US4710433A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Transparent conductive windows, coatings, and method of manufacture
Assignee: Northrop Grumman Corp
•
Filing: 1986-07-09
•
Granted: 1987-12-01
•
Expires: 2006-07-09
Abstract
Abstract Methods are disclosed for the manufacture of optical conductive transparent windows and coatings having high transparency over a wide bandwidth combined with a large acceptance angle of incidence. Particulars for making windows and coatings with gold films of high transparency and low sheet resistance using specified nucleating and barrier layers are given. Examples include windows and coatings constructed for operation in the infrared and ultraviolet.
Inventors
- 👤 James M. Rowe
- 👤 Rudolph W. Modster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:29
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3618; C03C17/3649; C03C17/3652; C03C17/3657; C03C17/3681; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12583; Y10T428/1259; Y10T428/12597; Y10T428/12611; Y10T428/1266; Y10T428/12667; Y10T428/12674; Y10T428/12736; Y10T428/1275; Y10T428/12764; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12861; Y10T428/12889; Y10T428/12896
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
176 words
An electrically conductive window having high optical transparency in the infrared, visible, or UV bands comprising a substrate having at lease one smooth contiuous surface on one side thereof, an intermediate dielectric impedance matching stack dsposited on said substrate surface, a first difusion barrier layer deposited on said intermediate matching stack, a nucleating layer deposited on said first barrier layer, a conductive metal layer deposited on said nucleating layer in a film of continuous uniform thickness of about 10 nm or lesss with optical constants n, k, said nucleating layer being selected to cooparate with said metal layer to allow the metal layer to form in a continuous thin film without agglomeration having optical constants n, k approximating these of the bulk metal and with a low sheet resistance, said intermediate stack forming an impedance match between said substrate and said conductive layer, a second diffusion barrier layer deposited on said metal layer, and an outer dieletric anti-reflection stack deposited on said second barrier layer to form an impedance match between said conductive layer and air.
Claim 2
Dependent Claim
176 words
An electrically conductive window having high optical transparency in the infrared, visible, or UV bands comprising a substrate having at lease one smooth contiuous surface on one side thereof, an intermediate dielectric impedance matching stack dsposited on said substrate surface, a first difusion barrier layer deposited on said intermediate matching stack, a nucleating layer deposited on said first barrier layer, a conductive metal layer deposited on said nucleating layer in a film of continuous uniform thickness of about 10 nm or lesss with optical constants n, k, said nucleating layer being selected to cooparate with said metal layer to allow the metal layer to form in a continuous thin film without agglomeration having optical constants n, k approximating these of the bulk metal and with a low sheet resistance, said intermediate stack forming an impedance match between said substrate and said conductive layer, a second diffusion barrier layer deposited on said metal layer, and an outer dieletric anti-reflection stack deposited on said second barrier layer to form an impedance match between said conductive layer and air.
Claim 3
Dependent Claim
24 words
The window as in claim 1 in which said layer of conductive metal is selected from the group consisting of Au, Al, and Ag.
Claim 4
Dependent Claim
27 words
The window as in claim 1 in which said layer of conductive metal is gold and said nucleating layer is Al metal or oxygen deficient oxide aluminum.
Claim 5
Dependent Claim
33 words
The window as in claim 1 selected for operation in the infrared in which said layer of metal is gold, and said nucleating layer is Al metal or highly oxygen deficient aluminum oxide.
Claim 6
Dependent Claim
17 words
The window as in claim 4 in which the diffusion barrier is Al 2 O 3 .
Claim 7
Dependent Claim
21 words
The window as in claim 4 in which said impedance matching stacks are made of layers of high index transparent materials.
Claim 8
Dependent Claim
19 words
The window as in claim 6 in which said materials are selected from the group consisting of and ZnS.
Claim 9
Dependent Claim
12 words
The window as in claim 6 in which said substrate is sapphire
Claim 10
Dependent Claim
20 words
The window as in claim 1 in which said conductive metal is aluminum and said nucleating layer is yttrium oxide.
Claim 11
Dependent Claim
30 words
The window as in claim 1 selected for operation in the ultraviolet in which said conductive metal layer is aluminum and said nucleating layer is Y 2 O 3 .
Claim 12
Dependent Claim
36 words
The window as in claim 10 in which said impedance matching stacks are made of dielectric materials selected from the group consisting of yttrium oxide (Y 2 O 3 ) and silicon dioxide (SiO 2 ).
Claim 13
Dependent Claim
39 words
The window as in claim 1 in which said outer anti-reflection stack is constructed and arranged to cause the electric field of the electromagnetic waves at the band of transparency to have a minimum value in the metal layer.
Claim 14
Dependent Claim
167 words
An electrically conductive window having optical transparency in the infrared, visible, or UV bands comprising a substrate transparent at said band and having a surface on one side thereof, means for impedance matching energy of said band to said substrate, means forming a first diffusion barrier at the surface of said last named means, means forming a nucleating surface on said barrier, a layer of substantially transparent conductive metal deposited on said nucleating means to a thickness yielding a resistance value of less than about 10 ohms/sq., said nucleating means being selected to cooperate with said metal layer to allow the metal layer to form in a continuous thin film without agglomeration having optical constants n, k approximating these of the bulk metal, said first matching means forming an impedance match between said substrate and said conductive layer, means forming a second diffusion barrier on said metal layaer, and means on said second barrier to form a impedance match between the underlying means and layer, and air.
