Process for the production of low-thermal-expansive (ZrO)2 P2 O7 ceramic
Assignee: Nihon Ceramics Co Ltd
•
Filing: 1986-03-24
•
Granted: 1987-10-27
•
Expires: 2006-03-24
Abstract
Abstract In the production of low-thermal-expansive zirconyl phosphate ceramic, whose chemical formula is (ZrO)2.P2O7 and whose chemical composition is 2ZrO2.P2O5 by sintering of the fine-powder compact, three kinds of reaction aids are employed. They are a densifying aid, a grain-growth-suppressing aid and a solid-solution-forming aid. The densifying aid is always employed, the grain-growth-suppressing aid is employed for producing a more thermal-resistant ceramic for high temperature use and the solid-solution-forming aid is employed for producing a more low-thermal-expansive ceramic.
Inventors
- 👤 Iwao Yamai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 15:57
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/447
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
117 words
A process for the production of low-thermal-expansive (ZrO) 2 .P 2 .O 7 polycrystalline ceramic which comprises sintering the fine-powder compact of (ZrO) 2 .P 2 O 7 crystal with a densifying aid selected from the group consisting of zinc oxide, magnesium oxide, bismuth oxide, manganese oxide, iron oxide, cobalt oxide, nickel oxide, the compounds of said metal oxides and mixtures thereof together with a grain-growth-suppressing aid selected from the group of consisting silicon dioxide, metal silicate and mixtures thereof at a temperature from 1200° C. to 1700° C. wherein the content of the densifying aid is from 0.2% to 10.0% by weight and the content of the grain-growth-suppressing aid is from 0 to 10% by weight.
Claim 2
Dependent Claim
117 words
A process for the production of low-thermal-expansive (ZrO) 2 .P 2 .O 7 polycrystalline ceramic which comprises sintering the fine-powder compact of (ZrO) 2 .P 2 O 7 crystal with a densifying aid selected from the group consisting of zinc oxide, magnesium oxide, bismuth oxide, manganese oxide, iron oxide, cobalt oxide, nickel oxide, the compounds of said metal oxides and mixtures thereof together with a grain-growth-suppressing aid selected from the group of consisting silicon dioxide, metal silicate and mixtures thereof at a temperature from 1200° C. to 1700° C. wherein the content of the densifying aid is from 0.2% to 10.0% by weight and the content of the grain-growth-suppressing aid is from 0 to 10% by weight.
Claim 3
Dependent Claim
44 words
A process according to claim 1, wherein the densifying aid is the powder of said metal oxides and the powder of the compounds of said metal oxides selected from the group consisting of the phosphates, the carbonate, the sulfates, the nitrates and mixtures thereof.
Claim 4
Dependent Claim
39 words
A process according to claim 1, wherein the grain-growth-suppressing aid is the powder of silicon dioxide and the powder of the silicate of metal selected from the group consisting of zinc, magnesium, manganese, cobalt, iron, aluminum and mixtures thereof.
Claim 5
Dependent Claim
56 words
A process according to claim 1, wherein the (ZrO) 2 .P 2 O 7 crystal is in solid solution with up to 5% by weight of niobium oxide, said solution being produced by the reaction of (ZrO) 2 .P 2 O 7 powder with niobium oxide powder at a temperature from 1200° C. to 1400° C.
Claim 6
Dependent Claim
22 words
A process according to claim 1, wherein (ZrO) 2 .P 2 O 7 powder is prepared by precipitation from an aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |