Process for preparing a pigmentary titanium dioxide

Claim 2

A process for preparing a titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag to a particle size of about 10 microns or less; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate, and an alkali metal oxide; (c) roasting the mixture at about 700° C. to about 900° C.; (d) digesting the roasted material in hydrochloric acid at about 90° C. to about 110° C. such that a suspension of a solid product in the acid is formed; and (e) calcining at least the solid product at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 3

The process of claim 1 wherein the titanium dioxide-bearing material is sorelslag.

Claim 4

The process of claim 2 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 5

The process of claim 3 wherein in step (b) the sorelslag is mixed with the sodium hydroxide in a ratio by weight of about 100:30 to about 100:60.

Claim 6

The process of claim 1 including the step of micronizing the calcined product to below about 0.3 micron.

Claim 7

The process of claim 1 wherein the digesting step is carried out at least two times.

Claim 8

A process for preparing a titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to a particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; and (e) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 9

A process for preparing a titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to a particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; and (e) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 10

The process of claim 7 wherein the titanium dioxide-bearing material is sorelslag.

Claim 11

The process of claim 8 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 12

The process of claim 9 wherein in step (b) the sorelslag is mixed with the sodium hydroxide in a ratio by weight of about 100:30 to about 100:60.

Claim 13

The process of claim 7 including the step of micronizing the calcined product to below about 0.3 micron.

Claim 14

The process of claim 7 wherein the digesting step is carried out at least two times.

Claim 15

A process for preparing a titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to a particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) filtering solubilized material from the roasted mixture; (e) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; (f) filtering the titanium dioxide material from the acid; and (g) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 16

A process for preparing a titanium dioxide pigment comprising the steps of: (a) sandmilling a mixture of titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag, and an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide in water to a particle size of about 10 microns or less; (b) roasting the mixture at about 700° C. to about 900° C.; (c) sandmilling the roasted mixture in water; (d) filtering solubilized material from the roasted mixture; (e) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; (f) filtering the titanium dioxide material from the acid; and (g) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 17

The process of claim 13 wherein the titanium dioxide-bearing material is sorelslag.

Claim 18

The process of claim 14 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 19

The process of claim 15 wherein in step (b) the sorelslag is mixed with the sodium hydroxide in a ratio by weight of about 100:30 to about 100:60.

Claim 20

The process of claim 13 including the step of micronizing the calcined product to below about 0.3 micron.

Claim 21

The process of claim 13 wherein the digest-ing step is carried out at least two times.

Claim 22

A process for preparing a titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag to a particle size of about 10 microns or less; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide; (c) roasting the mixture at about 700° C. to about 900° C.; (d) sandmilling the roasted mixture in water; (e) filtering solubilized material from the roasted mixture; (f) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; (g) filtering the titanium dioxide material from the acid; (h) washing the titanium dioxide material; and (i) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 23

A process for preparing a titanium dioxide pigment comprising the steps of: (a) comminuting a titanium dioxide-bearing material selected from the group consisting of sorelslag, beneficiated ilmenite and chloride slag to a particle size of about 10 microns or less; (b) mixing the titanium dioxide-bearing material with an alkali metal compound selected from the group consisting of an alkali metal hydroxide, an alkali metal carbonate or an alkali metal oxide; (c) roasting the mixture at about 700° C. to about 900° C.; (d) sandmilling the roasted mixture in water; (e) filtering solubilized material from the roasted mixture; (f) digesting the roasted mixture in hydrochloric acid at about 90° C. to about 110° C. to form a titanium dioxide material; (g) filtering the titanium dioxide material from the acid; (h) washing the titanium dioxide material; and (i) calcining the titanium dioxide material at a temperature ranging from about 800° C. to about 1000° C. to form a titanium dioxide pigment.

Claim 24

The process of claim 19 wherein the titanium dioxide-bearing material is sorelslag.

Claim 25

The process of claim 20 wherein the alkali metal hydroxide is sodium hydroxide.

Claim 26

The process of claim 21 wherein in step (b) the sorelslag is mixed with the sodium hydroxide in a ratio by weight of about 100:30 to about 100:60.

Claim 27

The process of claim 19 including the step of micronizing the calcined product to below about 0.3 micron.

Claim 28

The process of claim 19 wherein the digesting step is carried out at least two times.

Claim 29

The process of claims 1, 7, 13 or 19 wherein the digesting is carried out in about 10 to about 120 minutes.

Claim 30

The process of claims 1, 7, 13 or 19 wherein the titanium dioxide pigment produced after calcination has a brightness (R∞) of about 88 percent to about 93 percent.

Claim 31

The process of claims 1, 7, 13 or 19 wherein the titanium dioxide pigment produced after calcination has a scattering coefficient (S) of about 4000 cm 2 /g to about 9000 cm 2 /g.

Claim 32

The process of claims 1, 7, 13 or 19 wherein the titanium dioxide pigment produced after calcination has an iron content of about 30 ppm to about 520 ppm.