Assignee: Texas Instruments Inc
•
Filing: 1980-11-04
•
Granted: 1982-05-25
•
Expires: 2000-11-04
Abstract
Abstract A method of fabricating deep grooves having submicron widths in a semiconductor substrate. A pattern of submicron oxidation masking elements formed on the substrate surface serves as an oxidation mask for a thick oxide layer. After forming the oxide layer, the insulating elements are removed to form a pattern of submicron width openings in the oxide extending to the substrate. A selective anisotropic dry etch is then used to form deep, narrow grooves in the substrate conforming to the pattern of openings which are filled with an insulating material formed by thermal oxidation, chemical vapor deposition, or a combination thereof. This process is used to provide deep dielectric isolation between active areas in high density integrated circuits.
Inventors
- 👤 William R. Hunter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 04:07
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10P; H10P50/00; H10P50/69; H10P50/691; H10W10/014; H10W10/0145; H10W10/10; H10W10/13; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/051; Y10S148/085; Y10S148/111
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
98 words
A method of forming insulating barriers in a semiconductor substrate comprising the steps of: forming a pattern of submicron-width oxidation masking elements on a surface of said substrate; forming a layer of insulating material resistant to an etchant on the exposed areas of said substrate surface; removing said oxidation masking elements to expose said substrate in a pattern of submicron width openings; anisotropically etching said substrate with said etchant to form grooves therein conforming to said pattern of openings and having a depth substantially greater than their width; and forming an insulating material to substantially fill said grooves.
Claim 2
Independent Claim
98 words
A method of forming insulating barriers in a semiconductor substrate comprising the steps of: forming a pattern of submicron-width oxidation masking elements on a surface of said substrate; forming a layer of insulating material resistant to an etchant on the exposed areas of said substrate surface; removing said oxidation masking elements to expose said substrate in a pattern of submicron width openings; anisotropically etching said substrate with said etchant to form grooves therein conforming to said pattern of openings and having a depth substantially greater than their width; and forming an insulating material to substantially fill said grooves.
Claim 3
Dependent Claim
19 words
The method of claim 1, wherein said substrate is silicon and said submicron-width elements are formed of silicon nitride.
Claim 4
Dependent Claim
22 words
The method of claim 2, wherein said substrate etching step comprises forming said grooves with an anisotropic plasma etch selective for silicon.
Claim 5
Dependent Claim
23 words
The method of claim 2, wherein said substrate etching step comprises forming said grooves with an anisotropic reactive ion etch selective for silicon.
Claim 6
Independent Claim
25 words
The method of claims 3 or 4, wherein said step of forming an insulating material comprises forming silicon dioxide in said grooves by thermal oxidation.
Claim 7
Independent Claim
26 words
The method of claims 3 or 4, wherein said step of forming an insulating material comprises forming silicon dioxide in said grooves by chemical vapor deposition.
Claim 8
Independent Claim
50 words
The method of claims 3 or 4, wherein said step of forming an insulating material in said grooves comprises: partially filling said grooves with a conformal layer of silicon dioxide formed by thermal oxidation; and filling the remaining volume of said grooves with silicon dioxide formed by chemical vapor deposition.
Claim 9
Dependent Claim
21 words
The method of claim 6, further including the step of planarizing the surface of said silicon dioxide with an anisotropic etch.
Claim 10
Dependent Claim
21 words
The method of claim 7, further including the step of planarizing the surface of said silicon dioxide with an anisotropic etch.
Claim 11
Dependent Claim
22 words
The method of claim 7, wherein said step of forming a pattern of submicron-width oxidation masking elements comprises an edge definition process.
Claim 12
Dependent Claim
70 words
The method of claim 10, wherein said edge definition process comprises the steps of: depositing a layer of material such that the edges of said material correspond to said pattern of said submicron-width oxidation masking elements; conformally depositing silicon nitride atop said material; anisotropically etching said silicon nitride until said silicon nitride has been removed except in said pattern of submicron-width oxidation masking elements; and removing said layer of material.
Claim 13
Dependent Claim
26 words
The method of claim 1, 2, 3, or 4, wherein said step of forming a pattern of submicron-width oxidation masking elements comprises an edge definition process.
Claim 14
Dependent Claim
70 words
The method of claim 12, wherein said edge definition process comprises the steps of: depositing a layer of material such that the edges of said material correspond to said pattern of said submicron-width oxidation masking elements; conformally depositing silicon nitride atop said material; anisotropically etching said silicon nitride until said silicon nitride has been removed except in said pattern of submicron-width oxidation masking elements; and removing said layer of material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-24 | 1985-11-23 | 1986-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-24 | 1989-11-23 | 1990-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-24 | 1993-11-23 | 1994-05-25 | $7700.00 | Window Closed / Lapsed |