Semiconductor device fabrication process
Assignee: Texas Instruments Inc
•
Filing: 1987-03-10
•
Granted: 1987-11-24
•
Expires: 2007-03-10
Abstract
Abstract A semiconductor device fabrication process comprising the following sequential steps: Sequential formation of an oxide layer and first layer of masking material resistant both to oxidation (particularly preventing the action of oxidants, such as water vapors and O 2 ) and heat, on a principal plane of semiconductor substrate; Patternwise removal of these two layers in overlapping positions to form wells with the above semiconductor substrate exposed at bottom; Selective removal of the above oxide layer only around the wells thus formed to leave recesses; Deposition of the second layer of masking material resistant both oxidation and heat on the exposed surfaces of semiconductor substrate at the bottom of the above wells and in the recesses that are left after the above selective removal of oxide layer; Removal of the above second layer of masking material from the bottom of wells with the masking material left in the above recesses; and Selective oxidation of exposed surfaces of above semiconductor substrate under masking with the first and second layers of masking material that remain.
Inventors
- 👤 Osaomi Enomoto
- 👤 Katsuo Komatsuzaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:14
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/10; H10W10/13; C; C23; C23C; C23C16/00; C23C16/04; C23C16/042; H10B; H10B12/00; H10P; H10P14/00; H10P14/60; H10P14/61; H10P50/00; H10P50/73; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
145 words
A semiconductor device fabrication process comprising the following sequential steps: sequential formation of an oxide layer and first layer of a masking material that is resistant both to oxidation and heat on a principal plane of semiconductor substrate; patternwise removal of these two layers at overlapping positions to form wells with the above semiconductor substrate exposed at bottom; selective removal of said oxide layer only around said wells to leave recesses; deposition of a second layer of masking material resistant both to oxidation and heat on the exposed surfaces of semiconductor substrate at the bottom of said wells and also in said recesses; removal of said second layer of masking material from the bottom of wells with the masking material left in said recesses; and selective oxidation of exposed surfaces of semiconductor substrate under masking with the remaining first and second layers of masking material.
Claim 2
Dependent Claim
145 words
A semiconductor device fabrication process comprising the following sequential steps: sequential formation of an oxide layer and first layer of a masking material that is resistant both to oxidation and heat on a principal plane of semiconductor substrate; patternwise removal of these two layers at overlapping positions to form wells with the above semiconductor substrate exposed at bottom; selective removal of said oxide layer only around said wells to leave recesses; deposition of a second layer of masking material resistant both to oxidation and heat on the exposed surfaces of semiconductor substrate at the bottom of said wells and also in said recesses; removal of said second layer of masking material from the bottom of wells with the masking material left in said recesses; and selective oxidation of exposed surfaces of semiconductor substrate under masking with the remaining first and second layers of masking material.
Claim 3
Dependent Claim
46 words
A process as claimed in claim 1 wherein said first layer of masking material and said oxide layer are etched in the same pattern to form said wells and the remaining oxide layer is further overetched under masking with the remaining first layer of masking material.
Claim 4
Dependent Claim
44 words
A process as claimed in claim 1 wherein at cleaning following etching of said first layer of masking material said oxide layer is etched in the same pattern as said first layer of masking material and said oxide layer is then further continuously overetched.
Claim 5
Dependent Claim
22 words
A process as claimed in claim 2 wherein said wells are formed by dry etching while said overetching is a wet process.
Claim 6
Dependent Claim
28 words
A process as claimed in claim 3 wherein both etching of said first layer of masking material and said overetching that follows are performed by a wet process.
Claim 7
Dependent Claim
57 words
A process as claimed in claim 2 wherein said second layer of masking material is deposited in such a manner that said recesses formed by said overetching under eaves overhanging from said first layer of masking material (namely, hollow spaces with said oxide layer selectively removed) are fully filled with the masking material of said second layer.
Claim 8
Dependent Claim
33 words
A process as claimed in claim 1 wherein said second layer of masking material is etched by the etch back technique to leave the masking material of said second layer in said recesses.
Claim 9
Dependent Claim
40 words
A process as claimed in claim 1 wherein the surface of said semiconductor are patternwise oxidized under masking with said first and second layers of masking material to form a pattern of field oxide film for isolation of circuit elements.
Claim 10
Dependent Claim
34 words
A process as claimed in claim 1 wherein said oxide layer is composed of SiO 2 and both said first and second layers of masking material are composed of Si 3 N 4 .
Claim 11
Dependent Claim
22 words
A process as claimed in claim 1 wherein an impurity is introduced through said wells into said semiconductor substrate as channel stopper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-11-23 | 1991-05-25 | 1991-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-11-23 | 1995-05-25 | 1995-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-11-23 | 1999-05-25 | 1999-11-24 | $7700.00 | Window Closed / Lapsed |