US4749588A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing hydrogenated amorphous silicon thin film and a solar cell
Assignee: Individual
•
Filing: 1986-02-28
•
Granted: 1988-06-07
•
Expires: 2006-02-28
Abstract
Abstract The speed of forming a film of a hydrogenated amorphous silicon (a-Si:H) can be increased by controlling the amount of a supplied energy in relation to the film-forming speed. Application of this technique to the production of a solar cell enables a hydrogenated amorphous silicon solar cell (a-Si:H cell) having a high photoelectric conversion efficiency to be produced at high speeds. The aforesaid controlling procedure comprises adjusting the amount (KJ/g-Si2H6) of an energy to be supplied to a film-forming speed depends mainly upon the flow rate of the gas and is not substantially affected by the amount of the energy.
Inventors
- 👤 Nobuhiro Fukuda
- 👤 Yutaka Ohashi
- 👤 Kenji Miyaji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:01
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/10; H10F71/103; C; C23; C23C; C23C16/00; C23C16/22; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
122 words
A process for producing a thin film of hydrogenated amorphous silicon which comprises decomposing a film-forming gas composed of disilane by glow discharge while said gas is flowing, and thereby forming a thin film of hydrogenated amorphous silicon on a substrate, wherein the amount of energy for decomposition to be applied per unit weight of the gas is adjusted to such an amount that the speed of forming the thin film depends mainly upon the flow rate of the gas and is not substantially affected by the amount of the energy, said supplied energy being at least 6 KJ per gram of said gas and wherein the speed of forming the thin film is increased to prevent crystallization of the thin film.
Claim 2
Dependent Claim
122 words
A process for producing a thin film of hydrogenated amorphous silicon which comprises decomposing a film-forming gas composed of disilane by glow discharge while said gas is flowing, and thereby forming a thin film of hydrogenated amorphous silicon on a substrate, wherein the amount of energy for decomposition to be applied per unit weight of the gas is adjusted to such an amount that the speed of forming the thin film depends mainly upon the flow rate of the gas and is not substantially affected by the amount of the energy, said supplied energy being at least 6 KJ per gram of said gas and wherein the speed of forming the thin film is increased to prevent crystallization of the thin film.
Claim 3
Dependent Claim
38 words
The process of claim 1 wherein the amount of the energy is adjusted to at least 6 KJ per gram of said gas, and the speed of forming the thin film is adjusted to at least 6 Å/sec.
Claim 4
Dependent Claim
38 words
The process of claim 1 wherein the amount of the energy is adjusted to at least 10 KJ per gram of said gas, and the speed of forming the thin film is adjusted to at least 10 Å/sec.
Claim 5
Dependent Claim
38 words
The process of claim 1 wherein the amount of the energy is adjusted to 10 to 100 KJ per gram of said gas, and the speed of forming the thin film is adjusted to at least 15 Å/sec.
Claim 6
Dependent Claim
24 words
The process of any one of claims 1 to 4 wherein the thin film is formed at a temperature of 200° to 450° C.
Claim 7
Dependent Claim
24 words
The process of any one of claims 1 to 4 wherein the thin film is formed under a pressure of 1 to 10 torr.
Claim 8
Dependent Claim
21 words
The process of any one of claims 1 to 4 wherein the film-forming gas is diluted with helium, argon or hydrogen.
Claim 9
Dependent Claim
20 words
The process of claim 7 wherein the film-forming gas is diluted to a concentration of 5 to 20% by volume.
Claim 10
Dependent Claim
171 words
A process for producing a solar cell, which comprises decomposing a film-forming gas composed of disilane while it is flowing, and successively forming an amorphous silicon thin film layer of a first type electrical conductor, an essentially intrinisic amorphous silicon thin film layer, an amorphous silicon thin film layer of a second type electrical conductor and a second electrode in this order on a substrate having a first electrode, wherein at least the essentially intrinsic amorphous silicon thin film layer is composed of a thin film of hydrogenated amorphous silicon which is formed by adjusting the amount of energy for decomposition to be applied per unit weight of the gas to such an amount that the speed of forming the thin film depends mainly upon the flow rate of the gas and is not substantially affected by the amount of the energy, said supplied energy being at least 6 KJ per gram of said gas and increasing the speed of forming the thin film to prevent cyrstallization of the thin film.