Claim 15
Dependent Claim
167 words
An electrically conductive window having optical transparency in the infrared, visible, or UV bands comprising a substrate transparent at said band and having a surface on one side thereof, means for impedance matching energy of said band to said substrate, means forming a first diffusion barrier at the surface of said last named means, means forming a nucleating surface on said barrier, a layer of substantially transparent conductive metal deposited on said nucleating means to a thickness yielding a resistance value of less than about 10 ohms/sq., said nucleating means being selected to cooperate with said metal layer to allow the metal layer to form in a continuous thin film without agglomeration having optical constants n, k approximating these of the bulk metal, said first matching means forming an impedance match between said substrate and said conductive layer, means forming a second diffusion barrier on said metal layaer, and means on said second barrier to form a impedance match between the underlying means and layer, and air.
Claim 16
Dependent Claim
22 words
The window as in claim 13 in which said conductive metal is selected from the group consisting of Au, Al, and Ag.
Claim 17
Dependent Claim
25 words
The window as in claim 13 in which said conductive metal is gold and said nucleating layer is Al metal or oxygen deficient oxide aluminum.
Claim 18
Dependent Claim
33 words
The window as in claim 13 selected for operation in the infrared in which said conductive metal is gold, and said nucleating surface is made of Al metal or oxygen deficient aluminum oxide.
Claim 19
Dependent Claim
17 words
The window as in claim 16 in which the diffusion barriers are Al 2 O 3 .
Claim 20
Dependent Claim
21 words
The window as in claim 16 in which said impedance matching means are made of layers of high index transparent materials.
Claim 21
Dependent Claim
20 words
The window as in claim 18 in which said materials are selected from the group consisting of Ge and ZnS.
Claim 22
Dependent Claim
12 words
The window as in claim 18 in which said substratae is sapphire.
Claim 23
Dependent Claim
20 words
The window as in claim 13 in which said conductive metal is aluminum and said nucleating means is yttrium oxide.
Claim 24
Dependent Claim
29 words
The window as in claim 13 selected for operation in the ultraviolet in which said conductive metal is aluminum and said nucleating means is Y 2 O 3 .
Claim 25
Dependent Claim
36 words
The window as in claim 22 in which said impedance matching means are made of dielectric materials selected from the group consisting of yttrium oxide (Y 2 O 3 ) and silicon dioxide (SiO 2 ).
Claim 26
Dependent Claim
42 words
The window as in claim 13 in which said several means and metal layer are constructed and arranged to cause the electric field of the electromagnetic waves at the band of transparency to have a minimum value in the conductive metal layer.
Claim 27
Dependent Claim
134 words
A transparent, conductive window comprising a substrate having an outer surface, first means formed at said surface for matching the impedance of the substrate to overlaid material subsequently deposited or created, second means formed at the outer surface of said first means for creating a barrier against diffusion of overlaid material therethrough, third means formed at the outer surface of said second means for causing nucleation of overlaid material fourth substantially transparent means deposited on siad third means for forming a conductive metal layer at the surface thereof having a surface conductivity of less than 10 ohms/sq. fifth means formed on said fourth means for creating a barrier against upward outward migration of said fourth means, and sixth means formed on said fifth means for matching the impedance of the previous means to air.
Claim 28
Dependent Claim
134 words
A transparent, conductive window comprising a substrate having an outer surface, first means formed at said surface for matching the impedance of the substrate to overlaid material subsequently deposited or created, second means formed at the outer surface of said first means for creating a barrier against diffusion of overlaid material therethrough, third means formed at the outer surface of said second means for causing nucleation of overlaid material fourth substantially transparent means deposited on siad third means for forming a conductive metal layer at the surface thereof having a surface conductivity of less than 10 ohms/sq. fifth means formed on said fourth means for creating a barrier against upward outward migration of said fourth means, and sixth means formed on said fifth means for matching the impedance of the previous means to air.
Claim 29
Dependent Claim
15 words
The window as in claim 25 in which the fourth means is made of gold.
Claim 30
Dependent Claim
21 words
The window as in claim 25 in which the second and fifth means are made of Al 2 O 3 .
Claim 31
Dependent Claim
25 words
The window as in claim 25 in which the fourth means is made of gold and in which the third means is made of Al.
Claim 32
Dependent Claim
37 words
The window as in claim 25 in which said several means are constructed and arranged to cause the electric field of the electromagnetic waves at the predetermined frequency to have a minimum value in the fourth means.
References Cited (Backward Citations)
US2628927A
Cited
US3039896A
Cited
US3935458A
Cited
US4204374A
Cited
US4153518A
Cited
US4327967A
Cited
US4320169A
Cited
US4306110A
Cited
GB2126256A
Cited
US4563400A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-30 | 1991-06-01 | 1991-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-30 | 1995-06-01 | 1995-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-30 | 1999-06-01 | 1999-12-01 | $7700.00 | Window Closed / Lapsed |