Sandblasting nozzle
Assignee: National Aeronautics and Space Administration
•
Filing: 1976-02-17
•
Granted: 1981-02-24
•
Expires: 1996-02-17
Abstract
Abstract An improved nozzle for use with abrasive and/or corrosive materials is formed of sintered ceramic compositions having high temperature oxidation resistance, high hardness and high abrasion and corrosion resistance. The ceramic may be a binary solid solution of a ceramic oxide and silicon nitride, and preferably a ternary solid solution of a ceramic oxide, silicon nitride and aluminum nitride. The ceramic oxide is selected from a group consisting of Al2O3, Y2O3 and Cr2O3, or mixtures thereof. Titanium carbide particles are dispersed in the ceramic mixture before sintering. The nozzles are encased for protection from external forces while in use by a metal or plastic casing.
Inventors
- 👤 Gerald S. Perkins
- 👤 Eugene V. Pawlik
- 👤 Wayne M. Phillips
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:28
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
172 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, said carbide being present in an amount of about 25 percent by volume and being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures or carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consits of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 2
Dependent Claim
172 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, said carbide being present in an amount of about 25 percent by volume and being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures or carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consits of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 3
Dependent Claim
193 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, with the molar proportions of the ingredients in the ceramic material being defined by the area bounded by points A, B, C, and D on the ternary diagram in the accompanying drawing, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 4
Dependent Claim
193 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, with the molar proportions of the ingredients in the ceramic material being defined by the area bounded by points A, B, C, and D on the ternary diagram in the accompanying drawing, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 5
Dependent Claim
20 words
A process as defined in claim 2 wherein said carbide is included as a proportion of about 25% by volume.
Claim 6
Dependent Claim
193 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, with the molar proportions of the ingredients in the ceramic material being defined by the area bounded by points E, F, C, and D on the ternary diagram in the accompanying drawing, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten, and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 7
Dependent Claim
193 words
A process for producing a high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, and an oxide selected from the group consisting of aluminum oxide, yttrium oxide and chromium oxide, with the molar proportions of the ingredients in the ceramic material being defined by the area bounded by points E, F, C, and D on the ternary diagram in the accompanying drawing, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten, and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 8
Dependent Claim
20 words
A process as defined in claim 4 wherein said carbide is included as a proportion of about 25% by volume.
Claim 9
Dependent Claim
192 words
A process for producing high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, an an oxide selected from the group consisting of aluminum oxide, yttrium oxide, and chromium oxide, with the molar proportion of the ingredients in the ceramic material being defined by the area bounded by points G, H, J, and K on the ternary diagram in the accompanying drawings, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 10
Dependent Claim
192 words
A process for producing high temperature, oxidation resistant, and high abrasion and erosion resistant body comprising the steps of: forming a mixture consisting of powdered ceramic material and a carbide, said ceramic material comprising silicon nitride, aluminum nitride, an an oxide selected from the group consisting of aluminum oxide, yttrium oxide, and chromium oxide, with the molar proportion of the ingredients in the ceramic material being defined by the area bounded by points G, H, J, and K on the ternary diagram in the accompanying drawings, and said carbide being of an element selected from the group consisting of titanium, zirconium, hafnium, vanadium, tantalum, tungsten and silicon, and admixtures of carbides of these elements, and including solid solutions of carbides of these elements; placing said mixture which consists of powdered ceramic material and said carbide in a high temperature pressing mold, said mold having a cavity of the shape desired for said body, and said cavity being filled with said mixture in sufficient quantity to produce a desired density in said body, and sintering said mixture while applying pressure to said mold to compress said mixture in the form of said cavity.
Claim 11
Dependent Claim
20 words
A process as defined in claim 6 wherein said carbide is included as a proportion of about 25% by volume.
References Cited (Backward Citations)
US3367826A
Cited
US3455682A
Cited
US3907949A
Cited
US3903230A
Cited
US3886254A
Cited
US3950464A
Cited
US3996329A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-02-24 | 1984-08-25 | 1985-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-02-24 | 1988-08-25 | 1989-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-02-24 | 1992-08-25 | 1993-02-24 | $7700.00 | Window Closed / Lapsed |