Clear polyvinyl chloride articles and compositions

Claim 2

A polyvinyl chloride article consisting essentially of a PVC compostion wherein said PVC composition comprises: (A) 100 parts by weight of PVC; (B) stabilizer system comprising (i) from about 0.005 part by weight to about 1.0 part by weight of at least one zinc soap and (ii) from 0 to about 1.0 part by weight of at least one calcium soap; (C) co-stabilizer system comprising from about 0.2 part by weight to about 1.5 parts by weight of at least one co-stabilizer compound selected from the group consisting of compounds having the formula: OH--X--O--R and R--O--X--O--R wherein X is a straight chain, branched or cyclic radical having: (a) from 2 to about 20 oxygen atoms, wherein at least one of said oxygen atoms forms an ether linkage and the remainder forms bonds selected from the group consisting of ether, epoxy and hydroxy; (b) from about 4 to about 60 carbon atoms; wherein R is a straight chain radical having from about 5 to about 40 carbon atoms; (D) at least one lubricant; (E) at least one impact modifier; wherein said polyvinyl chloride article is characterized by having the following properties: (I) high degree of clarity as defined by having a percent light transmission greater than that described by the following formula: % Light Transmission=100-460 (inch thickness) as measured according to ASTM D-1746; (II) percent haze measured according to ASTM D-1003-61 and having a value less than that described by the following formula: % Haze=184.6 (inch thickness); (III) bluch less than 30% at 0.065 inch thickness after exposure for 48 hours at 50° C. in a 50/50 ethanol water solution; (IV) color stability time greater than 16 minutes to turn black when aged at 200° C., according to ASTM D-1925; (V) said PVC article does not impart an objectionable taste nor odor to other materials in contact with said PVC article; (VI) yellowness index less than about 13% at 0.065 inch thickness as measured according to ASTM D-1925 on an unpigmented compound.

Claim 3

A polyvinyl chloride article of claim 1 wherein said co-stabilizer in (C) is selected from the group consisting of oligo-glycerol, oligo-propylene glycol and olig-ethylene glycol; wherein said oligo-glycerol has the formula: ##STR6## said glycerol may be straight chain, branched or cyclic; wherein n=2 to 20 and R is a straight chain radical having from about 5 to abut 40 carbon atoms; said oligo-proplene glycol has the formula: ##STR7## wherein n and R are as defined above; said oligo-ethylene glycol has the formula: ##STR8## wherein n and R are as defined above.

Claim 4

An article of claim 2 wherein said oligo-glycerol is an ester of oligo-glycerol and a fatty acid wherein the molar ratio of glycerol to fatty acid is greater than 1:1.

Claim 5

An article of claim 3 wherein said molar ratio is greater than 2:1.

Claim 6

An article of claim 4 wherein said ester of oligo-glycerol and a fatty acid is selected from the group consisting of triglycerol monosterate, hexaglycerol monosterate of triglycerol monostearate, hexaglycerol monostearate and hexaglycerol distearate.

Claim 7

An article of claim 5 wherein the level of said ester is from about 0.4 part to about 1.5 parts by weight of PVC.

Claim 8

An article of claim 6 wherein the PVC is a PVC homopolymer.

Claim 9

An article of claim 7 wherein the levels of each of the zinc soap and calcium soap is from about 0.03 part by weight to about 0.30 part by weight per 100 parts by weight of PVC.

Claim 10

An article of claim 1 wherein in addition to the co-stabilizer of (C) there is present at least two additional co-stabilizers selected from the group consisting of phosphite, polymeric phosphite, beta-diketone and epoxidized soybean oil.

Claim 11

An article of claim 1 wherein said article has a percent light transmission greater than that described by the formula: % light transmission=100-400 (inch thickness).

Claim 12

An article of claim 10 wherein said article has a perent haze less than that described by the formula: % haze=100 (inch thickness).

Claim 13

An article of claim 11 wherein said article is substantially free of tin stabilizer.

Claim 14

An article of claim 12 wherein said article is a bottle.

Claim 15

A bottle of claim 13 having a wall thickness of from about 0.005 inch to about 0.100 inch.

Claim 16

An article of claim 1 wherein said article is a film.

Claim 17

A film of claim 15 wherein said film has a thickness of from about 0.001 inch to about 0.100 inch.

