Abrasion resistant articles based on silicon nitride

Claim 2

A densified composite ceramic cutting tool which retains high creep resistance, fracture toughness, and resistance to oxidation at temperatures above 1200° C., said composite consisting essentially of from about 20 to about 60 volume percent of particles of a hard refractory material having an average size of less than about 5 microns selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, and tantalum uniformly distributed in a two phase matrix consisting essentially of a first phase of crystalline silicon nitride and a second refractory intergranular phase consisting essentially of silicon nitride, magnesium oxide and silicon dioxide, said magnesium oxide and silicon dioxide comprising from about 1 to about 10 weight percent of said two phase matrix, wherein said second phase contains less than 5 weight percent silicon dioxide, less than 3 weight percent additional additives including cation impurities, the hardness of said composite being greater than 93 on the Rockwell A scale and greater than the combined individual hardness of the fractional weight of silicon nitride times the hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, the density of said composite being greater than 97.5 percent of theoretical density and approaching 100 percent of theoretical density.

Claim 3

A densified composite cutting tool according to claim 1 wherein said hard refractory material comprises titanium carbide.

Claim 4

A densified composite abrasion resistant ceramic article which retains high creep resistance, fracture toughness, and resistance to oxidation at temperatures above 1200° C., said composite consisting essentially of from about 20 to about 60 volume percent of particles of a hard refractory material having an average size less than about 20 microns selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, and tantalum uniformly distributed in a two phase matrix consisting essentially of a first phase of crystalline silicon nitride and a second refractory intergranular phase consisting essentially of silicon nitride, magnesium oxide and silicon dioxide, said magnesium oxide and silicon dioxide comprising from about 1 to about 10 weight percent of said two phase matrix, wherein said second phase contains less than 5 weight percent silicon dioxide, less than 3 weight percent additional additives including cation impurities, the hardness of said composite being greater than 93 on the Rockwell A scale and greater than the combined individual hardness of the fractional weight of silicon nitride times the hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, the density of said composite being greater than 97.5 percent of theoretical density and approaching 100 percent of theoretical density.

Claim 5

A densified composite abrasion resistant ceramic article which retains high creep resistance, fracture toughness, and resistance to oxidation at temperatures above 1200° C., said composite consisting essentially of from about 20 to about 60 volume percent of particles of a hard refractory material having an average size less than about 20 microns selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, and tantalum uniformly distributed in a two phase matrix consisting essentially of a first phase of crystalline silicon nitride and a second refractory intergranular phase consisting essentially of silicon nitride, magnesium oxide and silicon dioxide, said magnesium oxide and silicon dioxide comprising from about 1 to about 10 weight percent of said two phase matrix, wherein said second phase contains less than 5 weight percent silicon dioxide, less than 3 weight percent additional additives including cation impurities, the hardness of said composite being greater than 93 on the Rockwell A scale and greater than the combined individual hardness of the fractional weight of silicon nitride times the hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, the density of said composite being greater than 97.5 percent of theoretical density and approaching 100 percent of theoretical density.

Claim 6

A densified composite abrasion resistant ceramic article in accordance with claim 3 wherein said hard refractory material comprises titanium carbide.