Composite materials, their preparation and articles made therefrom
Assignee: MATCOM Inc
•
Filing: 1985-11-08
•
Granted: 1987-12-29
•
Expires: 2005-11-08
Abstract
Abstract High strength, light weight composite material, comprising discrete reinforcing elements surrounded by a matrix including polymer micro-bits that are substantially free of the intact cells of the expanded, hydrophobic, thermoplastic polymers from which they are produced, is prepared by hot pressing paper-like elements made using paper making technology.
Inventors
- 👤 Max Klein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:34
CPC Classifications
D; D21; D21H; D21H25/00; D21H25/04; D21H25/06; C; C08; C08J; C08J11/00; C08J11/04; C08J11/06; D21H21/00; D21H21/50; D21H21/52; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1314; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/249942; Y10T428/249945; Y10T428/249946; Y10T428/31504; Y10T428/31855; Y10T428/31909
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
90 words
An aqueous dispersion for the production of composite material in the form of a sheet or web comprising a continuous matrix phase which surrounds a reinforcement phase composed of discrete reinforcing elements, the disperse phase of said aqueous dispersion including (i) polymer micro-bits produced from an expanded, hydrophobic, thermoplastic polymer which is non-brittle in expanded form, said polymer micro-bits being substantially completely free of intact cells of the expanded polymer from which they are produced, (ii) at least one finely divided, hydrophobic, heat fusible resin, and (iii) said reinforcing elements.
Claim 2
Dependent Claim
90 words
An aqueous dispersion for the production of composite material in the form of a sheet or web comprising a continuous matrix phase which surrounds a reinforcement phase composed of discrete reinforcing elements, the disperse phase of said aqueous dispersion including (i) polymer micro-bits produced from an expanded, hydrophobic, thermoplastic polymer which is non-brittle in expanded form, said polymer micro-bits being substantially completely free of intact cells of the expanded polymer from which they are produced, (ii) at least one finely divided, hydrophobic, heat fusible resin, and (iii) said reinforcing elements.
Claim 3
Dependent Claim
52 words
Aqueous dispersion according to claim 1, wherein the heat fusible resin is selected from the group of polycarbonates, polyolefins, including low and high molecular weight polyethylene and polypropylene and co-polymers thereof, polyester, nylon, polyacetals, chloropolymers, including chlorinated ethylene and polyvinyl chloride, fluoropolymers, including polytetrofluoroethylene, acrylic resins, acrylonitrile-butadiene-styreene (A.B.S.) polymers or copolymers thereof.
Claim 4
Dependent Claim
48 words
Aqueous dispersion according to claim 1, wherein the expanded, hydrophobic, thermoplastic polymer is selected from the group of a styrene polymer, a lower polyolefin which is the polymer of an ethylenically unsaturateed hydrocarbon monomer having from 2 to 6 carbon atoms, or co-polymers or blends of said polymers.
Claim 5
Dependent Claim
23 words
Aqueous dispersion according to claim 1, including a fibrous reinforcing element selected from the group of glass, carbonaceous, polymer, inorganic, and metal fibers.
Claim 6
Dependent Claim
14 words
Aqueous dispersion according to claim 4, wherein the fibrous reinforcing element comprises cellulosic fiber.
Claim 7
Dependent Claim
28 words
Aqueous dispersion according to claim 5, wherein a portion of the polymer micro-bits component of the disperse phase is intimately blended with cellulose fibers to form a cobeat.
Claim 8
Dependent Claim
32 words
Aqueous dispersion according to claim 6, wherein said cobeat comprises about 35 to about 50 weight percent of polymer micro-bits and from about 50 to about 65 weight percent of cellulose fiber.
Claim 9
Dependent Claim
14 words
Aqueous dispersion according to claim 6, wherein polyester fiber is included in the cobeat.
Claim 10
Dependent Claim
14 words
Aqueous dispersion according to claim 8, wherein the polyester fiber is polyethylene terephthalate fiber.
Claim 11
Dependent Claim
32 words
Aqueous dispersion according to claim 5, wherein there is included a compatible binding agent in an amount effective for binding together the components of the disperse phase in sheet or web form.
Claim 12
Dependent Claim
21 words
Aqueous dispersion according to claim 10, wherein the binding agent is polyvinyl alcohol, optionally including a minor amount of melamine-formaldehyde resin.
Claim 13
Dependent Claim
39 words
Aqueous dispersion according to claim 1, wherein the disperse phase includes a particulate reinforcing element selected from the group of diatomaceous earth, polyurethane micro-bits, aluminum oxide, wood flour, saw dust, carbon powder, silicon dioxide, calcium carbonate, mica, and clay.
Claim 14
Dependent Claim
39 words
Aqueous dispersion according to claim 2, wherein the disperse phase includes a particulate reinforcing element selected from the group of diatomaceous earth, polyurethane micro-bits, aluminum oxide, wood flour, saw dust, carbon powder, silicon dioxide, calcium carbonate, mica, and clay.
Claim 15
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 1, which is capable of being heat fused into a composite material.
Claim 16
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 2, which is capable of being heat fused into a composite material.
Claim 17
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 3, which is capable of being heat fused into a composite material.
Claim 18
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 4, which is capable of being heat fused into a composite material.
Claim 19
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 5 which is capable of being heat fused into a composite material.
Claim 20
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 6 which is capable of being heat fused into a composite material.
Claim 21
Dependent Claim
22 words
A sheet or web prepared from the aqueous dispersion claim 7 which is capable of being heat fused into a composite material.
Claim 22
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 8 which is capable of being heat fused into a composite material.
Claim 23
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 9 which is capable of being heat fused into a composite material.
Claim 24
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 10 which is capable of being heat fused into a composite material.
Claim 25
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 11 which is capable of being heat fused into a composite material.
Claim 26
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 12 which is capable of being heat fused into a composite material.
Claim 27
Dependent Claim
23 words
A sheet or web prepared from the aqueous dispersion of claim 13 which is capable of being heat fused into a composite material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-12-28 | 1991-06-29 | 1991-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-12-28 | 1995-06-29 | 1995-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-12-28 | 1999-06-29 | 1999-12-29 | $7700.00 | Window Closed / Lapsed |