Hot melt adhesive for elastic banding and method for utlizing the same
Assignee: HB Fuller Licensing and Financing Inc
•
Filing: 1981-03-26
•
Granted: 1988-01-12
•
Expires: 2001-03-26
Abstract
Abstract A purpose of the disclosed method is to impart gathers and elasticity to a relatively inelastic film, membrane, or web substrate, through elastic banding with a viscoelastic hot melt pressure-sensitive adhesive (PSA). Typically, the resulting elastic-banded substrate product (e.g. 40) will be cut into discrete units and formed into garments or body-encircling members such as disposable diapers. One step of the preferred method involves extruding a ribbon or band (13 or 113) comprising a viscoelastic hot melt PSA, which PSA has unusually high cohesion, stretchiness, and elasticity without excessive loss of adhesive bonding strength. (The viscoelastic behavior of the PSA is believed to be determined, at least in part, by the relative size of its crystalline domains and its rubbery domains and the glass transition temperatures and softening points of its components.) A second step of the preferred method involves bringing the band of hot melt (13 or 113) into adherent contact with a surface of a moving continuous substrate (22 or 32 or 132). A typical substrate would be the polyolefin film used in the manufacture of disposable diapers. The band can be bonded to the substrate through a pressure activation technique, wherein the band itself has the necessary inherent adhesive properties.
Inventors
- 👤 William L. Bunnelle
- 👤 Richard C. Lindmark, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:07
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; A; A41; A41F; A41F9/00; A41F9/02; A61; A61F; A61F13/00; A61F13/15; A61F13/15577; A61F13/15585; A61F13/15593; B32B37/00; B32B37/14; B32B37/144; B32B37/12; B32B37/1207; B32B2037/1215; B32B2037/1223; B32B2309/00; B32B2309/02; B32B2309/08; B32B2309/10; B32B2309/105; B32B2555/00; B32B2555/02; B32B37/15; B32B37/153
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
334 words
A viscoelastic hot melt pressure-sensitive adhesive-elastic composition consisting essentially of: a major amount by weight, not exceeding 70% by weight, of a rubbery block copolymer which copolymer includes a rubbery midblock portion and which is terminated with crystalline vinyl arene end blocks; about 70 to about 80% by weight of said rubbery block copolymer comprising said rubbery midblock portion and about 20 to about 30% by weight of said rubbery block copolymer comprising said vinyl arene end blocks; a minor amount by weight, not less than 30% by weight, of a tackifying resin generally compatible with and generally associated with said midblock portion; 2-9% by weight of an aromatic, essentially hydrocarbon resin having a glass transition temperature and a softening point above those of said vinyl arene end blocks and said tackifying resin; said aromatic, essentially hydrocarbon resin being generally compatible with and generally associated with said end blocks; and - 5% by weight of essentially inert extenders, fillers, pigments, and antioxidants that do not substantially affect the adhesive or elastic properties of the composition; the foregoing proportions being selected to provide the following pressure-sensitive adhesive and rheological properties: (i) a tensile strength at 500% elongation, determined at 20°-25° C., of at least 50 pounds per square inch; (ii) a 180° peel resistance, according to PSTC-1, determined at 20°-25° C. 24 hours after formation of the pressure-sensitive adhesive bond, of at least about 450 grams per 25.4 mm-width; (iii) a dead load deformation, tested at room temperature, 37.8° C., 43.3° C., and 48.9° C. for 3 hours under 1500 g/cm 2 , of less than 50%, where dead load deformation=the increased length minus the original length divided by the original length of a sample at least 25 mm in length; (iv) the following loss modulus, storage modulus, and loss tangent values at 0.01-0.25 Hz throughout the temperature range of 25°-50° C.: loss modulus: 4×10 4 to 35×10 4 dynes/cm 2 storage modulus: 75×10 4 to 200×10 4 dynes/cm 2 loss tangent: 0.03 to 0.3
Claim 2
Dependent Claim
334 words
A viscoelastic hot melt pressure-sensitive adhesive-elastic composition consisting essentially of: a major amount by weight, not exceeding 70% by weight, of a rubbery block copolymer which copolymer includes a rubbery midblock portion and which is terminated with crystalline vinyl arene end blocks; about 70 to about 80% by weight of said rubbery block copolymer comprising said rubbery midblock portion and about 20 to about 30% by weight of said rubbery block copolymer comprising said vinyl arene end blocks; a minor amount by weight, not less than 30% by weight, of a tackifying resin generally compatible with and generally associated with said midblock portion; 2-9% by weight of an aromatic, essentially hydrocarbon resin having a glass transition temperature and a softening point above those of said vinyl arene end blocks and said tackifying resin; said aromatic, essentially hydrocarbon resin being generally compatible with and generally associated with said end blocks; and - 5% by weight of essentially inert extenders, fillers, pigments, and antioxidants that do not substantially affect the adhesive or elastic properties of the composition; the foregoing proportions being selected to provide the following pressure-sensitive adhesive and rheological properties: (i) a tensile strength at 500% elongation, determined at 20°-25° C., of at least 50 pounds per square inch; (ii) a 180° peel resistance, according to PSTC-1, determined at 20°-25° C. 24 hours after formation of the pressure-sensitive adhesive bond, of at least about 450 grams per 25.4 mm-width; (iii) a dead load deformation, tested at room temperature, 37.8° C., 43.3° C., and 48.9° C. for 3 hours under 1500 g/cm 2 , of less than 50%, where dead load deformation=the increased length minus the original length divided by the original length of a sample at least 25 mm in length; (iv) the following loss modulus, storage modulus, and loss tangent values at 0.01-0.25 Hz throughout the temperature range of 25°-50° C.: loss modulus: 4×10 4 to 35×10 4 dynes/cm 2 storage modulus: 75×10 4 to 200×10 4 dynes/cm 2 loss tangent: 0.03 to 0.3
Claim 3
Dependent Claim
15 words
The adhesive-elastic composition of claim 1 wherein the vinyl arene endblocks are poly styrene endblocks.