Claim 11
Dependent Claim
171 words
A process for producing a solar cell, which comprises decomposing a film-forming gas composed of disilane while it is flowing, and successively forming an amorphous silicon thin film layer of a first type electrical conductor, an essentially intrinisic amorphous silicon thin film layer, an amorphous silicon thin film layer of a second type electrical conductor and a second electrode in this order on a substrate having a first electrode, wherein at least the essentially intrinsic amorphous silicon thin film layer is composed of a thin film of hydrogenated amorphous silicon which is formed by adjusting the amount of energy for decomposition to be applied per unit weight of the gas to such an amount that the speed of forming the thin film depends mainly upon the flow rate of the gas and is not substantially affected by the amount of the energy, said supplied energy being at least 6 KJ per gram of said gas and increasing the speed of forming the thin film to prevent cyrstallization of the thin film.
Claim 12
Dependent Claim
38 words
The process of claim 9 wherein the amount of the energy is adjusted to at least 6 KJ per gram of said gas, and the speed of forming the thin film is adjusted to at least 6 Å/sec.
Claim 13
Dependent Claim
38 words
The process of claim 9 wherein the amount of the energy is adjusted to at least 10 KJ per gram of said gas, and the speed of forming the thin film is adjsuted to at least 10 Å/sec.
Claim 14
Dependent Claim
37 words
The process of claim 9 wherein the amount of the energy is adjusted to 10 to 100 KJ per gram of said gas, and the speed of forming thin film is adjusted to at least 15 Å/sec.
Claim 15
Dependent Claim
24 words
The process of any one of claims 9 to 12 wherein the thin film is formed at a temperature of 200° to 450° C.
Claim 16
Dependent Claim
24 words
The process of any one of claims 9 to 12 wherein the thin film is formed under a pressure of 1 to 10 torr.
Claim 17
Dependent Claim
21 words
The process of any one of claims 9 to 12 wherein the film-forming gas is diluted with helium, argon or hydrogen.
Claim 18
Dependent Claim
20 words
The process of claim 15 wherein the film-forming gas is diluted to a concentration of 5 to 20% by volume.
Claim 19
Dependent Claim
99 words
A process for producing a thin film of hydrogenated amorphous silicon comprising: decomposing a film-forming, flowing gas of disilane by glow discharge whereby an amount of energy for said decomposing is adjusted to at least 6 KJ per gram of said gas; forming said thin film of hydrogenated amorphous silicon on a substrate, said film being formed at a speed adjusted to at least 6 Å/sec between a temperature of 200° to 450° C. and a pressure of 1 to 10 torr, said speed of forming said thin film being selectively increased to prevent crystallization of said thin film.
Claim 20
Dependent Claim
99 words
A process for producing a thin film of hydrogenated amorphous silicon comprising: decomposing a film-forming, flowing gas of disilane by glow discharge whereby an amount of energy for said decomposing is adjusted to at least 6 KJ per gram of said gas; forming said thin film of hydrogenated amorphous silicon on a substrate, said film being formed at a speed adjusted to at least 6 Å/sec between a temperature of 200° to 450° C. and a pressure of 1 to 10 torr, said speed of forming said thin film being selectively increased to prevent crystallization of said thin film.
Claim 21
Dependent Claim
38 words
The process of claim 17 wherein the amount of the energy is adjusted to at least 10 KJ per gram of said gas, and the speed of forming said thin film is adjusted to at least 10 Å/sec.
Claim 22
Dependent Claim
38 words
The process of claim 18 wherein the amount of the enegy is adjusted to 10 to 100 KJ per gram of said gas, and the speed of forming the thin film is adjusted to at least 15 Å/sec.
Claim 23
Dependent Claim
16 words
The process of claim 19 further comprising: deleting said film-forming gas with helium, argon, or hydrogen.
Claim 24
Dependent Claim
22 words
The process of claim 20 wherein said diluting of said film-forming gas is to a concentration of 5 to 20% by volume.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-07 | 1991-12-07 | 1992-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-07 | 1995-12-07 | 1996-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-07 | 1999-12-07 | 2000-06-07 | $7700.00 | Window Closed / Lapsed |