Transparent non-vitreous ceramic particulate
Assignee: 3M Co
•
Filing: 1984-09-24
•
Granted: 1986-01-14
•
Expires: 2004-09-24
Abstract
Abstract Solid, transparent, non-vitreous, ceramic particles useful as lens elements in retroreflective pavement markings characterized by having: A. at least one metal oxide phase; and B. an average minimum dimension of more than 125 micrometers. These particles are formed by various sol gel techniques, one example of which is the chemical gelation of titania sols by first mixing with glacial acetic acid, then with ammonium acetate, followed by formation of microspheres in 2-ethylhexanol. Microspheres of this ceramic composition can have relatively large diameters (e.g. over 200-1000 micrometers) making them quite useful as retroreflective lens elements in pavement marking sheet materials.
Inventors
- 👤 Roger W. Lange
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:52
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; B; B82; B82Y; B82Y30/00; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C01B33/00; C01B33/113; C01B33/12; C01B33/16; C01G; C01G23/00; C01G23/04; C01G23/047; C01G25/00; C01G25/02; C04B35/14; C04B35/46; C04B35/481; C04B35/49; C04B35/622; C04B35/624; C09; C09C; C09C1/00; C09C1/0009; C09C1/0012; E; E01; E01F; E01F9/00; E01F9/50; E01F9/506; E01F9/524; C01P; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/51; C01P2004/60; C01P2004/61; C01P2004/64; C01P2004/80; C01P2004/82; C01P2006/00; C01P2006/21; C01P2006/60; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/24413; Y10T428/24421; Y10T428/2443; Y10T428/25; Y10T428/252; Y10T428/256; Y10T428/257; Y10T428/29; Y10T428/2982; Y10T428/31
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
49 words
Solid, transparent, non-vitreous, dense, ceramic microspheres comprising at least one crystalline phase comprising at least one metal oxide other than titanium dioxide, although titanium dioxide may be present in minor amounts, and having an average particle size of more than 125 micrometers, said microspheres being useful as lens elements.
Claim 2
Dependent Claim
49 words
Solid, transparent, non-vitreous, dense, ceramic microspheres comprising at least one crystalline phase comprising at least one metal oxide other than titanium dioxide, although titanium dioxide may be present in minor amounts, and having an average particle size of more than 125 micrometers, said microspheres being useful as lens elements.
Claim 3
Dependent Claim
22 words
The solid, transparent ceramic microspheres of claim 1 which are further characterized by an average grain size no larger than 1000 angstroms.
Claim 4
Dependent Claim
19 words
The transparent, ceramic microspheres of claim 1 which are further characterized by an average hardness greater than 400 Knoop.
Claim 5
Dependent Claim
14 words
The transparent, non-vitreous, ceramic microspheres of claim 1 wherein the metal oxide is zirconia.
Claim 6
Dependent Claim
16 words
The ceramic microspheres of claim 1 wherein the metal oxide is mixed with another metal oxide.
Claim 7
Dependent Claim
18 words
The transparent, ceramic microspheres of claim 1 comprising at least one polycrystalline and at least one amorphous phase.
Claim 8
Dependent Claim
14 words
The transparent, ceramic microspheres of claim 6 in which the amorphous phase comprises silica.
Claim 9
Dependent Claim
14 words
The transparent, ceramic microspheres of claim 7 in which the polycrystalline phase comprises zirconia.
Claim 10
Dependent Claim
17 words
The transparent, ceramic microspheres of claim 8 wherein the zirconia is predominantly of the tetragonal crystal structure.
Claim 11
Dependent Claim
23 words
The transparent, ceramic microspheres of claim 8 wherein the molar ratio of zirconia to silica is in the range of 10:1 to 1:10.
Claim 12
Dependent Claim
22 words
A sheet material comprising polymeric binder film in which is embedded a multiplicity of the solid, transparent, ceramic microspheres of claim 1.
Claim 13
Dependent Claim
31 words
A pavement marking sheet material comprising: a. a base sheet adherable to a roadway surface; and b. the sheet material of claim 11 adhered to one surface of the base sheet.
Claim 14
Dependent Claim
34 words
A retroreflective sheet material comprising a polymeric binder film in which a monolayer of the microspheres of claim 1 are embedded and in which said microspheres are in optical connection with a reflecting means.
Claim 15
Dependent Claim
17 words
Grinding grit comprising the solid, non-vitreous, ceramic microspheres of claim 6 which have been reduced in size.
Claim 16
Dependent Claim
26 words
Solid, transparent, non-vitreous, ceramic microspheres comprising polycrystalline titanium dioxide and having an average particle size greater than 200 micrometers, said microspheres being useful as lens elements.