Claim 18

a polyvinyl chloride composition comprising: (A) 100 parts by weight of PVC; (B) stabilizer system comprising (i) from about 0.005 part by weight to about 1.0 part by weight of at least one zinc soap, and (ii) from 0 to about 1.0 part by weight of at least one calcium soap; (C) co-stabilizer system comprising from about 0.2 part by weight to about 1.5 parts by weight of at least one co-stabilizer compound selected from the group consisting of compounds having the formula: OH--X--O--R and R--O--X--O--R wherein X is a straight chain, branched or cyclic radical having: (a) from 2 to about 20 oxygen atoms, wherein at least one of said oxygen atoms forms an ether linkage and the remainder forms bonds selected from the group consisting of ether, epoxy and hydroxy; (b) from about 4 to about 60 carbon atoms; wherein R is a straight chain radical having from about 5 to about 40 carbon atoms; (D) at least one lubricant; (E) at least one impact modifier; wherein said polyvinyl chloride composition is characterized by having the following properties: (I) high degree of clarity as defined by having a percent light transmission greater than that described by the following formula: % Light Transmission=100-460 (inch thickness) as measured according to ASTM D-1746; (II) percent haze measured according to ASTM D-1003-61 and having a value less than that described by the following formula: % Haze=184.6 (inch thickness); (III) blush less than 30% at 0.065 inch thickness after exposure for 48 hours at 50° C. in a 50/50 ethanol water solution; (IV) color stability time greater than 20 minutes to turn black when aged at 200° C., according to ASTM D-1925; (V) said PVC composition does not impart an objectionable taste nor odor to other materials in contact with said PVC composition; (VI) yellowness index less than about 13% at 0.065 inch thickness as measured according to ASTM D-1925 on an unpigmented compound.

Claim 19

a polyvinyl chloride composition comprising: (A) 100 parts by weight of PVC; (B) stabilizer system comprising (i) from about 0.005 part by weight to about 1.0 part by weight of at least one zinc soap, and (ii) from 0 to about 1.0 part by weight of at least one calcium soap; (C) co-stabilizer system comprising from about 0.2 part by weight to about 1.5 parts by weight of at least one co-stabilizer compound selected from the group consisting of compounds having the formula: OH--X--O--R and R--O--X--O--R wherein X is a straight chain, branched or cyclic radical having: (a) from 2 to about 20 oxygen atoms, wherein at least one of said oxygen atoms forms an ether linkage and the remainder forms bonds selected from the group consisting of ether, epoxy and hydroxy; (b) from about 4 to about 60 carbon atoms; wherein R is a straight chain radical having from about 5 to about 40 carbon atoms; (D) at least one lubricant; (E) at least one impact modifier; wherein said polyvinyl chloride composition is characterized by having the following properties: (I) high degree of clarity as defined by having a percent light transmission greater than that described by the following formula: % Light Transmission=100-460 (inch thickness) as measured according to ASTM D-1746; (II) percent haze measured according to ASTM D-1003-61 and having a value less than that described by the following formula: % Haze=184.6 (inch thickness); (III) blush less than 30% at 0.065 inch thickness after exposure for 48 hours at 50° C. in a 50/50 ethanol water solution; (IV) color stability time greater than 20 minutes to turn black when aged at 200° C., according to ASTM D-1925; (V) said PVC composition does not impart an objectionable taste nor odor to other materials in contact with said PVC composition; (VI) yellowness index less than about 13% at 0.065 inch thickness as measured according to ASTM D-1925 on an unpigmented compound.

Claim 20

A polyvinyl chloride composition of claim 17 wherein said co-stabilizer in (C) is selected from the group consisting of oligo-glycerol, oligo-propylene glycol and olig-ethylene glycol; wherein said oligo-glycerol has the formula: ##STR9## said glycerol may be straight chain, branched or cyclic; wherein n=2 to 20 and R is a straight chain radical having from about 5 to about 40 carbon atoms; said oligo-propylene glycol has the formula: ##STR10## wherein n and R are as defined above; said oligio-ethylene glycol has the formula: ##STR11## wherein n and R are as defined above.

Claim 21

A composition of claim 18 wherein said oligo-glycerol is an ester of oligo-glycerol and a fatty acid wherein the molar ratio of glycerol to fatty acid is greater than 1:1.

Claim 22

A composition of claim 19 wherein said molar ratio is greater than 2:1.

Claim 23

A composition of claim 20 wherein said ester of oligo-glycerol and a fatty acid is selected from the group consisting of triglycerol monosterate, hexaglycerol monostearate and hexaglycerol distearate.

Claim 24

A composition of claim 21 wherein the level of said ester is from about 0.4 part to about 1.5 parts by weight per 100 parts by weight of PVC.

Claim 25

A compostion of claim 22 wherein the polyvinyl chloride is a polyvinyl chloride homopolymer.

Claim 26

A composition of claim 23 wherein the levels of each of the zinc soap and calcium soap is from about 0.03 part by weight to about 0.3 part by weight per 100 parts by weight of PVC.

Claim 27

A composition of claim 24 wherein there is present at least two additional co-stabilizers selected from the group consisting of phosphite, polymeric phosphite, beta-diketone and epoxidized soybean oil.

Claim 28

A composition of claim 25 in the fused state.

Claim 29

A process for producing a clear polyvinyl chloride article comprising shaping a polyvinyl chloride composition having the following characteristics: (a) high degree of clarity as defined by having a percent light transmission greater than that described by the following formula: % Light Transmission=100-460 (inch thickness) as measured according to ASTM D-1746; (b) percent haze measured according to ASTM D-1003-61 and having a value less than that described by the following formula: % Haze=184.6 (inch thickness); (c) blush less than 30% at 0.065 inch thickness after exposure for 48 hours at 50°0 C. in a 50/50 ethanol water solution; (d) yellowness index less than about 13% at 0.065 inch thickness as measured according to ASTM D-1925 on an unpigmented compound. (e) color stability according to ASTM D-1925 of a time greater than 20 minutes to turn black when aged at 200° C.; (f) said compositions do not impart taste nor odor to materials in contact with said composition; said shaping is performed by molding, calendering, extruding, or pressing; wherein said polyvinyl chloride composition comprises: (A) 100 parts by weight of PVC; (B) stabilizer system comprising (i) from about 0.005 part by weight to about 1.0 part by weight of at least one zinc soap, and (ii) from 0 to about 1.0 part by weight of at least one calcium soap; (C) co-stabilizer system comprising from about 0.2 part by weight to about 1.5 parts by weight of at least one co-stabilizer compound selected from the group consisting of compounds having the formula: OH--X--O--R and R--O--X--O--R wherein X is a straight chain, branched or cyclic radical having: (I) from 2 to about 20 oxygen atoms, wherein at least one of said oxygen atoms forms an ether linkage and the remainder forms bonds selected from the group consisting of ether, epoxy and hydroxy; (II) from about 4 to about 60 carbon atoms; wherein R is a straight chain radical having from about 5 to about 40 carbon atoms; (D) at least one lubricant; (E) at least one impact modifier; extruding, or pressing.

Claim 30

A process for producing a clear polyvinyl chloride article comprising shaping a polyvinyl chloride composition having the following characteristics: (a) high degree of clarity as defined by having a percent light transmission greater than that described by the following formula: % Light Transmission=100-460 (inch thickness) as measured according to ASTM D-1746; (b) percent haze measured according to ASTM D-1003-61 and having a value less than that described by the following formula: % Haze=184.6 (inch thickness); (c) blush less than 30% at 0.065 inch thickness after exposure for 48 hours at 50°0 C. in a 50/50 ethanol water solution; (d) yellowness index less than about 13% at 0.065 inch thickness as measured according to ASTM D-1925 on an unpigmented compound. (e) color stability according to ASTM D-1925 of a time greater than 20 minutes to turn black when aged at 200° C.; (f) said compositions do not impart taste nor odor to materials in contact with said composition; said shaping is performed by molding, calendering, extruding, or pressing; wherein said polyvinyl chloride composition comprises: (A) 100 parts by weight of PVC; (B) stabilizer system comprising (i) from about 0.005 part by weight to about 1.0 part by weight of at least one zinc soap, and (ii) from 0 to about 1.0 part by weight of at least one calcium soap; (C) co-stabilizer system comprising from about 0.2 part by weight to about 1.5 parts by weight of at least one co-stabilizer compound selected from the group consisting of compounds having the formula: OH--X--O--R and R--O--X--O--R wherein X is a straight chain, branched or cyclic radical having: (I) from 2 to about 20 oxygen atoms, wherein at least one of said oxygen atoms forms an ether linkage and the remainder forms bonds selected from the group consisting of ether, epoxy and hydroxy; (II) from about 4 to about 60 carbon atoms; wherein R is a straight chain radical having from about 5 to about 40 carbon atoms; (D) at least one lubricant; (E) at least one impact modifier; extruding, or pressing.

Claim 31

A process of claim 27 wherein said process is conducted at a temperature greater than 180° C.