US4751203A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manufacturing vitreous beads
Assignee: AGC Glass Europe SA
•
Filing: 1986-06-20
•
Granted: 1988-06-14
•
Expires: 2006-06-20
Abstract
Abstract A process of manufacturing vitreous beads is disclosed in which feedstock particles of a glass-former composition containing less than 15% by dry weight of sodium and potassium calculated as their respective oxides and containing chemically bound water, are fed through a heating zone in which the particles are vitrified and spherulized and the resulting vitreous beads are cooled. The vitrifiable oxide forming elements of said glass-former composition may be chemically interlinked, and the feedstock may be prepared as a silica-based gel or precipitate having a composition suitable for vitrification into a glass of a desired composition which by virtue of its low alkali content is resistant to hydrolytic attack. By control of the cellulating agent content (bound water and optionally a gas evolving salt radical such as nitrate or sulphate) of the feedstock, and its granulometry, the relative proportions of solid and hollow beads which will be produced in a given spherulizing run can be controlled.
Inventors
- 👤 Francois Toussaint
- 👤 Pierre Goelff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:19
CPC Classifications
C; C03; C03C; C03C12/00; C03C1/00; C03C1/006; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
129 words
In a process for manufacturing vitreous beads, including the steps of: feeding a glass-forming composition in particulate form through a heating zone of a spherulizing furnace where the glass-forming composition is heated to a temperature effective to vitrify and spherulize the particles thereof; and cooling the resulting vitreous beads, the improvement comprising: providing a glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which contains chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides, and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates.
Claim 2
Dependent Claim
129 words
In a process for manufacturing vitreous beads, including the steps of: feeding a glass-forming composition in particulate form through a heating zone of a spherulizing furnace where the glass-forming composition is heated to a temperature effective to vitrify and spherulize the particles thereof; and cooling the resulting vitreous beads, the improvement comprising: providing a glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which contains chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides, and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates.
Claim 3
Dependent Claim
54 words
The process of claim 1, wherein the glass-forming composition has a particle size range and a content of at least one substance which becomes gaseous during feeding of the composition through the heating zone effective to obtain at least 20% by weight of the vitreous beads produced having a relative density greater than 1.0.
Claim 4
Dependent Claim
28 words
The process of claim 1, wherein the glass-forming composition contains less than 10% by dry weight of sodium and potassium calculated as the total of their respective oxides.
Claim 5
Dependent Claim
14 words
The process of claim 1, wherein the glass-forming composition is substantially insoluble in water.
Claim 6
Dependent Claim
27 words
The process of claim 1, wherein the glass-forming composition in particulate form has a particle size range which includes particles ranging from 20 μm to 250 μm.
Claim 7
Dependent Claim
26 words
The process of claim 1, wherein the glass-forming composition further comprises ions which serve as devitrification nucleating agents and the vitreous beads produced are vitro-ceramic beads.
Claim 8
Dependent Claim
24 words
The process of claim 6, wherein the ions which serve as devitrification nucleating agents comprise at least one of titanium ions and zirconium ions.
Claim 9
Dependent Claim
23 words
The process of claim 6, including the further step of subjecting the vitreous beads to a treatment to convert them into vitro-ceramic beads.
Claim 10
Dependent Claim
32 words
The process of claim 1, wherein the glass-forming composition further comprises at least one of boron and aluminum in an amount of at least 10% dry weight calculated as the respective oxide.
Claim 11
Dependent Claim
32 words
The process of claim 1, wherein the glass-forming composition further comprises at least one of boron and aluminum in an amount of at least 15% dry weight calculated as the respective oxide.
Claim 12
Dependent Claim
36 words
The process of claim 1, wherein the glass-forming composition further comprises glass-forming components which vitrify to form a special glass selected from the group consisting of an alumino-silicate glass, a boro-silicate glass, and an alumino-boro-silicate glass.
Claim 13
Dependent Claim
105 words
A glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which is convertible to vitreous beads by heating in a spherulizing furnace at a temperature effective to vitrify and spherulize the glassforming composition, the composition comprising: at least one substance containing chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides; and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates.
Claim 14
Dependent Claim
105 words
A glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which is convertible to vitreous beads by heating in a spherulizing furnace at a temperature effective to vitrify and spherulize the glassforming composition, the composition comprising: at least one substance containing chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides; and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates.
Claim 15
Dependent Claim
27 words
The composition of claim 12, wherein the composition comprises less than 10% by dry weight of sodium and potassium calculated as the total of their respective oxides.
Claim 16
Dependent Claim
13 words
The composition of claim 12, wherein the composition is substantially insoluble in water.
Claim 17
Dependent Claim
27 words
The composition of claim 12, wherein the glass-forming composition in particulate form has a particle size range which includes particles ranging from 20 μm to 250 μm.
Claim 18
Dependent Claim
24 words
The composition of claim 12, wherein the glass-forming composition further comprises ions which function as devitrification nucleating agents for the formation of vitro-ceramic beads.
Claim 19
Dependent Claim
24 words
The composition of claim 16, wherein the ions which function as devitrification nucleating agents comprise at least one of titanium ions and zirconium ions.
Claim 20
Dependent Claim
33 words
The composition of claim 12, wherein the glass-forming composition further comprises at least one of boron and aluminum in an amount of at least 10% by dry weight calculated as the respective oxide.
Claim 21
Dependent Claim
33 words
The composition of claim 12, wherein the glass-forming composition further comprises at least one of boron and aluminum in an amount of at least 15% by dry weight calculated as the respective oxide.
Claim 22
Dependent Claim
37 words
The composition of claim 12, wherein the glass-forming composition further comprises glass-forming components which are vitrifiable to form a special glass selected from the group consisting of an alumino-silicate glass, a boro-silicate glass, and an alumino-boro-silicate glass.
Claim 23
Dependent Claim
55 words
The composition of claim 12, wherein the glass-forming composition has a particle size range and a content of at least one substance which becomes gaseous during feeding of the composition through the spherulizing furnace effective to obtain at least 20 percent by weight of the vitreous beads produced having a relative density greater than 1.0.
Claim 24
Dependent Claim
122 words
Vitreous beads produced by a process comprising: providing a glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which contains chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides, and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates; feeding the glass-forming composition in particulate form through a heating zone of a spherulizing furnace where the glass-forming composition is heated to a temperature effective to vitrify and spherulize the particles thereof; and cooling the resulting vitreous beads.
Claim 25
Dependent Claim
122 words
Vitreous beads produced by a process comprising: providing a glass-forming composition in particulate form which has particles falling within a particle size range effective to form both hollow vitreous beads and solid vitreous beads, which is one of a silica-based gel and a silica-based precipitate and which contains chemically bound water, less than 15% by dry weight of sodium and potassium calculated as the total of their respective oxides, and at least one gas-evolving salt selected from the group consisting of nitrates and sulfates; feeding the glass-forming composition in particulate form through a heating zone of a spherulizing furnace where the glass-forming composition is heated to a temperature effective to vitrify and spherulize the particles thereof; and cooling the resulting vitreous beads.
References Cited (Backward Citations)
US3030215A
Cited
US3242032A
Cited
GB1011596A
Cited
US3838998A
Cited
US4113915A
Cited
US4002482A
Cited
US4063916A
Cited
US4133854A
Cited
US4367919A
Cited
FR2463108A2
Cited
US4340642A
Cited
US4336338A
Cited
GB2151610A
Cited
US4391646A
Cited
US4448599A
Cited
US4472185A
Cited
US4564556A
Cited
US4640905A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |