Method for manufacture of printed circuit boards
Assignee: MacDermid Acumen Inc
•
Filing: 1986-06-18
•
Granted: 1988-04-05
•
Expires: 2006-06-18
Abstract
Abstract A method of preparing printed circuit boards is described in which the solder mask on the circuit pattern and, optionally, the solder on the through-holes surrounding pads, and like areas to receive solder, is applied over a layer of lead covering the copper layer at said loci. This method eliminates the need to strip tin-lead alloy etch resist which step is commonly employed in prior processes. The method overcomes the problems associated with migration of tin into the copper layer which can occur when tin-lead alloys are applied directly over copper.
Inventors
- 👤 Peter E. Kukanskis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:11
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H05K3/02; H05K3/06; H05K3/061; H05K3/062; H05K3/38; H05K3/382; H05K3/384; H05K3/40; H05K3/42; H05K2203/00; H05K2203/03; H05K2203/0361; H05K3/10; H05K3/108; H05K3/28; H05K3/425; H05K3/427
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
161 words
A method for manufacturing printed circuit boards said method comprising the steps of: (a) providing a non-conductive substrate having a copper layer on both sides thereof and having through-holes made therein; (b) electrolessly depositing copper on the copper layer and through-hole and surrounding pad surfaces; (c) applying a resist image of a trace pattern on said copper layer; (d) subjecting the resulting substrate to a copper electroplating process to deposit additional copper thickness on all exposed copper surfaces including said trace pattern and said through-hole and surrounding pad surfaces; (e) electroplating a continuous layer of lead on all exposed copper surfaces including said copper-plated trace pattern, through-holes and surrounding pad surfaces; (f) removing the imaged material; (g) removing all copper from those areas not protected by said layer of lead; (h) selectively applying a solder mask to said board including lead coated trace pattern but not to loci which are to receive solder; and (i) applying solder to the latter loci.
Claim 2
Independent Claim
161 words
A method for manufacturing printed circuit boards said method comprising the steps of: (a) providing a non-conductive substrate having a copper layer on both sides thereof and having through-holes made therein; (b) electrolessly depositing copper on the copper layer and through-hole and surrounding pad surfaces; (c) applying a resist image of a trace pattern on said copper layer; (d) subjecting the resulting substrate to a copper electroplating process to deposit additional copper thickness on all exposed copper surfaces including said trace pattern and said through-hole and surrounding pad surfaces; (e) electroplating a continuous layer of lead on all exposed copper surfaces including said copper-plated trace pattern, through-holes and surrounding pad surfaces; (f) removing the imaged material; (g) removing all copper from those areas not protected by said layer of lead; (h) selectively applying a solder mask to said board including lead coated trace pattern but not to loci which are to receive solder; and (i) applying solder to the latter loci.
Claim 3
Dependent Claim
25 words
A method according to claim 1 wherein step (i) is carried out by immersion in a bath of solder followed by a hot air levelling.
Claim 4
Dependent Claim
27 words
A method according to claim 2 wherein said solder is applied without first removing the said layer of lead from said loci which are to receive solder.
Claim 5
Dependent Claim
26 words
A method according to claim 1 wherein the layer of lead on said loci which are to receive solder is removed prior to applying solder thereto.
Claim 6
Dependent Claim
17 words
A method according to claim 4 wherein said layer of lead is stripped using an acid bath.
Claim 7
Dependent Claim
67 words
A method according to claim 1 which comprises the additional steps, introduced after step (e), of applying a second plating resist to said layer of lead on said trace patterns and thereafter applying solder to the remaining lead coated copper loci prior to carrying out step (f) which removes said second plating resist in addition to the plating resist material remaining on the substrate from step (c).
Claim 8
Dependent Claim
26 words
A method according to claim 6 wherein the final step (i) comprises reflowing the solder which has been applied, in the second of said additional steps.
Claim 9
Independent Claim
213 words
A method for manufacturing printed circuit boards containing conductive through-holes, conductive pads surrounding said through-holes and conductive copper traces forming a circuit pattern on said board, and wherein said pads and through-holes are provided with a solder coating and said copper traces are coated with a non-reflowable metal and provided with a solder mask, said method comprising the steps of: (a) providing a non-conductive substrate having copper foil laminated to both sides thereof and having through-holes made therein; (b) electrolessly depositing a copper layer on the copper foil and through-hole and surrounding pad surfaces; (c) applying a trace pattern on said copper layer; (d) subjecting the resulting substrate to a copper electroplating process to deposit additional copper thickness on all exposed copper surfaces including said trace pattern and said through-holes and surrounding pad surfaces; (e) electroplating a continuous layer of lead on all exposed copper surfaces including said copper plated trace pattern, through-holes and surrounding pad surfaces; (f) removing the imaged material; (g) removing all copper from areas not protected by said layer of lead; (h) applying a solder mask to said board including the lead coated trace pattern but not to loci including said through-holes and surrounding surfaces which are to receive solder; and (i) applying the solder to the latter loci.
Claim 10
Independent Claim
213 words
A method for manufacturing printed circuit boards containing conductive through-holes, conductive pads surrounding said through-holes and conductive copper traces forming a circuit pattern on said board, and wherein said pads and through-holes are provided with a solder coating and said copper traces are coated with a non-reflowable metal and provided with a solder mask, said method comprising the steps of: (a) providing a non-conductive substrate having copper foil laminated to both sides thereof and having through-holes made therein; (b) electrolessly depositing a copper layer on the copper foil and through-hole and surrounding pad surfaces; (c) applying a trace pattern on said copper layer; (d) subjecting the resulting substrate to a copper electroplating process to deposit additional copper thickness on all exposed copper surfaces including said trace pattern and said through-holes and surrounding pad surfaces; (e) electroplating a continuous layer of lead on all exposed copper surfaces including said copper plated trace pattern, through-holes and surrounding pad surfaces; (f) removing the imaged material; (g) removing all copper from areas not protected by said layer of lead; (h) applying a solder mask to said board including the lead coated trace pattern but not to loci including said through-holes and surrounding surfaces which are to receive solder; and (i) applying the solder to the latter loci.
Claim 11
Dependent Claim
24 words
A method according to claim 8 wherein the solder is applied without first removing said layer of lead from said loci to receive solder.
Claim 12
Dependent Claim
26 words
A method according to claim 8 wherein the layer of lead on said loci which are to receive solder is removed prior to applying solder thereto.
Claim 13
Dependent Claim
67 words
A method according to claim 8 which comprises the additional steps, introduced after step (e), of applying a second plating resist to said layer of lead on said trace patterns and thereafter applying solder to the remaining lead coated copper loci prior to carrying out step (f) which removes said second plating resist in addition to the plating resist material remaining on the substrate from step (c).
Claim 14
Dependent Claim
26 words
A method according to claim 11 wherein the final step (i) comprises reflowing the solder which has been applied in the second of said additional steps.
Claim 15
Dependent Claim
41 words
In a process for the preparation of a circuit board wherein the copper circuit traces are coated with a non-reflowable metal and provided with a solder mask over said non-reflowable metal the improvement which comprises employing lead as said non-reflowable metal.
Claim 16
Dependent Claim
41 words
In a process for the preparation of a circuit board wherein the copper circuit traces are coated with a non-reflowable metal and provided with a solder mask over said non-reflowable metal the improvement which comprises employing lead as said non-reflowable metal.
Claim 17
Dependent Claim
20 words
A process according to claim 13 wherein said circuit board is provided with through-holes and surrounding pads covered with solder.
Claim 18
Dependent Claim
25 words
A process according to claim 14 wherein said through-holes and surrounding pads are coated with a layer of lead over which the solder is applied.
References Cited (Backward Citations)
US2959525A
Cited
US3297442A
Cited
US3483615A
Cited
US3673680A
Cited
US4104111A
Cited
US4135988A
Cited
US4312897A
Cited
US4436806A
Cited
US4444619A
Cited
US4512829A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-04-05 | 1991-10-05 | 1992-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-04-05 | 1995-10-05 | 1996-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-04-05 | 1999-10-05 | 2000-04-05 | $7700.00 | Window Closed / Lapsed |