Process for making contacts and interconnections using direct-reacted silicide
Assignee: Texas Instruments Inc
•
Filing: 1985-09-11
•
Granted: 1988-06-14
•
Expires: 2005-09-11
Abstract
Abstract Metal contacts and interconnections for semiconductor integrated circuits are formed by a process using direct-reacted silicide to increase step or sidewall coverage. A thin layer of titanium or the like is deposited, extending into a contact hole, then polysilicon is deposited over the titanium coating the vertical sides of steps or apertures. A second thin layer of titanium is deposited, then a heat treatment forms silicide to create a titanium silicide layer, including conductive sidewalls or a plug. Metal contacts and interconnections then engage the direct-reacted silicide rather than relying upon step coverage.
Inventors
- 👤 Dirk N. Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:23
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; Y; Y10; Y10S; Y10S148/00; Y10S148/147
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
143 words
A method of making contact to a face of a semiconductor body through an aperture in an insulating layer on said face, comprising the steps of: (a) depositing a thin layer of refractory metal on said face to cover the semiconductor body within said aperture and also to cover the insulating layer and the sidewalls of the aperture, (b) depositing a layer of semiconductor material on the thin layer of refractory metal extending over said insulating layer and on the sidewalls, (c) depositing another thin layer of refractory metal on the layer of semiconductor material to extend continuously over the insulator and down the sidewall into the aperture, (d) reacting the thin layers of refractory metal with the semiconductor material, and (e) depositing a metal layer over said insulator to make contact to the reacted refractory metal and semiconductor material at said aperture.
Claim 2
Independent Claim
143 words
A method of making contact to a face of a semiconductor body through an aperture in an insulating layer on said face, comprising the steps of: (a) depositing a thin layer of refractory metal on said face to cover the semiconductor body within said aperture and also to cover the insulating layer and the sidewalls of the aperture, (b) depositing a layer of semiconductor material on the thin layer of refractory metal extending over said insulating layer and on the sidewalls, (c) depositing another thin layer of refractory metal on the layer of semiconductor material to extend continuously over the insulator and down the sidewall into the aperture, (d) reacting the thin layers of refractory metal with the semiconductor material, and (e) depositing a metal layer over said insulator to make contact to the reacted refractory metal and semiconductor material at said aperture.
Claim 3
Dependent Claim
12 words
A method according to claim 1 wherein said semiconductor material is silicon.
Claim 4
Dependent Claim
22 words
A method according to claim 2 wherein said layer of semiconductor material is polycrystalline silicon, and said insulating layer is silicon oxide.
Claim 5
Dependent Claim
12 words
A method according to claim 2 wherein said refractory metal is titanium.
Claim 6
Independent Claim
131 words
A method of making a metal connection at a face of a semiconductor body, said connection extending over a step in an insulating layer on said face, comprising the steps of: (a) depositing a first layer of refractory metal on said face to cover the semiconductor body and to cover the insulating layer and the sidewall of the step, (b) depositing a layer of semiconductor material on the first layer of refractory metal over said face and said sidewall, (c) depositing a second layer of said refractory metal on the layer of semiconductor material to extend continuously across the step, (d) reacting the refractory metal layers with the semiconductor material, and (e) depositing a conductor on said face to engage the reacted refractory metal layers and semiconductor material at said step.
Claim 7
Independent Claim
131 words
A method of making a metal connection at a face of a semiconductor body, said connection extending over a step in an insulating layer on said face, comprising the steps of: (a) depositing a first layer of refractory metal on said face to cover the semiconductor body and to cover the insulating layer and the sidewall of the step, (b) depositing a layer of semiconductor material on the first layer of refractory metal over said face and said sidewall, (c) depositing a second layer of said refractory metal on the layer of semiconductor material to extend continuously across the step, (d) reacting the refractory metal layers with the semiconductor material, and (e) depositing a conductor on said face to engage the reacted refractory metal layers and semiconductor material at said step.
Claim 8
Dependent Claim
12 words
A method according to claim 5 wherein said semiconductor material is silicon.
Claim 9
Dependent Claim
22 words
A method according to claim 6 wherein said layer of semiconductor material is polycrystalline silicon, and said insulating layer is silicon oxide.
Claim 10
Dependent Claim
12 words
A method according to claim 7 wherein said refractory metal is titanium.
Claim 11
Dependent Claim
19 words
A method according to claim 5 wherein said refractory metal layers are titanium and said semiconductor material is silicon.
References Cited (Backward Citations)
US3740835A
Cited
US3918149A
Cited
US4180596A
Cited
US4322453A
Cited
US4398341A
Cited
US4507853A
Cited
US4545116A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-14 | 1991-12-14 | 1992-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-14 | 1995-12-14 | 1996-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-14 | 1999-12-14 | 2000-06-14 | $7700.00 | Window Closed / Lapsed |