Producing glass-reinforced polyolefin compositions
Assignee: Mitsubishi Chemical Corp
•
Filing: 1972-08-30
•
Granted: 1977-01-18
•
Expires: 1992-08-30
Abstract
Abstract A modified polyolefin obtained by adding to 100 parts by weight of a polyolefin 0.01 to 0.8 parts by weight of an unsaturated carboxylic acid or anhydride thereof having 3 to 8 carbon atoms in the molecule and 0.05 to 0.5 parts by weight of an organic peroxide and melt-mixing these components in an extruder, has an outstanding adhesion to glass fibers. A blend of such a modified polyolefin filled with glass reinforcements has excellent physical properties as well as excellent appearance. The modification of polyolefin may be effected in the presence of a glass reinforcement to achieve both modification and mixing in a single stage, resulting in a composition with superior physical properties owing to improved dispersion and least break down of the glass reinforcement.
Inventors
- 👤 Fumio Ide
- 👤 Isao Sasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:17
CPC Classifications
C; C08; C08F; C08F255/00; B; B29; B29C; B29C48/00; B29C48/022; B29C48/25; B29C48/285; B29C48/288; B29C48/2886; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/12; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; B29C48/03; B29C48/05; B29K; B29K2105/00; B29K2105/06; B29K2105/12
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
124 words
In an extrusion process for providing a glass-reinforced polyolefin composite comprising the addition of an unsaturated carboxylic acid or anhydride thereof having 3 to 8 carbon atoms and 0.05 to 0.5 parts by weight of an organic peroxide to 100 parts by weight of a polyolefin, meltmixing the mixture in an extruder to form a modified polyolefin, and blending the resulting modified polyolefin with 5 to 200 parts by weight of a glass reinforcement, the improvement which comprises: controlling the amount of the unsaturated carboxylic acid or anhydride thereof added within a range of 0.01 to 0.8 parts by weight, the unsaturated carboxylic acid or anhydried thereof serving as the essential agent to enhance adhesion and affinity of the polyolefin to the glass reinforcement.
Claim 2
Dependent Claim
124 words
In an extrusion process for providing a glass-reinforced polyolefin composite comprising the addition of an unsaturated carboxylic acid or anhydride thereof having 3 to 8 carbon atoms and 0.05 to 0.5 parts by weight of an organic peroxide to 100 parts by weight of a polyolefin, meltmixing the mixture in an extruder to form a modified polyolefin, and blending the resulting modified polyolefin with 5 to 200 parts by weight of a glass reinforcement, the improvement which comprises: controlling the amount of the unsaturated carboxylic acid or anhydride thereof added within a range of 0.01 to 0.8 parts by weight, the unsaturated carboxylic acid or anhydried thereof serving as the essential agent to enhance adhesion and affinity of the polyolefin to the glass reinforcement.
Claim 3
Dependent Claim
122 words
In an extrusion process for providing a glass-reinforced polyolefin composite comprising the addition of an unsaturated carboxylic acid or anhydride thereof having 3 to 8 carbon atoms, 0.05 to 0.5 parts by weight of an organic peroxide and 5 - 200 parts by weight of a glass reinforcement to 100 parts by weight of a polyolefin, melt-mixing the mixture in an extruder to form a modified polyolefin blended with the glass reinforcement the improvement which comprises: controlling the amount of the unsaturated carboxylic acid or anhydride thereof added within a range of 0.01 to 0.8 parts by weight, the unsaturated carboxylic acid or anhydride thereof serving as the essential agent to enhance adhesion and affinity of the polyolefin to the glass reinforcement.
Claim 4
Dependent Claim
122 words
In an extrusion process for providing a glass-reinforced polyolefin composite comprising the addition of an unsaturated carboxylic acid or anhydride thereof having 3 to 8 carbon atoms, 0.05 to 0.5 parts by weight of an organic peroxide and 5 - 200 parts by weight of a glass reinforcement to 100 parts by weight of a polyolefin, melt-mixing the mixture in an extruder to form a modified polyolefin blended with the glass reinforcement the improvement which comprises: controlling the amount of the unsaturated carboxylic acid or anhydride thereof added within a range of 0.01 to 0.8 parts by weight, the unsaturated carboxylic acid or anhydride thereof serving as the essential agent to enhance adhesion and affinity of the polyolefin to the glass reinforcement.
Claim 5
Dependent Claim
11 words
A process according to claim 1, wherein the polyolefin is polypropylene.
Claim 6
Dependent Claim
11 words
A process according to claim 2, wherein the polyolefin is polypropylene.
Claim 7
Dependent Claim
11 words
A process according to claim 1, wherein the polyolefin is polyethylene.
