Aluminum nitride sintered body and process for producing the same
Assignee: Toshiba Corp
•
Filing: 1985-07-31
•
Granted: 1988-05-24
•
Expires: 2005-07-31
Abstract
Abstract Disclosed are an aluminum nitride sintered body comprising aluminum nitride, rare earth element-aluminum compounds and alkaline earth metal-aluminum compounds, and a process for producing an aluminum nitride sintered body, which comprises adding to aluminum nitride powder: (a) powder of at least one compound selected from the group consisting of rare earth element oxides, rare earth element fluorides and compounds capable of being converted into these oxides or fluorides by calcination, and (b) powder of at least one compound selected from the group consisting of alkaline earth metal oxides, alkali earth metal fluorides and compounds capable of being converted into these oxides or fluorides by calcination, in a total amount of 0.01 to 20 wt % as calculated on the weight of the oxides or the fluorides, and then molding and sintering the resultant mixture.
Inventors
- 👤 Mituo Kasori
- 👤 Kazuo Shinozaki
- 👤 Kazuo Anzai
- 👤 Akihiko Tsuge
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:26
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/581
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
86 words
An aluminum nitride sintered body comprising aluminum nitride, at least one rare earth element-aluminum compound and at least one alkaline earth metal-aluminum compound selected from the group consisting of a calcium-aluminum compound, a strontium-aluminum compound and a barium-aluminum compound, wherein (i) the weight ratio of said alkaline earth metal-aluminum compound to said rare earth element-aluminum compound ranges from about 1:9 to 9:1 and (ii) the total amount of said rare earth element-aluminum compound and said alkaline earth metal-aluminum compound ranges between 0.01 and 20% by weight.
Claim 2
Dependent Claim
86 words
An aluminum nitride sintered body comprising aluminum nitride, at least one rare earth element-aluminum compound and at least one alkaline earth metal-aluminum compound selected from the group consisting of a calcium-aluminum compound, a strontium-aluminum compound and a barium-aluminum compound, wherein (i) the weight ratio of said alkaline earth metal-aluminum compound to said rare earth element-aluminum compound ranges from about 1:9 to 9:1 and (ii) the total amount of said rare earth element-aluminum compound and said alkaline earth metal-aluminum compound ranges between 0.01 and 20% by weight.
Claim 3
Dependent Claim
21 words
The aluminum nitride sintered body according to claim 1, wherein the content of aluminum nitride is 80 to 99.99 wt %.
Claim 4
Dependent Claim
28 words
The aluminum nitride sintered body according to claim 1, wherein the ratio of said alkaline earth metal-aluminum compound to said rare earth-aluminum compound ranges from 1:3 to 3:1.
Claim 5
Dependent Claim
29 words
The aluminum nitride sintered body according to claim 1, wherein said rare earth element compound is a yttrium-aluminum compound and said alkaline earth metal-aluminum compound is a calcium-aluminum compound.
Claim 6
Dependent Claim
50 words
The aluminum nitride sintered body according to claim 1, wherein said sintered body contains a smaller amount of AlON or 27R polytype AlN than another sintered body identically prepared except for using an alkaline earth metal oxide alone or a rare earth element oxide alone in the latter sintered body.
Claim 7
Dependent Claim
22 words
The aluminum nitride sintered body according to claim 5, wherein said sintered body is substantially free of AlON and 27R polytype AlN.
Claim 8
Dependent Claim
221 words
A process for producing an aluminum nitride sintered body, which comprises the steps of (1) adding to aluminum nitride powder containing 0.001 to 7 wt % of oxygen: (a) powder comprising at least one compound selected from the group consisting of a rare earth element oxide, a rare earth element fluoride and a compound capable of being converted into a rare earth element oxide or fluoride by calcination, and (b) powder comprising at least one compound selected from the group consisting of (i) calcium oxide, strontium oxide, barium oxide, calcium fluoride, strontium fluoride and barium fluoride and (ii) a compound capable of being converted to an oxide or fluoride of (i) by calcination, such that the total amount of said powder (a) and said powder (b) is between 0.01 and 20% by weight, as calculated from the weight of the oxides or the fluorides based on the total amount of the AlN powder, powder (a) and powder (b); and that the weight ratio of said powder (b) to said powder (a) ranges from about 1:9 to 9:1, and then (2) molding and sintering the resultant mixture by an atmosphere sintering method at a sintering temperature of 1700° C. or lower, wherein said aluminum nitride powder and said powders (a) and (b) have average particle sizes, respectively, of 5 μm or less.
Claim 9
Dependent Claim
221 words
A process for producing an aluminum nitride sintered body, which comprises the steps of (1) adding to aluminum nitride powder containing 0.001 to 7 wt % of oxygen: (a) powder comprising at least one compound selected from the group consisting of a rare earth element oxide, a rare earth element fluoride and a compound capable of being converted into a rare earth element oxide or fluoride by calcination, and (b) powder comprising at least one compound selected from the group consisting of (i) calcium oxide, strontium oxide, barium oxide, calcium fluoride, strontium fluoride and barium fluoride and (ii) a compound capable of being converted to an oxide or fluoride of (i) by calcination, such that the total amount of said powder (a) and said powder (b) is between 0.01 and 20% by weight, as calculated from the weight of the oxides or the fluorides based on the total amount of the AlN powder, powder (a) and powder (b); and that the weight ratio of said powder (b) to said powder (a) ranges from about 1:9 to 9:1, and then (2) molding and sintering the resultant mixture by an atmosphere sintering method at a sintering temperature of 1700° C. or lower, wherein said aluminum nitride powder and said powders (a) and (b) have average particle sizes, respectively, of 5 μm or less.
Claim 10
Dependent Claim
32 words
The process according to claim 7, wherein the rare earth element in the rare earth element oxides or fluorides is Y, La, Ce, Sm, Dy, Nd, Gd, Pr, Ho, Er or Yb.
Claim 11
Dependent Claim
24 words
The process according to claim 8, wherein the rare earth element in the rare earth element oxides or fluorides is Y, La or Ce.
Claim 12
Dependent Claim
34 words
The process according to claim 7, wherein the rare earth element oxides or fluorides and the alkaline earth metal oxides or fluorides are added in a total amount of 0.01 to 17 wt %.
Claim 13
Dependent Claim
22 words
The process according to claim 7, wherein the ratio of said powder (b) to said powder (a) ranges from 1:3 to 3:1.
Claim 14
Dependent Claim
20 words
The process according to claim 7, wherein said powder (a) comprises yttrium oxide and said powder (b) comprises calcium oxide.
Claim 15
Dependent Claim
43 words
The process according to claim 7, wherein said powder (a) consists essentially of at least one compound from said group of rare earth element compounds, and said powder (b) consists essentially of at least one compound from said group of oxides and fluorides.
References Cited (Backward Citations)
US3238018A
Cited
GB978734A
Cited
US3531245A
Cited
US3930875A
Cited
US4540673A
Cited
US4435513A
Cited
JPS5950077A
Cited
DE3247985A1
Cited
US4591537A
Cited
DE3313836A1
Cited
US4547471A
Cited
EP0147101A2
Cited
EP0166073A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |