Method of diffusing conductivity type imparting material into III-V compound semiconductor material
Assignee: Verizon Laboratories Inc
•
Filing: 1986-06-26
•
Granted: 1988-02-16
•
Expires: 2006-06-26
Abstract
Abstract Method of diffusing sulfur into gallium arsenide without degrading the surface of the gallium arsenide. A gallium arsenide wafer is placed in close proximity to a quantity of powdered gallium sulfide intermixed with powdered gallium arsenide. The assemblage is heated in an open-tube furnace in the presence of flowing nitrogen to vaporize sulfur while the gallium arsenide and gallium sulfide are in thermodynamic equilibrium whereby sulfur diffuses into the gallium arsenide wafer without eroding the surface.
Inventors
- 👤 Moshe Oren
- 👤 Francisco C. Prince
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:30
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P32/174
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
123 words
The method of introducing a donor element into a body of gallium arsenide comprising placing a body of gallium arsenide in close proximity to a donor source consisting essentially of a quantity of a donor compound in powder form intermixed with gallium arsenide in powder form, said donor compound having gallium as one constituent element and having as a second constituent element an element which is a donor element for gallium arsenide; placing the body of gallium arsenide and donor source in an open-tube furnace; and heating while flowing an inert gas through the open-tube furnace to vaporize said donor element with the gallium arsenide and the donor compound in thermodynamic equilibrium whereby said donor element diffuses into the body of gallium arsenide.
Claim 2
Independent Claim
123 words
The method of introducing a donor element into a body of gallium arsenide comprising placing a body of gallium arsenide in close proximity to a donor source consisting essentially of a quantity of a donor compound in powder form intermixed with gallium arsenide in powder form, said donor compound having gallium as one constituent element and having as a second constituent element an element which is a donor element for gallium arsenide; placing the body of gallium arsenide and donor source in an open-tube furnace; and heating while flowing an inert gas through the open-tube furnace to vaporize said donor element with the gallium arsenide and the donor compound in thermodynamic equilibrium whereby said donor element diffuses into the body of gallium arsenide.
Claim 3
Dependent Claim
22 words
The method in accordance with claim 1 wherein said donor element is selected from the group consisting of sulfur, tellurium, and selenium.
Claim 4
Dependent Claim
14 words
The method in accordance with claim 1 wherein said donor compound is gallium sulfide.
Claim 5
Dependent Claim
22 words
The method in accordance with claim 3 wherein heating comprises heating at a temperature of between about 750° C. and 900° C.
Claim 6
Independent Claim
158 words
The method of introducing a donor element into a wafer of gallium arsenide comprising placing a wafer of gallium arsenide and a quantity of a donor source in a boat with a planar surface of the wafer of gallium arsenide facing and in close proximity to the donor source; said quantity of a donor source consisting essentially of a quantity of a donor compound in powder form intermixed with gallium arsenide in powder form; said donor compound having gallium as one constituent element and having as a second constituent element an element which is a donor element for gallium arsenide; placing the boat containing the wafer of gallium arsenide and the quantity of the donor source in an open-tube furnace; and heating while flowing an inert gas through the open-tube furnace to vaporize said donor element with the gallium arsenide and the donor compound in thermodynamic equilibrium whereby said donor element diffuses into the wafer of gallium arsenide.
Claim 7
Independent Claim
158 words
The method of introducing a donor element into a wafer of gallium arsenide comprising placing a wafer of gallium arsenide and a quantity of a donor source in a boat with a planar surface of the wafer of gallium arsenide facing and in close proximity to the donor source; said quantity of a donor source consisting essentially of a quantity of a donor compound in powder form intermixed with gallium arsenide in powder form; said donor compound having gallium as one constituent element and having as a second constituent element an element which is a donor element for gallium arsenide; placing the boat containing the wafer of gallium arsenide and the quantity of the donor source in an open-tube furnace; and heating while flowing an inert gas through the open-tube furnace to vaporize said donor element with the gallium arsenide and the donor compound in thermodynamic equilibrium whereby said donor element diffuses into the wafer of gallium arsenide.
Claim 8
Dependent Claim
22 words
The method in accordance with claim 5 wherein said donor element is selected from the group consisting of sulfur, tellurium, and selenium.
Claim 9
Dependent Claim
14 words
The method in accordance with claim 5 wherein said donor compound is gallium sulfide.
Claim 10
Dependent Claim
22 words
The method in accordance with claim 7 wherein heating comprises heating at a temperature of between about 750° C. and 900° C.
Claim 11
Dependent Claim
21 words
The method in accordance with claim 8 wherein heating comprises heating for a period of from about 15 to 30 minutes.
Claim 12
Dependent Claim
38 words
The method in accordance with claim 9 wherein said surface of the wafer of gallium arsenide is separated from the quantity of gallium sulfide intermixed with gallium arsenide by approximately one millimeter while heating in the open-tube furnace.
Claim 13
Dependent Claim
80 words
The method in accordance with claim 10 including forming a coating of a masking material in a predetermined pattern on said surface of said wafer of gallium arsenide prior to placing the wafer in close proximity to said quantity of gallium sulfide intermixed with gallium arsenide, and placing the wafer with said coating facing said quantity of gallium sulfide intermixed with gallium arsenide whereby sulfur diffuses into said wafer at the portion of the surface not coated with masking material.
References Cited (Backward Citations)
US3139362A
Cited
US3215571A
Cited
US3485685A
Cited
US3713910A
Cited
US3755016A
Cited
US3984267A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-02-15 | 1991-08-17 | 1992-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-02-15 | 1995-08-17 | 1996-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-02-15 | 1999-08-17 | 2000-02-16 | $7700.00 | Window Closed / Lapsed |