Claim 4
Dependent Claim
14 words
The adhesive-elastic composition of claim 1 wherein the rubbery midblock is a polyisoprene midblock.
Claim 5
Dependent Claim
77 words
The adhesive-elastic composition of claim 1 wherein at 0.01 Hz the loss modulus is about 5×10 4 to 20×10 4 dynes/cm 2 , the storage modulus is about 75×10 4 to 150×10 4 dynes/cm 2 , and the loss tangent is 0.05-0.2, and at 0.25 Hz the loss modulus is 7×10 4 to 25×10 4 , the storage modulus is about 85×10 4 to about 150×10 4 dynes/cm 2 , and the loss tangent is about 0.07-0.25.
Claim 6
Dependent Claim
35 words
The adhesive-elastic composition of claim 1 wherein the rubbery block copolymer comprises a polystyrene-polyisoprene-polystyrene block copolymer which is present in the composition at an amount of about 51-70 wt-% based on the entire adhesive-elastic composition.
Claim 7
Dependent Claim
33 words
The adhesive-elastic composition of claim 1 wherein the tackifying resin is a synthetic terpene tackifying resin and is present at an amount of about 30 to 49 wt-% based on the adhesive-elastic composition.
Claim 8
Dependent Claim
32 words
The adhesive-elastic composition of claim 1 wherein the aromatic, essentially hydrocarbon resin, is a coumarone-indene resin which is present in an amount of 2 to 7 wt-% based on the adhesive-elastic composition.
Claim 9
Dependent Claim
38 words
The adhesive-elastic composition of claim 1 wherein the aromatic, essentially hydrocarbon resin is a polystyrene, polyalphamethylstyrene, a vinyl toluene resin, or a mixture thereof at a concentration of about 2 to 7 wt-% based on the adhesive-elastic composition.
Claim 10
Dependent Claim
28 words
The adhesive-elastic composition of claim 6 wherein the synthetic terpene resin is present in an amount of about 45-95 parts per 100 parts of the rubbery block copolymer.
Claim 11
Dependent Claim
33 words
The adhesive-elastic composition of claim 8 wherein the resin is present at a concentration of about 3 to about 10 parts by weight of the resin per 100 parts of rubbery block copolymer.
References Cited (Backward Citations)
CA844015A
Cited
CA901710A
Cited
US975004A
Cited
US2022852A
Cited
US2559649A
Cited
US2531234A
Cited
US2574200A
Cited
US2737701A
Cited
US2846492A
Cited
US3239402A
Cited
GB985614A
Cited
FR1403980A
Cited
GB1033115A
Cited
US3239478A
Cited
US3231635A
Cited
US3352944A
Cited
US3449306A
Cited
US3242038A
Cited
US3518142A
Cited
US3507934A
Cited
US3562204A
Cited
US3519585A
Cited
US3464850A
Cited
US3641205A
Cited
US3592788A
Cited
US3555112A
Cited
US3538031A
Cited
US3686107A
Cited
US3736281A
Cited
FR2014204A1
Cited
US3630980A
Cited
US3632540A
Cited
US3635861A
Cited
US3600250A
Cited
US3567487A
Cited
US3576911A
Cited
GB1324591A
Cited
US3634549A
Cited
US3630201A
Cited
US3575175A
Cited
US3592710A
Cited
US3595237A
Cited
US3676202A
Cited
US3625752A
Cited
US3643662A
Cited
US3658740A
Cited
US3665923A
Cited
CA994053A
Cited
US3570491A
Cited
US3753936A
Cited
US3660323A
Cited
US3672371A
Cited
US3652720A
Cited
US3716503A
Cited
US3678134A
Cited
NL7309156A
Cited
US3688771A
Cited
GB1405786A
Cited
CA997084A
Cited
DE2222518A1
Cited
US4046838A
Cited
CA1031503A
Cited
US3956223A
Cited
GB1576046A
Cited
UST975004I4
Cited
US4259220A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-01-11 | 1991-07-13 | 1992-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-01-11 | 1995-07-13 | 1996-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-01-11 | 1999-07-13 | 2000-01-12 | $7700.00 | Window Closed / Lapsed |