Sealed cavity semiconductor pressure transducers and method of producing the same
Assignee: Wisconsin Alumni Research Foundation
•
Filing: 1986-04-24
•
Granted: 1988-05-17
•
Expires: 2006-04-24
Abstract
Abstract Sealed cavity structures suitable for use as pressure transducers are formed on a single surface of a semiconductor substrate (20) by, for example, deposit of a polycrystalline silicon layer (32) from silane gas over a relatively large silicon dioxide post (22) and smaller silicon dioxide ridges (27) leading outwardly from the post. The polysilicon layer is masked and etched to expose the outer edges of the ridges and the entire structure is then immersed in an etchant which etches the silicon dioxide forming the ridges and the post but not the substrate (20) or the deposited polysilicon layer (32). A cavity structure results in which channels (35) are left in place of the ridges and extend from communication with the atmosphere to the cavity (36) left in place of the post. The cavity (36) may be sealed off from the external atmosphere by a second vapor deposition of polysilicon or silicon nitride, which fills up and seals off the channels (35), or by exposing the substrate and the structure thereon to an oxidizing ambient which results in growth of silicon dioxide in the channels sufficient to seal off the channels. Deflection of the membrane spanning the cavity occurring as a result of pressure changes, may be detected, for example, by piezoresistive devices formed on the membrane.
Inventors
- 👤 Henry Guckel
- 👤 David W. Burns
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:27
CPC Classifications
G; G01; G01L; G01L9/00; G01L9/0041; G01L9/0042; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49103
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
280 words
A method of producing a deformable membrane of a transducer on a substrate, comprising the steps of: (a) masking a suface of the substrate to expose a selected area where a cavity of the transducer is to be located; (b) forming an etchable substance in the exposed area of the substrate to define an etchable post; (c) removing the mask from the substrate to leave the etchable post isolated on the substrate; (d) masking the substrate in areas of the surface of the substrate adjacent to the post in a pattern in which at least one continuous exposed area extends from the post to a position on the substrate remote from the post; (e) forming an etchable substance in the exposed areas of the substrate to define at least one ridge on the substrate; (f) removing the mask from the substrate to leave the post and the ridge isolated thereon; (g) depositing a solid material from a gas phase in a layer over the post and ridge and adjacent areas of the substrate; (h) removing peripheral portions of the deposited layer to expose an outer edge of the ridge at a position remote from the post; (i) applying an etchant to the substrate and the deposited layer thereon which etches the material of the post and ridge but does not substantially etch the material of the substrate or the deposited layer, such that the etchant etches out the ridge to form a channel in the deposited layer and then etches out the post to leave a cavity which is spanned by the covering deposited layer defining said deformable membrane and with the cavity communicating to ambient atmosphere through the channel.
Claim 2
Independent Claim
280 words
A method of producing a deformable membrane of a transducer on a substrate, comprising the steps of: (a) masking a suface of the substrate to expose a selected area where a cavity of the transducer is to be located; (b) forming an etchable substance in the exposed area of the substrate to define an etchable post; (c) removing the mask from the substrate to leave the etchable post isolated on the substrate; (d) masking the substrate in areas of the surface of the substrate adjacent to the post in a pattern in which at least one continuous exposed area extends from the post to a position on the substrate remote from the post; (e) forming an etchable substance in the exposed areas of the substrate to define at least one ridge on the substrate; (f) removing the mask from the substrate to leave the post and the ridge isolated thereon; (g) depositing a solid material from a gas phase in a layer over the post and ridge and adjacent areas of the substrate; (h) removing peripheral portions of the deposited layer to expose an outer edge of the ridge at a position remote from the post; (i) applying an etchant to the substrate and the deposited layer thereon which etches the material of the post and ridge but does not substantially etch the material of the substrate or the deposited layer, such that the etchant etches out the ridge to form a channel in the deposited layer and then etches out the post to leave a cavity which is spanned by the covering deposited layer defining said deformable membrane and with the cavity communicating to ambient atmosphere through the channel.
Claim 3
Dependent Claim
51 words
The method of claim 1 including, after the step of applying the etchant, the further steps of depositing a solid material from a gas phase in the channel for a period of time sufficient to seal the channel so that atmospheric gases cannot enter or exit the cavity through the channel.
Claim 4
Dependent Claim
85 words
The method of claim 1 wherein the material of the deposited layer forms an oxide with gaseous oxygen which grows from the material, and including, after the step of applying an etchant, the further steps of exposing the substrate and the deposited layer thereon to an oxidizing gas including oxygen for a period of time sufficient to form a growing oxide of the deposited layer in the channel which seals the channel so that atmospheric gases cannot enter or exit the cavity through the channel.
Claim 5
Dependent Claim
85 words
The method of claim 1 wherein the substrate is formed of crystalline silicon, and wherein the steps of forming etchable material on the substrate to define the post and the ridge are performed by growing silicon dioxide on the substrate by exposing the unmasked areas of the substrate to an oxidizing gas under temperature conditions such that the silicon of the substrate combines with oxygen in the ambient gas to grow silicon dioxide layers on the substrate to define the base post and the ridge.
Claim 6
Dependent Claim
32 words
The method of claim 1 wherein the step of forming the ridge on the substrate surface is carried out until the height of the ridge is no more than approximately 1,500 angstroms.
Claim 7
Dependent Claim
49 words
The method of claim 1 wherein the step of depositing a layer of solid material is performed by depositing polycrystalline silicon from silane gas at temperature and pressure conditions such that a solid layer of polycrystalline silicon is formed over the ridge, the post, and the adjacent substrate surface.
Claim 8
Dependent Claim
30 words
The method of claim 4 wherein the layer of deposited material is formed of polycrystalline silicon and wherein the etchant in the step of applying an etchant contains hydrofluoric acid.
Claim 9
Dependent Claim
90 words
The method of claim 4 wherein the deposited layer is formed of polysilicon and including, after the step of applying etchant to the structure, the step of depositing polysilicon from a gaseous silicon carrying phase onto the walls of the channels for a period of time sufficient to seal the channels so that atmospheric gases cannot enter or exit the cavity and for a time sufficient for substantially all of the silicon from the gaseous phase trapped in the cavity to be deposited on the interior walls of the cavity.
Claim 10
Dependent Claim
60 words
The method of claim 1 wherein the layer deposited from a gas phase is formed to a thickness of between 1,000 angstroms and 15 microns, whereby the portion of the layer deposited over the post, which remains after the post is etched out, defines a solid membrane which may be deformed in response to changes in pressure across the membrane.
Claim 11
Dependent Claim
28 words
The method of claim 1 wherein the substrate is selected form the group consisting of crystalline silicon, germanium, sapphire, silicon on sapphire, spinel, silicon dioxide, and ceramic compositions.
Claim 12
Dependent Claim
50 words
The method of claim 1 wherein the post is formed to a height in the range of 1,000 angstroms to 5 microns and wherein the ridge is formed to a height not more than one tenth the height of the post and in the range of 200 to 1,000 angstroms.
Claim 13
Dependent Claim
50 words
The method of claim 1 wherein a plurality of raised ridges are formed on the substrate, and wherein the ridges include inner ridges extending from the post to a laterally extending ridge and outer ridges extending outwardly from the laterally extending ridge which do not align with the inner ridges.
Claim 14
Independent Claim
154 words
A method of forming on a substrate a deformable membrane of a transducer over a cavity, comprising the steps of: (a) forming a post of an etchable material to a selected depth and shape on a substrate; (b) forming a ridge of etchable material on the substrate extending from the post outwardly to a position remote from the post; (c) depositing a solid material in a cohesive layer from a gaseous phase of the material over the post, the ridge and the adjacent surface of the substrate; and (d) applying an etchant to the surface of the substrate to etch out the etchable material in the ridge to leave a channel under the deposited material layer and to etch out the post to leave the cavity covered by the deposited layer with a portion of the layer over the cavity defining said deformable membrane with the cavity communicating with ambient atmosphere through the channel.
Claim 15
Independent Claim
154 words
A method of forming on a substrate a deformable membrane of a transducer over a cavity, comprising the steps of: (a) forming a post of an etchable material to a selected depth and shape on a substrate; (b) forming a ridge of etchable material on the substrate extending from the post outwardly to a position remote from the post; (c) depositing a solid material in a cohesive layer from a gaseous phase of the material over the post, the ridge and the adjacent surface of the substrate; and (d) applying an etchant to the surface of the substrate to etch out the etchable material in the ridge to leave a channel under the deposited material layer and to etch out the post to leave the cavity covered by the deposited layer with a portion of the layer over the cavity defining said deformable membrane with the cavity communicating with ambient atmosphere through the channel.
Claim 16
Dependent Claim
25 words
The method of claim 13 wherein the solid material deposited in a layer is selected from the group consisting of polycrystalline silicon and silicon nitride.
Claim 17
Dependent Claim
51 words
The method of claim 13 including, after the step of applying the etchant, the further steps of depositing a solid material from a gas phase in the channel for a period of time sufficient to seal the channel so that atmospheric gases cannot enter or exit the cavity through the channel.
Claim 18
Dependent Claim
25 words
The method of claim 15 wherein the solid material deposited in the channel is selected from the group consisting of polycrystalline silicon and silicon nitride.
Claim 19
Dependent Claim
85 words
The method of claim 13 wherein the material of the deposited layer forms an oxide with gaseous oxygen which grows from the material, and including, after the step of applying an etchant, the further steps of exposing the substrate and the deposited layer thereon to an oxidizing gas including oxygen for a period of time sufficient to form a growing oxide of the deposited layer in the channel which seals the channel so that atmospheric gases cannot enter or exit the cavity through the channel.
Claim 20
Dependent Claim
76 words
The method of claim 13 wherein the substrate is formed of crystalline silicon, and wherein the steps of forming etchable material on the substrate to define the post and the ridge are performed by growing silicon dioxide on the substrate in a first layer to define the post, growing silicon dioxide in a second, thinner layer around the post, and masking and etching the second layer to leave ridges of silicon dioxide extending to the post.
Claim 21
Dependent Claim
33 words
The method of claim 13 wherein the step of forming the ridge on the substrate surface is carried out such that the height of the ridge is no more than approximately 1,500 angstroms.
Claim 22
Dependent Claim
49 words
The method of claim 13 wherein the step of depositing a layer of solid material is performed by depositing polycrystalline silicon from silane gas at temperature and pressure conditions such that a solid layer of polycrystalline silicon is formed over the ridge, the post, and the adjacent substrate surface.
Claim 23
Dependent Claim
30 words
The method of claim 18 wherein the layer of deposited material is formed of polycrystalline silicon and wherein the etchant in the step of applying an etchant contains hydrofluoric acid.
Claim 24
Dependent Claim
87 words
The method of claim 18 wherein the deposited layer is formed of polysilicon and including, after the step of applying etchant, the step of depositing polysilicon from a gaseous silicon carrying phase onto the walls of the channels for a period of time sufficient to seal the channels so that atmospheric gases cannot enter or exit the cavity and for a time sufficient for substantially all of the silicon from the gaseous phase trapped in the cavity to be deposited on the interior walls of the cavity.
Claim 25
Dependent Claim
53 words
The method of claim 13 wherein the deposited layer is formed to a thickness of between 1,000 angstroms and 15 microns, wherein the layer deposited over the post which remains after the post is etched out defines a solid membrane which may be deformed in response to changes in pressure across the membrane.
Claim 26
Dependent Claim
28 words
The method of claim 13 wherein the substrate is selected from the group consisting of crystalline silicon, germanium, sapphire, silicon on sapphire, spinel, silicon dioxide, and ceramic compositions.
Claim 27
Dependent Claim
50 words
The method of claim 13 wherein the post is formed to a height in the range of 1,000 angstroms to 5 microns and wherein the ridge is formed to a height not more than one tenth the height of the post and in the range of 200 to 1,000 angstroms.
Claim 28
Dependent Claim
50 words
The method of claim 13 wherein a plurality of raised ridges are formed on the substrate, and wherein the ridges include inner ridges extending from the post to a laterally extending ridge and outer ridges extending outwardly from the laterally extending ridge which do not align with the inner ridges.
References Cited (Backward Citations)
SU306960A1
Cited
US3489995A
Cited
US3681134A
Cited
US3634727A
Cited
US3886584A
Cited
US3748571A
Cited
US3853650A
Cited
US3900597A
Cited
US4064549A
Cited
US4203128A
Cited
US4168518A
Cited
US4208782A
Cited
US4262399A
Cited
US4240196A
Cited
US4234361A
Cited
US4386453A
Cited
US4502917A
Cited
US4371890A
Cited
US4356211A
Cited
US4471525A
Cited
US4415948A
Cited
US4384899A
Cited
US4428796A
Cited
US4528855A
Cited
US4592238A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-17 | 1991-11-16 | 1992-05-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-17 | 1995-11-16 | 1996-05-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-17 | 1999-11-16 | 2000-05-17 | $7700.00 | Window Closed / Lapsed |