Claim 8
Dependent Claim
11 words
A process according to claim 2, wherein the polyolefin is polyethylene.
Claim 9
Dependent Claim
17 words
A process according to claim 1, wherein the unsaturated carboxylic acid is acrylic acid or methacrylic acid.
Claim 10
Dependent Claim
17 words
A process according to claim 2, wherein the unsaturated carboxylic acid is acrylic acid or methacrylic acid.
Claim 11
Dependent Claim
17 words
A process according to claim 1, wherein the anhydride of an unsaturated carboxylic acid is maleic anhydride.
Claim 12
Dependent Claim
17 words
A process according to claim 2, wherein the anhydride of an unsaturated carboxylic acid is maleic anhydride.
Claim 13
Dependent Claim
23 words
A process according to claim 1, wherein 0.05 to 0.5 part by weight of the unsaturated carboxylic acid or anhydride thereof is used.
Claim 14
Dependent Claim
23 words
A process according to claim 2, wherein 0.05 to 0.5 part by weight of the unsaturated carboxylic acid or anhydride thereof is used.
Claim 15
Dependent Claim
36 words
A process according to claim 1, wherein the organic peroxide is at least one compound selected from the group consisting of benzoyl peroxide, lauroyl peroxide, dicumyl peroxide, methyl ethyl ketone peroxide, di-tertbutyl peroxide, and tert-butyl hydroperoxide.
Claim 16
Dependent Claim
36 words
A process according to claim 2, wherein the organic peroxide is at least one compound selected from the group consisting of benzoyl peroxide, lauroyl peroxide, dicumyl peroxide, methyl ethyl ketone peroxide, di-tert-butyl peroxide, and tert-butyl hydroperoxide.
Claim 17
Dependent Claim
30 words
A process according to claim 1, wherein the glass reinforcement is at least one member selected from the group consisting of glass fiber, glass powder, glass bead, and glass balloon.
Claim 18
Dependent Claim
30 words
A process according to claim 2, wherein the glass reinforcement is at least one member selected from the group consisting of glass fiber, glass powder, glass bead, and glass balloon.
Claim 19
Dependent Claim
35 words
A process according to claim 1, wherein the modified polyolefin is a mixture of a modified polyolefin and an unmodified polyolefin, and the modified polyolefin content of said mixture is at least 20% by weight.
Claim 20
Dependent Claim
71 words
A process according to claim 1, wherein the polyolefin, unsaturated carboxylic acid or anhydride thereof, and organic peroxide are mixed to modify the polyolefin in a melt-mixing equipment having a cylinder and a screw rotating therein and forming, in sequence, a feeding zone, metering zone, decompression zone, and transport zone, under such conditions that the reaction temperature is 150° to 280° C. and the reaction period is 5 to 30 minutes.
Claim 21
Dependent Claim
79 words
A process according to claim 2, wherein the polyolefin, unsaturated carboxylic acid or anhydride thereof, organic proxide and the glass reinforcement are mixed to modify the polyolefin and disperse the glass reinforcement in a melt-mixing equipment having a cylinder and a screw rotating therein and forming, in sequence, a feeding zone, metering zone, decompression zone, and transport zone, under such conditions that the reaction temperature is 150° to 280° C. and the reaction period is 5 to 30 minutes.
Claim 22
Dependent Claim
18 words
A process according to claim 9, wherein the amount of maleic anhydride is 0.05 to 0.8% by weight.
Claim 23
Dependent Claim
22 words
A process according to claim 1, wherein the amount of unsaturated carboxylic acid or anhydride thereof is 0.05 to 0.8% by weight.
Claim 24
Dependent Claim
34 words
A process according to claim 2, wherein the amount of unsaturated carboxylic acid or anhydride thereof is 0.05 to 0.8% by weight, and the melting and kneading is carried out under a nitrogen atmosphere.
Claim 25
Dependent Claim
29 words
A process of claim 1, wherein said unsaturated carboxylic acid or anhydride thereof is acrylic acid, methacrylic acid, maleic acid, fumaric acid, crotonic acid, itaconic acid and their anhydrides.
Claim 26
Dependent Claim
29 words
A process of claim 2, wherein said unsaturated carboxylic acid or anhydride thereof is acrylic acid, methacrylic acid, maleic acid, fumaric acid, crotonic acid, itaconic acid and their anhydrides.
References Cited (Backward Citations)
US3177269A
Cited
US3308090A
Cited
US3416990A
Cited
GB1095700A
Cited
US3437550A
Cited
US3579476A
Cited
US3733300A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-18 | 1980-07-19 | 1981-01-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-18 | 1984-07-19 | 1985-01-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-18 | 1988-07-19 | 1989-01-18 | $7700.00 | Window Closed / Lapsed |