Polycrystalline sintered bodies on a base of silicon nitride with high fracture toughness and hardness
Assignee: ELEKTROSCHEMELZWERK KEMPTEN MUNICH WEST GmbH
•
Filing: 1987-02-26
•
Granted: 1988-05-10
•
Expires: 2007-02-26
Abstract
Abstract Polycrystalline sintered bodies are provided consisting of at least 66% by weight of a crystalline Si 3 N 4 phase, of which at least 90% by weight is in the beta-modification, and of up to 34% by weight of secondary intergranular grain boundary phases of oxide, carbide and/or nitride. At least 25% by weight of the secondary grain boundary phases consists of a quasi-ternary crystalline compound in the E 1 --E 2 --E 3 triangle of the Ga 2 O 3 --La 2 O 3 -Al 2 O 3 ternary system called "Gala", the "Gala" compound being prepared from gallium oxide, lanthanum oxide and aluminum oxide prior to producing the sintered bodies. The polycrystalline sintered bodies are produced by sintering with and without application of pressure from silicon nitride powders having a portion of impurities not exceeding 4.0% by weight, sintering additives of oxides and optionally other refractory admixtures of carbides and/or nitrides. Powders of a quasi-ternary crystalline compound (Gala compound) are employed as at least one sintering additive prepared, prior to mixing with the remaining components and to sintering, from gallium oxide, lanthanum oxide and aluminum oxide by heating to temperatures from 1500° C. to 1850° C. When using at least 70% by weight of silicon nitride powder, there can be used up to 30% by weight of a crystalline "Gala" compound alone or mixed with other admixtures of oxides, carbides or nitrides, but altogether at least 1% by weight of a crystalline "Gala" compound must be present. The sintered bodies are especially tough and very hard and can be used for the machining of iron materials at high cutting speeds.
Inventors
- 👤 Detlef Steinmann
- 👤 Alfred Lipp
- 👤 Hubert Thaler
- 👤 Dietrich Lange
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:14
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/5935
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
212 words
Polycrystalline sintered bodies of great fracture toughness and hardness consisting essentially of at least 66% by weight of a crystalline silicon nitride phase, of which at least 90% by weight is present in the beta-modification, and up to 34% by weight of secondary, intergranular grain boundary phases based on oxides, carbides and/or nitrides, of which at least one is crystalline, and wherein at least 25% by weight of the intergranular, secondary grain boundary phases consists essentially of a quasi-ternary crystalline compound of Ga 2 O 3 --La 2 O 3 --Al 2 O 3 , the quantitative portions of which in % by mole in the ternary system Ga 2 O 3 --La 2 O 3 --Al 2 O 3 are determined by the triangular surface with the corners E 1 =5%Ga 2 O 3 --5%La 2 O 3 --90%Al 2 O 3 E 2 =90%Ga 2 O 3 --5%La 2 O 3 --5%Al 2 O 3 E 2 =5%Ga 2 O 3 --90%La 2 O 3 --5%Al 2 O 3 of the FIGURE, and the quasi-ternary crystalline compound is prepared from gallium oxide, lanthanum oxide and aluminum oxide prior to producing the polycrystalline sintered bodies and wherein at least 1% by weight of the sintered body is the quasi-ternary crystalline compound.
Claim 2
Dependent Claim
212 words
Polycrystalline sintered bodies of great fracture toughness and hardness consisting essentially of at least 66% by weight of a crystalline silicon nitride phase, of which at least 90% by weight is present in the beta-modification, and up to 34% by weight of secondary, intergranular grain boundary phases based on oxides, carbides and/or nitrides, of which at least one is crystalline, and wherein at least 25% by weight of the intergranular, secondary grain boundary phases consists essentially of a quasi-ternary crystalline compound of Ga 2 O 3 --La 2 O 3 --Al 2 O 3 , the quantitative portions of which in % by mole in the ternary system Ga 2 O 3 --La 2 O 3 --Al 2 O 3 are determined by the triangular surface with the corners E 1 =5%Ga 2 O 3 --5%La 2 O 3 --90%Al 2 O 3 E 2 =90%Ga 2 O 3 --5%La 2 O 3 --5%Al 2 O 3 E 2 =5%Ga 2 O 3 --90%La 2 O 3 --5%Al 2 O 3 of the FIGURE, and the quasi-ternary crystalline compound is prepared from gallium oxide, lanthanum oxide and aluminum oxide prior to producing the polycrystalline sintered bodies and wherein at least 1% by weight of the sintered body is the quasi-ternary crystalline compound.
Claim 3
Dependent Claim
196 words
A process for the preparation of a polycrystalline sintered body according to claim 1 which comprises sintering a powder mixture of silicon nitride, oxide sintering additives and optionally carbide and/or nitride refractory admixtures, with or without application of pressure, at a temperature in the range of from 1700° to 2100° C., wherein a powder of quasi-ternary crystalline compounds of Ga 2 O 3 --La 2 O 3 --Al 2 O 3 , are present in the mixture as at least one sintering additive, the composition of said quasi-ternary crystalline compounds in % by mole in the ternary system Ga 2 O 3 --La 2 O 3 --Al 2 o 3 are determined by the triangular surface with the corners E 1 =5%Ga 2 O 3 --5%La 2 O 3 --90%Al 2 O 3 E 2 =90%Ga 2 O 3 --5%La 2 O 3 --5%Al 2 O 3 E 3 =5%Ga 2 O 3 --90%La 2 O 3 --5%Al 2 O 3 prior to forming the mixture to be sintered, the quasi-ternary compounds are prepared by heating to temperatures from 1500°-1850° C. a mixture of gallium oxide, lanthanum oxide and aluminum oxide in the above defined amounts.
Claim 4
Dependent Claim
123 words
A process for the preparation of a polycrystalline sintered body according to claim 2, wherein the powder mixture is a homogeneous mixture having an average particle size of less than 2 μm said mixture consisting essentially of at least 70% by weight silicon nitride, at least 80% by weight of the silicon nitride being in the alpha-modification, and wherein the impurities in the silicon nitride in the form of oxides and free carbon does not exceed 4.0% by weight, and up to 30% by weight of the quasi-ternary crystalline compounds in the E 1 --E 2 --E 3 triangle of the Ga 2 O 3 --La 2 O 3 --Al 2 O 3 system alone or mixed with oxides and/or carbides and/or nitrides.
Claim 5
Dependent Claim
51 words
A process according to claim 3, wherein the quasi-ternary crystalline compounds are admixed with at least one oxide selected from the group consisting of crystalline silicates of natural origin, metal oxides of metal atoms from groups 2a and 3b of the Periodic System, including the lanthanides and aluminum and silicon-aluminum oxynitride.
Claim 6
Dependent Claim
59 words
A process according to claim 3, wherein the quasi-ternary crystalline compounds are admixed with at least one carbide selected from the group consisting of metal carbides of metal atoms from groups 4b, 5b and 6b of the Periodic System, boron, silicon and admixtures with at least one nitride selected from the group consisting of titanium nitride and titanium carbonitride.
Claim 7
Dependent Claim
64 words
A process according to claim 2 wherein the composition of the quasi-ternary crystalline compound is determined by the triangular surface corners E 13 =5%Ga 2 O 3 --50%La 2 O 3 --45%Al 2 O 3 E 15 =45%Ga 2 O 3 --50%La 2 O 3 --5%Al 2 O 3 E 21 =40%Ga 2 O 3 --20%La 2 O 3 --40%Al 2 O 3 .
Claim 8
Dependent Claim
64 words
A process according to claim 3 wherein the composition of the quasi-ternary crystalline compound is determined by the triangular surface corners E 13 =5%Ga 2 O 3 --50%La 2 O 3 --45%Al 2 O 3 E 15 =45%Ga 2 O 3 --50%La 2 O 3 --5%Al 2 O 3 E 21 =40%Ga 2 O 3 --20%La 2 O 3 --40%Al 2 O 3 .
Claim 9
Dependent Claim
64 words
A process according to claim 4 wherein the composition of the quasi-ternary crystalline compound is determined by the triangular surface corners E 13 =5%Ga 2 O 3 --50%La 2 O 3 --45%Al 2 O 3 E 15 =45%Ga 2 O 3 --50%La 2 O 3 --5%Al 2 O 3 E 21 =40%Ga 2 O 3 --20%La 2 O 3 --40%Al 2 O 3 .
Claim 10
Dependent Claim
64 words
A process according to claim 5 wherein the composition of the quasi-ternary crystalline compound is determined by the triangular surface corners E 13 =5%Ga 2 O 3 --50%La 2 O 3 --45%Al 2 O 3 E 15 =45%Ga 2 O 3 --50%La 2 O 3 --5%Al 2 O 3 E 21 =40%Ga 2 O 3 --20%La 2 O 3 --40%Al 2 O 3 .
Claim 11
Dependent Claim
65 words
A sintered body of claim 1 wherein the quasi-ternary crystalline body has a composition determined by the triangular surface with the corners E 13 =5%Ga 2 O 3 --50%La 2 O 3 --45%Al 2 O 3 E 15 =45%Ga 2 O 3 --50%La 2 O 3 --5%Al 2 O 3 E 21 =40%Ga 2 O 3 --20%La 2 O 3 --40%Al 2 O 3 .
References Cited (Backward Citations)
US4218257A
Cited
US4127416A
Cited
US4127416B1
Cited
US4401617A
Cited
US4280973A
Cited
US4227842A
Cited
US4264548A
Cited
US4388085A
Cited
US4628039A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |