
Cited
US3796779A
Cited
US3922328A
Cited
US3806291A
Cited
US3962387A
Cited
US4096218A
Cited
US3988404A
Cited
US4229395A
Cited
US4352893A
Cited
US4284596A
Cited
US4360484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |