US4749665A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low temperature fired ceramics
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1986-10-16
•
Granted: 1988-06-07
•
Expires: 2006-10-16
Abstract
Abstract Partially crystallized ceramic articles is prepared by firing at low temperatures of 800° to 1100° C., a mixture consisting essentially of, (a) 40 to 50 wt. % of powdered, noncrystalline glass consisting essentially of 10 to 55 wt. % of at least one selected from the group consisting of CaO and MgO, 45 to 70 wt. % of SiO 2 , 0 to 30 wt. % of Al 2 O 3 , 0 to 30% of B 2 O 3 and up to 10% impurities, the powder size of said glass being at least 4.0 m 2 /g in terms of specific surface area measured by the BET Method; and (b) 60 to 50 wt. % of powdered Al 2 O 3 and the ceramic article is composed essentially of a noncrystallized glass phase, alumina and at least one of crystallized glass phase among anorthite, wollastonite, cordierite and mullite formed by partially crystallizing the glass (a). The ceramic articles exhibit a very high flexural strength well comparable with alumina substrate, together with greatly improved dielectric constant and thermal expansion and thus are especially useful in making multi-layer ceramic substrates for electronic applications.
Inventors
- 👤 Shinsuke Yano
- 👤 Susumu Nishigaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:07
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C10/0054; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
124 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of 800° to 1100° C., a mixture consisting essentially of, in weight percentages: (a) 40 to less than 50% of powdered, noncrystalline glass consisting essentially of 10 to 55% of at least one material selected from the group consisting of CaO and MgO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , 0 to 30% of B 2 O 3 and up to 10% impurities, the powder size of said glass being at least 4.0 m 2 /g in terms of specific surface area measured by the BET Method; and (b) 60 to more than 50% of powdered Al 2 O 3 .
Claim 2
Dependent Claim
124 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of 800° to 1100° C., a mixture consisting essentially of, in weight percentages: (a) 40 to less than 50% of powdered, noncrystalline glass consisting essentially of 10 to 55% of at least one material selected from the group consisting of CaO and MgO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , 0 to 30% of B 2 O 3 and up to 10% impurities, the powder size of said glass being at least 4.0 m 2 /g in terms of specific surface area measured by the BET Method; and (b) 60 to more than 50% of powdered Al 2 O 3 .
Claim 3
Dependent Claim
45 words
A paritally crystallized ceramic article as claimed in claim 1 which consists essentially of a noncrystallized glass phase, alumina and at least one of crystallized glass phase selected from the group consisting of anorthite, wollastonite, cordierite and mullite formed by partially crystallizing said glass (a).
Claim 4
Dependent Claim
69 words
A partially crystallized ceramic article as claimed in claim 1 in which said glass (a) was prepared by melting CaO, MgO, SiO 2 and Al 2 O 3 , or their corresponding carbonates or hydroxides, at a temperature of 1300° to 1450° C. to form molten glass, then pouring the molten glass into water to obtain glass frit and then milling the glass frit to obtain the glass (a).
Claim 5
Dependent Claim
55 words
A partially crystallized ceramic article as claimed in claim 1 in which said powdered, noncrystalline glass consists essentially of 21.1 to 27.3% of CaO, 0 to 0.6% of MgO, 50 to 59.1% of SiO 2 , 4.5 to 14.3% of Al 2 O 3 , and 8.2 to 9.1% of B 2 O 3 .
Claim 6
Dependent Claim
112 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of 800° to 1100° C., a mixture consisting essentially of, in weight percentages: (a) 40 to less than 50% of powdered, noncrystalline glass consisting essentially of 10 to 55% of MgO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , 0 to 30% of B 2 O 3 and up to 10% impurities, the powder size of said glass being at least 4.0 m 2 /g in terms of specific surface area measured by the BET Method; and (b) 60 to more than 50% of powdered Al 2 O 3 .
Claim 7
Dependent Claim
112 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of 800° to 1100° C., a mixture consisting essentially of, in weight percentages: (a) 40 to less than 50% of powdered, noncrystalline glass consisting essentially of 10 to 55% of MgO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , 0 to 30% of B 2 O 3 and up to 10% impurities, the powder size of said glass being at least 4.0 m 2 /g in terms of specific surface area measured by the BET Method; and (b) 60 to more than 50% of powdered Al 2 O 3 .
Claim 8
Dependent Claim
38 words
A partially crystallized ceramic article as claimed in claim 5 in which said powdered, noncrystalline glass consists essentially of 51.7% SiO 2 , 15% Al 2 O 3 , 16.7% MgO and 16.7% B 2 O 3 .
References Cited (Backward Citations)
DE1082016B
Cited
GB883287A
Cited
DE1220094B
Cited
US3380838A
Cited
GB1342823A
Cited
JPS50119814A
Cited
JPS54111517A
Cited
US4301324A
Cited
JPS5817695A
Cited
US4621066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-07 | 1991-12-07 | 1992-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-07 | 1995-12-07 | 1996-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-07 | 1999-12-07 | 2000-06-07 | $7700.00 | Window Closed / Lapsed |