Claim 17
Dependent Claim
26 words
Solid, transparent, non-vitreous, ceramic microspheres comprising polycrystalline titanium dioxide and having an average particle size greater than 200 micrometers, said microspheres being useful as lens elements.
Claim 18
Dependent Claim
46 words
A formed mass of discrete, solid, dense, transparent, non-vitreous, ceramic microspheres averaging at least 125 micrometers in diameter and useful as lens elements in retroreflective pavement markings, said microspheres comprising an amorphous, grainy silica matrix filled with zirconia crystallites less than about 1000 angstroms in size.
Claim 19
Dependent Claim
46 words
A formed mass of discrete, solid, dense, transparent, non-vitreous, ceramic microspheres averaging at least 125 micrometers in diameter and useful as lens elements in retroreflective pavement markings, said microspheres comprising an amorphous, grainy silica matrix filled with zirconia crystallites less than about 1000 angstroms in size.
Claim 20
Dependent Claim
30 words
Solid, transparent, non-vitreous, ceramic microspheres consisting essentially of silica, having an average particle size of more than 125 micrometers, and being fully dense, said microspheres being useful as lens elements.
Claim 21
Dependent Claim
30 words
Solid, transparent, non-vitreous, ceramic microspheres consisting essentially of silica, having an average particle size of more than 125 micrometers, and being fully dense, said microspheres being useful as lens elements.
Claim 22
Dependent Claim
30 words
A pavement marking containing solid, transparent, non-vitreous, dense ceramic microspheres averaging greater than 125 micrometers in diameter and which consist essentially of grains less than about 1000 angstroms in size.
Claim 23
Dependent Claim
30 words
A pavement marking containing solid, transparent, non-vitreous, dense ceramic microspheres averaging greater than 125 micrometers in diameter and which consist essentially of grains less than about 1000 angstroms in size.
Claim 24
Dependent Claim
110 words
A chemical gelation process for making solid, non-vitreous ceramic particles comprising the steps of: (i) mixing a sol comprising a source of a metal oxide selected from the group consisting of titania, silica, zirconia and mix;tures of the foregoing with a gelling agent comprising ammonium acetate; (ii) adding the composition from step (i) to a forming fluid in which particles form; (iii) separating the gel particles from the forming agent; (iv) drying the gel particles from step (iii); (v) firing the particles at temperatures between about 500° and 1200° C. in order to form fired, ceramic particles; and (vi) allowing the fired, transparent, ceramic particles from step (v) to cool.
Claim 25
Dependent Claim
110 words
A chemical gelation process for making solid, non-vitreous ceramic particles comprising the steps of: (i) mixing a sol comprising a source of a metal oxide selected from the group consisting of titania, silica, zirconia and mix;tures of the foregoing with a gelling agent comprising ammonium acetate; (ii) adding the composition from step (i) to a forming fluid in which particles form; (iii) separating the gel particles from the forming agent; (iv) drying the gel particles from step (iii); (v) firing the particles at temperatures between about 500° and 1200° C. in order to form fired, ceramic particles; and (vi) allowing the fired, transparent, ceramic particles from step (v) to cool.
Claim 26
Dependent Claim
27 words
The chemical gelation process of claim 19 wherein the metal oxide is titania and which further comprises mixing the titania sol with acetic acid before step (i).
Claim 27
Dependent Claim
21 words
The chemical gelation process of claim 19 which further comprises adding a colloidal silica sol to the sol of step (i).
Claim 28
Dependent Claim
22 words
The chemical gelation process of claim 21 wherein the silica sol has a colloid particle size of less than about 200 angstroms.
Claim 29
Dependent Claim
27 words
The chemical gelation process of claim 19 in which the metal oxide includes zirconia and the temperature of step (v) is between about 950° and 1100° C.
Claim 30
Dependent Claim
18 words
The chemical gelation process of claim 19 wherein the forming fluid of step (ii) is substantially water immiscible.
Claim 31
Dependent Claim
19 words
The solid, transparent, non-vitreous, ceramic microspheres of claim 15 wherein the titanium dioxide is mixed with another metal oxide.
References Cited (Backward Citations)
US2354018A
Cited
US2326634A
Cited
US2963378A
Cited
US3026177A
Cited
US3313602A
Cited
US3442821A
Cited
US3709706A
Cited
US3714071A
Cited
US3700305A
Cited
US3872217A
Cited
US3795524A
Cited
US3941719A
Cited
US4166147A
Cited
US4025159A
Cited
US4117192A
Cited
US4349456A
Cited
US4148864A
Cited
US4367919A
Cited
US4255286A
Cited
US4248932A
Cited
US4314827A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-01-13 | 1989-07-15 | 1990-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-01-13 | 1993-07-15 | 1994-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-01-13 | 1997-07-15 | 1998-01-14 | $7700.00 | Window Closed / Lapsed |